固溶处理对Cr23Ni7Mo2Cu0.6双相不锈钢组织与性能的影响

doi:10.13251/j.issn.0254-6051.2022.06.010

金属热处理 ›› 2022, Vol. 47 ›› Issue (6): 59-63.DOI: 10.13251/j.issn.0254-6051.2022.06.010

固溶处理对Cr23Ni7Mo2Cu0.6双相不锈钢组织与性能的影响

陈佳俊, 朱治愿, 李建强, 王守乾

江苏科技大学材料科学与工程学院, 江苏镇江 212000

收稿日期:2022-01-18 修回日期:2022-04-09 出版日期:2022-06-25 发布日期:2022-07-05
通讯作者: 朱治愿,教授,硕士,E-mail:salanganezhu@163.com
作者简介:陈佳俊(1997—),男,硕士研究生,主要研究方向为高导高强铜合金,E-mail:1912199247@qq.com。
基金资助:
江苏省重点研发计划(BE2017143)

Effect of solution treatment on microstructure and properties of Cr23Ni7Mo2Cu0.6 duplex stainless steel

Chen Jiajun, Zhu Zhiyuan, Li Jianqiang, Wang Shouqian

School of Materials Science and Engineering, Jiangsu University of Science and Technology, Zhenjiang Jiangsu 212000, China

Received:2022-01-18 Revised:2022-04-09 Online:2022-06-25 Published:2022-07-05

摘要/Abstract

摘要： 利用XSL-4-12箱式热处理炉、ZEISS金相显微镜、HRS-150数显洛氏硬度计及拉伸试验机研究了固溶处理对Cr23Ni7Mo2Cu0.6双相不锈钢组织与性能的影响。结果表明,铁素体含量随着固溶温度的升高而增加,在930~960 ℃之间铁素体与奥氏体面积比达到1∶1,σ相的含量随着固溶温度的升高而逐渐减少,在960 ℃时仅有少量σ相存在于相界处,1020 ℃时由于锻造造成的奥氏体相分布不均的情况也得到了改善。合金硬度与抗拉强度随着固溶温度的上升呈现先下降后上升的趋势,分别在1020 ℃和1050 ℃达到最小值94.4 HRB和547 MPa,伸长率则随着固溶温度的升高呈现先上升后下降的趋势,在990 ℃时达到峰值41.5%。综合钢丝拉拔变形过程中材料的硬度、塑韧性及组织均匀性对材料成形性能的影响,Cr23Ni7Mo2Cu0.6双相不锈钢的固溶温度宜选择1020 ℃。

关键词: Cr23Ni7Mo2Cu0.6双相不锈钢, 固溶处理, σ相, 组织, 性能

Abstract: Effect of solution treatment on microstructure and properties of Cr23Ni7Mo2Cu0.6 duplex stainless steel was studied by XSL-4-12 box heat treatment furnace, Zeiss metallographic microscope, HRS-150 digital Rockwell hardness tester and tensile test machine. The results show that the content of ferrite increases with the increase of solution temperature, and the area ratio of ferrite to austenite reaches 1∶1 between 930 ℃ and 960 ℃. The content of σ phase decreases with the increase of solution temperature, only a small amount of σ phase exists at phase boundary at 960 ℃, and the uneven distribution of austenite phase due to forging at 1020 ℃ is also improved. The hardness and tensile strength of the alloy decrease at first and then increase with the increase of solution temperature, reaching the minimum values of 94.4 HRB at 1020 ℃ and 547 MPa at 1050 ℃, respectively. The elongation increases at first and then decreases with the increase of solution temperature, reaching a peak value of 41.5% at 990 ℃. Considering the effects of hardness, plasticity, toughness and microstructure uniformity of the material on formability of the material during drawing and deformation of the steel wire, the optimal solution temperature of the Cr23Ni7Mo2Cu0.6 duplex stainless steel is 1020 ℃.

Key words: Cr23Ni7Mo2Cu0.6 duplex stainless steel, solution treatment, σ phase, microstructure, properties

中图分类号:

TG156.94

陈佳俊, 朱治愿, 李建强, 王守乾. 固溶处理对Cr23Ni7Mo2Cu0.6双相不锈钢组织与性能的影响[J]. 金属热处理, 2022, 47(6): 59-63.

