GB/T 7216—2023《灰铸铁金相检验》标准解读

doi:10.13251/j.issn.0254-6051.2025.04.050

金属热处理 ›› 2025, Vol. 50 ›› Issue (4): 323-329.DOI: 10.13251/j.issn.0254-6051.2025.04.050

• 标准化 • 上一篇

GB/T 7216—2023《灰铸铁金相检验》标准解读

张振威¹, 马裕辰², 赵洁¹, 蒋锐¹, 陈敏¹, 李爽¹, 李曙³

1.中国兵器科学研究院宁波分院, 浙江宁波 315103;
2.长安大学长安都柏林国际交通学院, 陕西西安 710064;
3.宁波市生态环境局镇海分局, 浙江宁波 315200

收稿日期:2024-11-04 修回日期:2025-02-19 发布日期:2025-06-13
作者简介:张振威(1991—),男,助理研究员,硕士,主要研究方向为金属材料检验及失效分析,E-mail: zzwTaylor@163.com
基金资助:
中国兵器科学研究院宁波分院基金(NBF 2023-14)

Interpretation of standard GB/T 7216—2023 Metallographic test for gray cast iron

Zhang Zhenwei¹, Ma Yuchen², Zhao Jie¹, Jiang Rui¹, Chen Min¹, Li Shuang¹, Li Shu³

1. Ningbo Branch of Chinese Academy of Ordnance Science, Ningbo Zhejiang 315103, China;
2. Chang'an Dublin International College ofTransportation at Chang'an University, Chang'an University, Xi'an Shaanxi 710064, China;
3. Zhenhai Branch of Ningbo Municipal Bureau of Ecology and Environment, Ningbo Zhejiang 315200, China

Received:2024-11-04 Revised:2025-02-19 Published:2025-06-13

摘要/Abstract

摘要： 在与GB/T 7216—2009对比的基础上,从标准适用范围、术语和定义、检测项目和评级图谱及结果表示方面对GB/T 7216—2023进行了解读。GB/T 7216—2023中更改了标准的适用范围及各种组织类型的测量方法和参照图谱;增加了术语和定义、石墨含量计算方法和石墨形状长度表述示例;附录部分增加了与ISO 945-1:2019的对比情况及典型片状石墨分布形态和石墨类型图像分析识别方法。

关键词: 灰铸铁, 片状石墨, 碳化物, 磷共晶, 共晶团数量

Abstract: Based on comparison with GB/T 7216—2009, GB/T 7216—2023 was interpreted from standard application scope, terms and definitions, inspection items, rating images, and result representation. In GB/T 7216—2023, the application scope of the standard, the measurement methods and reference images for various types of microstructure are changed. Terms and definitions, the calculation method of graphite content, and examples of graphite shape length expressions are added. In the appendix part, the comparison with ISO 945-1: 2019, the typical flake graphite distribution patterns, and image analysis identification methods for graphite types are added.

Key words: gray cast iron, flake graphite, carbide, phosphorus eutectic, eutectic clusters count

中图分类号:

TG251
N65

张振威, 马裕辰, 赵洁, 蒋锐, 陈敏, 李爽, 李曙. GB/T 7216—2023《灰铸铁金相检验》标准解读[J]. 金属热处理, 2025, 50(4): 323-329.

Zhang Zhenwei, Ma Yuchen, Zhao Jie, Jiang Rui, Chen Min, Li Shuang, Li Shu. Interpretation of standard GB/T 7216—2023 Metallographic test for gray cast iron[J]. Heat Treatment of Metals, 2025, 50(4): 323-329.

参考文献

[1] 李双, 吕海宁, 黄小华, 等. 船用灰铸铁材料裂纹扩展的近场动力学研究[J]. 船舶力学, 2023, 27(9): 1379-1389.
Li Shuang, Lü Haining, Huang Xiaohua, et al. Peridynamic study on crack propagation of marine gray cast iron[J]. Journal of Ship Mechanics, 2023, 27(9): 1379-1389.
[2] 李淑昌, 娄长胜, 刘凤国, 等. 加铜提高灰铸铁的耐磨耐蚀和抗菌性能[J]. 材料导报, 2023, 37(S1): 342-347.
Li Shuchang, Lou Changsheng, Liu Fengguo, et al. Improvement of wear resistance, corrosion resistance and antibacterial properties of gray cast iron by addition of different copper content[J]. Materials Reports, 2023, 37(S1): 342-347.
[3] 时晓宇, 温道胜, 王守仁, 等. 激光熔覆灰铸铁制动盘Fe-Ni-Cr梯度复合涂层微观组织及高温摩擦磨损性能研究[J]. 中国激光, 2022, 49(2): 188-199.
Shi Xiaoyu, Wen Daosheng, Wang Shouren, et al. Microstructures and high-temperature friction and wear properties of laser cladded Fe-Ni-Cr gradient composite coating for brake disc[J]. Chinese Journal of Lasers, 2022, 49(2): 188-199.
[4] 陈贻亮, 宋生强, 周柱华, 等. 钼对灰铸铁中碳化物析出和微观组织及性能的影响[J]. 材料与冶金学报, 2022, 21(4): 285-292.
Chen Yiliang, Song Shengqiang, Zhou Zhuhua, et al. Effect of molybdenum on carbide precipitation, microstructure and properties of gray cast iron[J]. Journal of Materials and Metallurgy, 2022, 21(4): 285-292.
[5] 郭士锐, 赵阳, 崔陆军, 等. 基于灰铸铁表面多道搭接熔覆成形质量及组织性能研究[J]. 有色金属工程, 2022, 12(4): 31-35.
Guo Shirui, Zhao Yang, Cui Lujun, et al. Study on forming quality, microstructure and properties of multi-lap cladding on the surface of gray cast iron[J]. Nonferrous Metals Engineering, 2022, 12(4): 31-35.
[6] 王佳香. 高硫高氮增碳剂在降低灰铸铁缸体铸件废品率上的应用[J]. 铸造, 2023, 72(7): 827-832.
Wang Jiaxiang. Application of high sulfur nitrogen recarburizer to reducing the rejection rate of gray cast iron cylinder block castings[J]. Foundry, 2023, 72(7): 827-832.
[7] 李涛涛. 灰铁刹车盘裂纹的失效分析[J]. 材料保护, 2020, 53(5): 152-155.
Li Taotao. Analysis on cracking failure of gray cast iron brake disk[J]Materials Protection, 2020, 53(5): 152-155.
[8] 毕革平. 灰铸铁和球墨铸铁金相检验标准变更比对分析[J]. 金属热处理, 2011, 36(1): 127-130.
Bi Geping. Standard changes contrastive analysis of metallographic test for spheroidal graphite cast iron and gray cast iron[J]. Heat Treatment of Metals, 2011, 36(1): 127-130.

