回火时间对Nb微合金化压力容器用钢析出物的影响

doi:10.13251/j.issn.0254-6051.2025.10.010

金属热处理 ›› 2025, Vol. 50 ›› Issue (10): 70-73.DOI: 10.13251/j.issn.0254-6051.2025.10.010

回火时间对Nb微合金化压力容器用钢析出物的影响

刘晨希^1,2, 胡昕明^1,2, 欧阳鑫^1,2, 邢梦楠^1,2, 白云峰^1,2, 王锐琛³

1.海洋装备用金属材料及其应用国家重点实验室, 辽宁鞍山 114009;
2.鞍钢集团钢铁研究院, 辽宁鞍山 114009;
3.鞍钢股份鲅鱼圈钢铁分公司, 辽宁营口 115007

收稿日期:2025-05-09 修回日期:2025-08-18 出版日期:2025-10-25 发布日期:2025-11-04
作者简介:刘晨希(1994—),男,工程师,硕士,主要研究方向为压力容器用钢,E-mail:794419216@qq.com

Effect of tempering time on precipitates in Nb microalloyed pressure vessel steel

Liu Chenxi^1,2, Hu Xinming^1,2, Ouyang Xin^1,2, Xing Mengnan^1,2, Bai Yunfeng^1,2, Wang Ruichen³

1. State Key Laboratory of Metal Material for Marine Equipment and Application, Anshan Liaoning 114009, China;
2. Iron & Steel Research Institute of Angang Group, Anshan Liaoning 114009, China;
3. Bayuquan Steel Branch of Angang Co., Ltd., Yingkou Liaoning 115007, China

Received:2025-05-09 Revised:2025-08-18 Online:2025-10-25 Published:2025-11-04

摘要/Abstract

摘要： 对某Nb微合金化压力容器用钢板进行950 ℃保温50 min淬火+620 ℃保温不同时间(12.5、25、50和200 min)回火处理后,对其进行TEM及EDS分析,研究了回火时间对钢中析出物的影响。结果表明,在回火保温时间12.5 min下,组织主要为回火索氏体+粒状贝氏体,基体上分布着细小粒状渗碳体和M-A岛。回火保温时间延长至200 min,粒状贝氏体分解完全。钢中析出物主要成分为Nb、Ti、C,为MC型碳化物,回火保温时间延长能够促进析出物生成,且析出物尺寸由18.2 nm长大至82.4 nm。

关键词: Nb微合金钢, 回火时间, 组织, 析出物

Abstract: Effect of tempering time on precipitates of a Nb-microalloyed pressure vessel steel plate after quenching at 950 ℃ for 50 min followed by tempering at 620 ℃ for different time (12.5, 25, 50, 200 min) was investigated by means of transmission electron microscope (TEM) and energy dispersive spectroscopy (EDS). The results show that when the tempering time is 12.5 min, the microstructure is mainly composed of tempered martensite+granular bainite, with fine granular cementite and M-A islands distributing on the matrix. When the tempering time is extended to 200 min, the granular bainite decomposes completely. The main components of the precipitates in the steel are Nb, Ti, and C, which are MC-type carbides. Prolonging the tempering time can promote the formation of precipitates, and the size of the precipitates grows from 18.2 nm to 82.4 nm.

Key words: Nb-microalloyed steel, tempering time, microstructure, precipitates

中图分类号:

TG142.1

刘晨希, 胡昕明, 欧阳鑫, 邢梦楠, 白云峰, 王锐琛. 回火时间对Nb微合金化压力容器用钢析出物的影响[J]. 金属热处理, 2025, 50(10): 70-73.

Liu Chenxi, Hu Xinming, Ouyang Xin, Xing Mengnan, Bai Yunfeng, Wang Ruichen. Effect of tempering time on precipitates in Nb microalloyed pressure vessel steel[J]. Heat Treatment of Metals, 2025, 50(10): 70-73.