Chen Jiajun, Zhu Zhiyuan, Li Jianqiang, Wang Shouqian. Effect of solution treatment on microstructure and properties of Cr23Ni7Mo2Cu0.6 duplex stainless steel[J]. Heat Treatment of Metals, 2022, 47(6): 59-63.

参考文献

[1]Parayil T R, Howell P R. Decomposition of deformed ferrite in a duplex stainless steel[J]. Material Science and Technology, 1986, 2(11): 1131-1139.
[2]Peick W, Pohl M, Padilha A F. Recrystallization-transformation combined reactions during annealing of a cold rolled ferritic-austenitic duplex stainless steel[J]. ISIJ International, 1998, 38(6): 567-571.
[3]Lo K H, Shek C H, Lai J K L. Recent developments in stainless steels[J]. Materials Science and Engineering R-Reports, 2009, 65(4-6): 39-104.
[4]Maehara Y, Koike M, Fujino N, et al. Precipitation of σ phase in a 25Cr-7Ni-3Mo duplex phase stainless steel[J]. Transactions of the Iron and Steel Institute of Japan, 1983, 23(3): 240-246.
[5]Han Y, Zou D N, Zhang W, et al. Sigma phase precipitation of duplex stainless steel and its effect on corrosion resistance[J]. Materials Science Forum, 2009, 620-622: 391-394.
[6]刘燕, 高仁强, 陈兴润, 等. 2205双相不锈钢中σ相析出的影响因素分析[J]. 金属热处理, 2021, 46(3): 180-183.
Liu Yan, Gao Renqiang, Chen Xingrun, et al. Analysis of influencing factors of σ phase precipitation in 2205 duplex stainless steel[J]. Heat Treatment of Metals, 2021, 46(3): 180-183.
[7]高晓丹, 任学平, 李晶琨, 等. 时效工艺对2205双相不锈钢σ相析出行为的影响[J]. 金属热处理, 2020, 45(10): 1-5.
Gao Xiaodan, Ren Xueping, Li Jingkun, et al. Effect of aging process on σ phase precipitation of 2205 duplex stainless steel[J]. Heat Treatment of Metals, 2020, 45(10): 1-5.
[8]王小勇, 黄乐庆, 王海宝, 等. 固溶处理对双相不锈钢组织与性能的影响[J]. 金属热处理, 2018, 43(5): 101-105.
Wang Xiaoyong, Huang Leqing, Wang Haibao, et al. Influence of solution treatment on microstructure and properties of duplex stainless steel[J]. Heat Treatment of Metals, 2018, 43(5): 101-105.
[9]Shek C H, Wong K W, Lai J K L, et al. Hot tensile properties of 25Cr-8Ni duplex stainless steel containing cellular (σ+γ₂) structure after various thermal treatments[J]. Materials Science and Engineering A, 1997, 231(1/2): 42-47.
[10]Shek C H, Li D J, Wong K W, et al. Creep properties of aged duplex stainless steels containing σ phase[J]. Materials Science and Engineering A, 1999, 266(1/2): 30-36.
[11]Wang Y Q, Han J, Wu H C, et al. Effect of sigma phase precipitation on the mechanical and wear properties of Z3CN20.09M cast duplex stainless steel[J]. Nuclear Engineering and Design, 2013, 259: 1-7.
[12]Badji R, Bouabdallah M, Bacroix B, et al. Phase transformation and mechanical behavior in annealed 2205 duplex stainless steel welds[J]. Materials Characterization, 2008, 59(4): 447-453.
[13]Moayed M H, Laycock N J, Newman R C. Dependence of the critical pitting temperature on surface roughness[J]. Corrosion Science, 2003, 45(6): 1203-1216.
[14]Sieurin H, Sandström R. Austenite reformation in the heat-affected zone of duplex stainless steel 2205[J]. Materials Science and Engineering A, 2006, 418(1/2): 250-256.
[15]Gideon B, Ward L, Biddle G. Duplex stainless steel welds and their susceptibility to intergranular corrosion[J]. Journal of Minerals and Materials Characterization and Engineering, 2008, 7(3): 247-263.
[16]Liou H Y, Hsieh R H, Tsai W T. Microstructure and pitting corrosion in simulated heat-affected zones of duplex stainless[J]. Materials Chemistry and Physics, 2002, 74(1): 33-42.
[17]Chen T H, Yang J R. Microstructural characterization of simulated heat affected zone in a nitrogen-containing 2205 duplex stainless steel[J]. Materials Science and Engineering A, 2002, 338(1/2): 166-181.