[1]	张立冰, 程陆凡, 陈昊, 石全强, 严伟, 罗贯虹, 李瑞平, 王威. Nb、V微合金化Q355B钢的组织与性能[J]. 金属热处理, 2025, 50(4): 48-54.
[2]	杨少朋, 赵爱军, 张炎杰, 王可印, 许晶晶, 张经纬. 国内外高Mo型压铸模具钢的研究现状[J]. 金属热处理, 2025, 50(4): 65-71.
[3]	刘浩, 赵雷杰, 王艳辉, 张孜, 周骞, 曾洪涛, 杨国强, 岳赟. 奥氏体晶粒细化与亚Ms点等温淬火协同作用对中碳贝氏体钢组织与性能的影响[J]. 金属热处理, 2025, 50(4): 143-148.
[4]	齐祥羽, 赵苗苗, 杜林秀, 严玲. 晶粒细化与析出相耦合作用对304不锈钢晶间腐蚀行为的影响[J]. 金属热处理, 2025, 50(4): 149-155.
[5]	李海宏, 朱留平, 庞学东, 孙勇, 迟宏宵, 谷金波. Cr-Co-Mo轴承钢的渗碳层组织及摩擦磨损性能[J]. 金属热处理, 2025, 50(4): 264-269.
[6]	贺帅, 洪晓莉, 赵金环, 刘鑫, 秦哲, 王军生. Cr8Mo2SiV钢中碳化物析出行为的原位观察[J]. 金属热处理, 2025, 50(3): 214-219.
[7]	陈洁明, 苏军锋, 王硕, 李雪峰. 1Cr17Ni2不锈钢螺栓断裂原因分析[J]. 金属热处理, 2025, 50(3): 303-306.
[8]	杨斯媛, 李爱国, 罗平, 张文良, 李贤君, 张明皓, 安伟骋, 王恺择. 一种无碳化物贝氏体钢的CCT与TTT曲线[J]. 金属热处理, 2025, 50(2): 74-80.
[9]	李昌昊, 刘智, 章小峰, 杨永, 周华生, 赵鑫磊. Fe-Mn-Al-C系低密度钢中κ-碳化物研究进展[J]. 金属热处理, 2025, 50(1): 22-30.
[10]	李忠波, 胡海江, 何平, 任可, 袁清, 吴润. 淬火和回火温度对Cr-Mo系耐磨钢组织及力学性能的影响[J]. 金属热处理, 2025, 50(1): 88-96.
[11]	严昊明, 于朋翰, 于兴福. 高端数控机床导轨用灰铸铁感应淬火裂纹成因分析[J]. 金属热处理, 2025, 50(1): 282-286.
[12]	孙陶安, 吴正义, 周继顺, 肖丙政, 王海川, 范鼎东, 邓爱军. Mo含量对高碳钢组织和耐磨性的影响[J]. 金属热处理, 2024, 49(9): 64-71.
[13]	高兴成, 吴博雅, 吴晓春. 4Cr5Mo2V热作模具钢的CCT曲线及碳化物沿晶析出温度测定[J]. 金属热处理, 2024, 49(9): 72-79.
[14]	任鹏帅, 秦凤, 周骞, 赵雷杰, 崔护, 彭子奥, 武常生. 等温淬火对含铝无碳化物贝氏体钢组织和性能的影响[J]. 金属热处理, 2024, 49(9): 103-109.
[15]	白瑞, 杜云飞, 贺秀丽, 梁红玉. Al含量对高锰高铝轻质钢组织和力学性能的影响[J]. 金属热处理, 2024, 49(8): 48-52.

GB/T 7216—2023《灰铸铁金相检验》标准解读

Interpretation of standard GB/T 7216—2023 Metallographic test for gray cast iron

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价