参考文献

[1] 余国, 陆如泉, 刘佳, 等. 新形势下的能源转型与能源合作—“2022年国际能源发展高峰论坛”综述[J]. 国际石油经济, 2023, 31(2): 23-29.
Yu Guo, Lu Ruquan, Liu Jia, et al. Energy transition and energy cooperation under the new situation—Review of International Energy Executive Forum 2022[J]. International Petroleum Economics, 2023, 31(2): 23-29.
[2] 江慧丰. 我国压力容器用低合金调质高强度钢板的现状与发展趋势[J]. 热加工工艺, 2015, 44(4): 16-19, 24.
Jiang Huifeng. Current status and development trend of quenched and tempered high strength low-alloy steel plates for pressure vessels in China[J]. Hot Working Technology, 2015, 44(4): 16-19, 24.
[3] 王博, 白星良, 战东平, 等. 回火温度对12MnNiVR压力容器钢板组织和性能的影响[J]. 金属热处理, 2019, 44(9): 189-193.
Wang Bo, Bai Xingliang, Zhan Dongping, et al. Effect of the tempering temperature on microstructure and mechanical properties of 12MnNiVR pressure vessel steel[J]. Heat Treatment of Metals, 2019, 44(9): 189-193.
[4] 欧阳鑫, 姚震, 张坤, 等. 12MnNiVR钢板超声探伤不合格原因分析及改进措施[J]. 轧钢, 2024, 41(2): 30-35.
Ouyang Xin, Yao Zhen, Zhang Kun, et al. Cause analysis and improvement measures for ultrasonic flaw detection disqualification of 12MnNiVR steel plate[J]. Steel Rolling, 2024, 41(2): 30-35.
[5] 陈学东, 范志超, 陈永东, 等. 我国高端压力容器设计制造与维护技术进展[J]. 机械工程学报, 2023, 59(20): 18-33.
Chen Xuedong, Fan Zhichao, Chen Yongdong, et al. Technological progress on design, manufacturing and maintenance of high-end pressure vessels in China[J]. Journal of Mechanical Engineering, 2023, 59(20): 18-33.
[6] 马庆生, 李栋, 郭亮, 等. 3000 m³液态二氧化碳球形储罐设计[J]. 石油化工设备, 2024, 53(1): 33-39.
Ma Qingsheng, Li Dong, Guo Liang, et al. Design of 3000 m³ liquid carbon dioxide spherical storage tank[J]. Petro-Chemical Equipment, 2024, 53(1): 33-39.
[7] 崔建海. 07MnNiMoDR钢热处理工艺、组织及性能研究[D]. 重庆: 重庆大学, 2022.
[8] 李天怡, 陈义冕, 马国强, 等. Nb、V微合金化对高强管线钢相析出及强度的影响[J]. 鞍钢技术, 2023(6): 64-70, 83.
Li Tianyi, Chen Yimian, Ma Guoqiang, et al. Effect of microalloying by adding Nb and V on phase precipitation behaviors and strengths of high strength pipeline steels[J]. Angang Technology, 2023(6): 64-70, 83.
[9] 蒲春雷, 姜嫄, 闫洞旭, 等. Nb/V/Ti微合金化对20MnSi钢组织和力学性能影响[J]. 材料热处理学报, 2023, 44(7): 99-106.
Pu Chunlei, Jiang Yuan, Yan Dongxu, et al. Effect of Nb/V/Ti microalloying on microstructure and mechanical properties of 20MnSi steel[J]. Transactions of Materials and Heat Treatment, 2023, 44(7): 99-106.
[10] 叶晓瑜, 雷蕾, 张开华, 等. 冷却工艺对热轧V微合金化钢板组织性能的影响[J]. 轧钢, 2015, 32(1): 27-30.
Ye Xiaoyu, Lei Lei, Zhang Kaihua, et al. Influence of cooling process on microstructure and properties of V-microalloyed hot rolled plate[J]. Steel Rolling, 2015, 32(1): 27-30.

[1]	田育金, 杨胶溪, 高枫, 王高生, 刘琦, 李怀学. 激光等离子复合喷涂NiCr-Cr₃C₂涂层的组织与性能[J]. 金属热处理, 2025, 50(9): 1-6.
[2]	吴保平, 付媛媛, 张绪亮, 孙长波, 杨草, 王凯, 吴剑涛. 热校形工艺对Ni₃Al基高温合金组织与性能的影响[J]. 金属热处理, 2025, 50(9): 34-38.
[3]	刘斌华, 李可尔, 赵鹏程, 陈威. Ti55531钛合金热轧对α相析出行为及力学性能的影响[J]. 金属热处理, 2025, 50(9): 76-85.
[4]	吉效科, 毛勇, 李茂, 张丛笑, 见飞龙, 庄磊, 王玮晨, 刘二勇. 不锈钢熔覆层的微观组织和腐蚀磨损性能[J]. 金属热处理, 2025, 50(9): 92-98.
[5]	吴庆美, 郭强, 卜凡征, 肖景江. 不同热镀锌层的组织与摩擦性能对比[J]. 金属热处理, 2025, 50(9): 113-117.
[6]	胡雁阵, 李婷, Carlos Gracia, Caraballo Isaac Toda, Carallero Francisca Garcia, 于皓. 均一化处理对增材制造镍基合金组织与性能的影响[J]. 金属热处理, 2025, 50(9): 118-124.
[7]	王天琪, 柴希阳, 罗小兵, 师仲然. 控轧控冷工艺对ULCB钢组织与性能的影响[J]. 金属热处理, 2025, 50(9): 146-150.
[8]	杨恬, 孙上清, 田彦文, 王涛, 任勇. 固溶处理温度和冷却速率对TC6钛合金组织与性能的影响[J]. 金属热处理, 2025, 50(9): 151-155.
[9]	李佳傲, 黄硕, 李瑞红, 赵莉萍, 王海燕, 杨礼林, 金自力. 时效时间对Mg-10Gd-2Sm-1Y-0.5Zr合金组织与性能的影响[J]. 金属热处理, 2025, 50(9): 156-160.
[10]	徐凤祥, 卢道胜, 秦小飞, 李秋杰, 吴高盛. 40Cr钢锥面零件的激光淬火[J]. 金属热处理, 2025, 50(9): 165-169.
[11]	柳会梅, 陈珍妮, 许立雄, 熊俊伟, 孙昌政, 胡海江. 连续退火时效时间对低碳钢组织与性能的影响[J]. 金属热处理, 2025, 50(9): 170-174.
[12]	张海东, 闫献国, 向瑾, 李晋峰, 高丽梅. 深冷处理对40CrNiMo钢组织与性能的影响[J]. 金属热处理, 2025, 50(9): 175-180.
[13]	付世强, 张江, 廖斌, 蒋桂. 冷轧及退火工艺对新能源电池用铝塑膜箔组织与性能的影响[J]. 金属热处理, 2025, 50(9): 181-190.
[14]	何苗, 武晓峰, 董志强, 王端, 索忠源. 淬火温度对斗齿用35CrMnSi2钢组织与性能的影响[J]. 金属热处理, 2025, 50(9): 191-194.
[15]	肖晨亮, 程从前, 赵杰, 曹铁山. 淬火回火工艺对DF13钢组织与力学性能的影响[J]. 金属热处理, 2025, 50(9): 195-201.

回火时间对Nb微合金化压力容器用钢析出物的影响

Effect of tempering time on precipitates in Nb microalloyed pressure vessel steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价