固溶处理对Cr23Ni7Mo2Cu0.6双相不锈钢组织与性能的影响

Effect of solution treatment on microstructure and properties of Cr23Ni7Mo2Cu0.6 duplex stainless steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	谷国超, 李瑞芬, 辛振民, 相立新, 许文花, 吕宇鹏. 固溶温度对2507双相不锈钢力学性能及耐蚀性的影响[J]. 金属热处理, 2022, 47(6): 1-6.
[2]	吴杨, 黄晖, 石薇, 文胜平, 吴晓蓝, 荣莉, 魏午. 固溶时效处理对Al-Cu-Mn-Er铸造合金力学性能和显微组织的影响[J]. 金属热处理, 2022, 47(6): 7-12.
[3]	贾新云, 陈升平, 宗毳, 谭永宁, 黄朝晖. DD5合金单晶双联整铸导向叶片的热工艺匹配性[J]. 金属热处理, 2022, 47(6): 13-18.
[4]	田亚强, 赵志浩, 杨子旋, 徐海卫, 韩赟, 郑小平, 李红斌, 陈连生. 温轧温度对中碳钢组织与力学性能的影响[J]. 金属热处理, 2022, 47(6): 19-24.
[5]	蒋明忠, 赵勇, 潘钱付, 吴裕, 王馨敏, 蒋文龙. F/M钢包壳管材热处理工艺优化[J]. 金属热处理, 2022, 47(6): 25-32.
[6]	翟传田, 孙有平, 何江美, 孟祥超, 万斯雨. 轧制变形量对Mg-Zn-Y合金组织和性能的影响[J]. 金属热处理, 2022, 47(6): 39-45.
[7]	李晓琛, 王世颖, 华天宇, 陈智栋. 深冷处理对TC4钛合金退火过程中微观组织和力学性能的影响[J]. 金属热处理, 2022, 47(6): 46-53.
[8]	冯树明, 万德成, 胡进朋, 李杰. 配分温度对0.2C-2.96Mn-1.73Si钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(6): 54-58.
[9]	于娟, 冯朝辉, 赵唯一, 姚勇, 游文. 预拉伸变形量对2050铝锂合金组织和性能的影响[J]. 金属热处理, 2022, 47(6): 64-68.
[10]	白兴红, 赵席春, 赵德利, 王大鹏, 南玉静. 冷却速度对支承辊用Cr5钢显微组织与力学性能的影响[J]. 金属热处理, 2022, 47(6): 69-71.
[11]	徐新犬, 方舟, 刘新宽, 王子延. 热处理对铜铝低温钎焊的影响[J]. 金属热处理, 2022, 47(6): 78-84.
[12]	严翔, 李德发, 官计生, 杨治争. 形变对低碳微合金化热处理钢组织和性能的影响[J]. 金属热处理, 2022, 47(6): 85-88.
[13]	吴文津, 李相辉, 李雪辰, 陈晶阳, 汤鑫. 固溶处理对K447A高温合金碳化物组织的影响[J]. 金属热处理, 2022, 47(6): 89-92.
[14]	韩颢源, 杨涛, 邱娟, 杨刚, 余万华, 翟月雯, 周乐育. 固溶处理对TC4合金组织和硬度的影响[J]. 金属热处理, 2022, 47(6): 93-97.
[15]	钟彬, 陈义庆, 李琳, 高鹏, 伞宏宇, 艾芳芳, 田秀梅. 淬火油温对40CrMnMo钢钻杆组织和性能的影响[J]. 金属热处理, 2022, 47(6): 98-102.