高温预时效对6061铝合金第二相粒子与力学性能的影响

doi:10.13251/j.issn.0254-6051.2026.01.033

金属热处理 ›› 2026, Vol. 51 ›› Issue (1): 226-229.DOI: 10.13251/j.issn.0254-6051.2026.01.033

高温预时效对6061铝合金第二相粒子与力学性能的影响

谭国寅

昆明冶金研究院有限公司, 云南昆明 650031

收稿日期:2025-07-28 修回日期:2025-10-31 出版日期:2026-01-25 发布日期:2026-01-27
作者简介:谭国寅(1986—),男,高级工程师,硕士,主要研究方向为有色金属加工,E-mail: 80982250@163.com
基金资助:
云南省重大科技专项计划(202302AB080007)

Effect of high-temperature pre-aging on secondary phase particles and mechanical properties of 6061 aluminum alloy

Tan Guoyin

Kunming Metallurgical Research Institute Co., Ltd., Kunming Yunnan 650031, China

Received:2025-07-28 Revised:2025-10-31 Online:2026-01-25 Published:2026-01-27

摘要/Abstract

摘要： 对6061铝合金进行固溶+常规时效和固溶+高温预时效+低温时效处理,利用OM、SEM、TEM和拉伸试验机研究了高温预时效对其组织与力学性能影响。结果表明,较常规时效,增加高温预时效后,合金中析出第二相粒子更为均匀细小,可充分钉扎晶界,联合低温再时效工序能有效抑制合金的再结晶过程,使6061铝合金强度和伸长率提高。

关键词: 6061铝合金, 高温预时效, 力学性能, 第二相粒子

Abstract: A 6061 aluminum alloy was subjected to solution treatment+conventional aging (T6) and solution treatment+high-temperature pre-aging+low-temperature final aging (two-step aging) processes. Effect of high-temperature pre-aging on microstructure and mechanical properties of the alloy was investigated using optical microscopy (OM), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and tensile testing machine. The results show that compared with that of conventional aging, the introduction of high-temperature pre-aging leads to more uniform and finer secondary phase precipitates in the alloy, which can effectively pin grain boundaries. Combined with the subsequent low-temperature aging step, the recrystallization process of the alloy is significantly inhibited, resulting in simultaneous improvements in the strength and elongation of the 6061 aluminum alloy.

Key words: 6061 aluminum alloy, high temperature pre-aging, mechanical properties, secondary phase particles

中图分类号:

TG166.3

谭国寅. 高温预时效对6061铝合金第二相粒子与力学性能的影响[J]. 金属热处理, 2026, 51(1): 226-229.

Tan Guoyin. Effect of high-temperature pre-aging on secondary phase particles and mechanical properties of 6061 aluminum alloy[J]. Heat Treatment of Metals, 2026, 51(1): 226-229.

参考文献

[1] 占紫怡, 李亮雨, 江勇. 新能源汽车用铸造铝合金的研究现状和发展趋势[J]. 现代交通与冶金材料, 2024, 4(6): 68-76.
Zhan Ziyi, Li Liangyu, Jiang Yong. Research and development of cast aluminum alloys for new energy vehicles: A brief review[J]. Modern Transportation and Metallurgical Materials, 2024, 4(6): 68-76.
[2] 李乾. 铝合金在汽车轻量化设计中的应用研究[J]. 汽车知识, 2024(11): 89-92.
Li Qian. Research on the application of aluminum alloy in automotive lightweight design[J]. Auto Know, 2024(11): 89-92.
[3] 刘帅. 浅析汽车轻量化技术[J]. 铝加工, 2024(3): 3-10.
Liu Shuai. Analysis of automobile lightweight technology[J]. Aluminium Fabrication, 2024(3): 3-10.
[4] 韩如意, 董刘颖, 冯哲, 等. 汽车用6111铝合金板材成形性和烤漆性研究[J]. 热处理技术与装备, 2024, 45(2): 26-29, 33.
Han Ruyi, Dong Liuying, Feng Zhe, et al. Study on the formability and paintability of 6111 aluminum alloy sheet for automobile[J]. Heat Treatment Technology and Equipment, 2024, 45(2): 26-29, 33.
[5] 李海, 毛庆忠, 王芝秀, 等. 高温预时效+低温再时效对Al-Mg-Si-Cu合金力学性能及晶间腐蚀敏感性的影响[J]. 金属学报, 2014, 50(11): 1357-1366.
Li Hai, Mao Qingzhong, Wang Zhixiu, et al. Effect of high temperature pre-aging and low temperaturere-aging on mechanical properties and intergranular corrosion susceptibility of Al-Mg-Si-Cu alloys[J]. Acta Metallurgica Sinica, 2014, 50(11): 1357-1366.
[6] 雷越, 臧金鑫, 邢清源, 等. 第二级时效对7085铝合金厚板力学性能及晶间腐蚀性能的影响[J]. 有色金属工程, 2022, 12(1): 36-41.
Lei Yue, Zang Jinxin, Xing Qingyuan, et al. Effect of second stage aging on mechanical and intergranular corrosion properties of 7085 plate[J]. Nonferrous Metals Engineering, 2022, 12(1): 36-41.
[7] 杨哲, 陈水胜. 时效工艺对ADC12铝合金析出相与力学性能的影响[J]. 金属热处理, 2024, 49(9): 216-220.
Yang Zhe, Chen Shuisheng. Effect of aging on precipitated phases and mechanical properties of ADC12 aluminum alloy[J]. Heat Treatment of Metals, 2024, 49(9): 216-220.
[8] 徐亚琪, 翁瑶瑶, 陈家浩, 等. 预时效对含0.1%In的Al-Mg-Si合金微观结构和力学性能的影响[J]. 材料工程, 2023, 51(6): 101-110.
Xu Yaqi, Weng Yaoyao, Chen Jiahao, et al. Effect of pre-aging on microstructure and mechanical properties of Al-Mg-Si alloy containing 0.1%In[J]. Journal of Materials Engineering, 2023, 51(6): 101-110.
[9] 徐向美, 王琪晨. 预时效处理对AlZnMgCu铝合金自然时效和烘烤硬化行为的影响[J]. 金属热处理, 2023, 48(10): 188-192.
Xu Xiangmei, Wang Qichen. Influence of pre-aging on natural aging and bake hardening behavior of AlZnMgCu aluminum alloy[J]. Heat Treatment of Metals, 2023, 48(10): 188-192.

[1]	唐家璇, 杨忠民, 笪光杰, 范长增, 陈颖, 李昭东, 王凯. 回火温度对Si-Mn-Mo系贝氏体钢组织与性能的影响[J]. 金属热处理, 2026, 51(1): 22-29.
[2]	邹伟, 彭金波, 韩中宝. TC2钛合金的高温力学性能及预测模型[J]. 金属热处理, 2026, 51(1): 56-64.
[3]	王军, 李智勇, 巢昺轩, 王豪, 郭楠, 应俊龙, 张韶佳. 淬火介质对1Cr17Ni2调质钢组织与性能的影响[J]. 金属热处理, 2026, 51(1): 95-102.
[4]	包科杰, 赵强, 李月梅. 热变形温度对高强塑积汽车用中锰钢组织与性能的影响[J]. 金属热处理, 2026, 51(1): 116-123.
[5]	乔恩利, 张明玉, 顾忠明. 热变形温度对TA2纯钛微观组织与力学性能的影响[J]. 金属热处理, 2026, 51(1): 133-137.
[6]	石晓辉, 乔语祺, 陈嘉彬, 乔珺威, 霍锋锋. 热机械处理工艺对ER8车轮钢组织与力学性能的影响[J]. 金属热处理, 2026, 51(1): 138-144.
[7]	石浩, 李绍宏, 李权, 李根, 包汉生. 退火温度对含铜00Cr13Si2钢显微组织、力学性能和磁性能的影响[J]. 金属热处理, 2026, 51(1): 145-152.
[8]	孟立鑫, 李文琪, 汪英芝, 夏伊婷, 梁伟. 淬火配分工艺对430铁素体不锈钢组织与性能的影响[J]. 金属热处理, 2026, 51(1): 153-158.
[9]	朱璋琳, 曹晨, 史姗. 无磁钢钻杆摩擦焊及焊后热处理组织与力学性能[J]. 金属热处理, 2026, 51(1): 173-178.
[10]	崔凯禹, 李正荣, 李海波, 陈述, 汪创伟, 熊雪刚, 刘一博. 终轧温度和卷取温度对V-Ti微合金化耐候钢组织与性能的影响[J]. 金属热处理, 2026, 51(1): 179-188.
[11]	魏军祥, 边丽萍, 李灵浩, 王涛, 陈鹏, 郑留伟, 梁伟. 轧制工艺对Mg-14Li-0.18Al-0.5Ca-0.5Y合金组织与性能的影响[J]. 金属热处理, 2026, 51(1): 189-194.
[12]	王天琪, 李浩然, 刘海华, 李晨东. 热处理对316L钢/Inconel625镍基合金双金属增材结构件微观组织与力学性能的影响[J]. 金属热处理, 2026, 51(1): 207-213.
[13]	嵇萌萌, 翁华晶, 朱晓磊, 陆晓峰, 王健. 回火温度对42CrMo钢组织与力学性能的影响[J]. 金属热处理, 2026, 51(1): 214-220.
[14]	潘诗良, 刘庆冬, 王泽民, 许媛媛. 热处理工艺对3D打印20Cr13Mo模具钢组织与性能的影响[J]. 金属热处理, 2026, 51(1): 236-240.
[15]	王亚齐, 李亚萍, 乔柳平, 唐俊榕, 陈沙. 热处理对等离子弧增材制造Ti-6Al-4V合金微观组织与力学性能的影响[J]. 金属热处理, 2026, 51(1): 241-247.

高温预时效对6061铝合金第二相粒子与力学性能的影响

Effect of high-temperature pre-aging on secondary phase particles and mechanical properties of 6061 aluminum alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价