稳定化处理对347H不锈钢第二相及性能的影响

doi:10.13251/j.issn.0254-6051.2021.07.028

摘要/Abstract

摘要： 通过JMatPro软件对347H不锈钢相图进行模拟,并结合生产工艺分析其稳定化温度对第二相、力学性能及耐腐蚀性能的影响。结果表明:347H钢凝固过程中第二相主要为NbN、Nb(C,N)、M₂₃C₆、σ相和Z相。1140 ℃固溶后的第二相主要为Nb(C, N)和少量NbN、M₂₃C₆,相尺寸约为0.5 μm。经800~1000 ℃稳定化退火处理后,晶粒尺寸随稳定化温度的增加变化较小,晶粒度为7.5级,第二相随稳定化温度的升高,尺寸显著长大到5 μm以上,经EDS分析表明,数量增加和长大的第二相主要为NbC。800 ℃和850 ℃稳定化退火后347H钢的屈服强度较高,抗拉强度随稳定化温度的升高变化不大。稳定化退火后347H钢的腐蚀速率较固溶态的腐蚀速率低,稳定化退火提升了347H钢的耐晶间腐蚀性能。

关键词: 347H不锈钢, 稳定化, 第二相, 性能

Abstract: Phase diagram of the 347H stainless steel was simulated by JMatPro software, and the effect of stabilization temperature on second phase, mechanical properties and corrosion resistance were analyzed. The results show that the second phase of the 347H steel during solidification is mainly NbN, Nb(C,N), M₂₃C₆, σ phase and Z phase. The second phase after solid solution at 1140 ℃ is mainly Nb (C, N) and a small amount of NbN and M₂₃C₆, with the size of about 0.5 μm.After stabilization at 800-1000 ℃, the grain size of the steel plate changes little with the increase of stabilization temperature,and the grain size is 7.5 grade. With the increase of stabilization temperature, the size of the second phase grows significantly to over 5 μm, and EDS analysis shows that NbC is the main secondary phase. The yield strength of the 347H steel stabilized at 800 ℃ and 850 ℃ is higher, and the tensile strength changes little with the increase of stabilizing temperature. The corrosion rate of the stabilized steel is lower than that of the solid solution state, and the intergranular corrosion resistance of the 347H steel is improved.

Key words: 347H stainless steel, stabilization, second phase, property

中图分类号:

刘天增, 王珂, 陈安忠, 李鸿亮. 稳定化处理对347H不锈钢第二相及性能的影响[J]. 金属热处理, 2021, 46(7): 149-154.

Liu Tianzeng, Wang Ke, Cheng Anzhong, Li Hongliang. Effect of stabilization treatment on second phase and properties of347H stainless steel[J]. Heat Treatment of Metals, 2021, 46(7): 149-154.

参考文献

[1] 戴真全. 347H奥氏体不锈钢的焊接热裂纹和再热裂纹[J]. 化工设备与管道, 2010, 47(3): 54-58.
Dai Zhenquan. Heat crack and reheat crack in weld in austenitic steel 347H[J]. Process Equipment and Piping, 2010, 47(3): 54-58.
[2] 谷宇, 孙铭山, 范光伟. 铌含量对17%Cr超纯铁素体不锈钢组织与高温强度的影响[J]. 钢铁, 2011, 46(1): 71-74, 85.
Gu Yu, Sun Mingshan, Fan Guangwei. Effect of Nb content on microstructure and high temperature strength of 17%Cr ferritic stainless steel[J]. Iron and Steel, 2011, 46(1): 71-74, 85.
[3] 张朝晖, 柳永宁, 金波, 等. 铌微合金钢形变连续冷却过程中的相变[J]. 机械工程材料, 2007, 31(4): 85-88.
Zhang Zhaohui, Liu Yongning, Jin Bo, et al. Continuous cooling transformation of Nb micro-alloyed steel after deformation[J]. Materials for Mechanical Engineering, 2007, 31(4): 85-88.
[4] 王新华, 昌波, 李景捷, 等. 700-1000 ℃间含Nb钢铸坯的延塑性降低与Nb(C, N)析出[J]. 金属学报, 1997, 33(5): 485-491.
Wang Xinhua, Chang Bo, Li Jingjie, et al. Ductility loss and Nb(C,N) precipitation in Nb-containing steel slab in the temperature range from 700 to 1000 ℃[J]. Acta Metallrugica Sinica, 1997, 33(5): 485-491.
[5] 李新梅, 张忠文, 杜宝帅, 等. 长期高温服役后S31042奥氏体耐热钢的微观组织[J]. 金属热处理, 2019, 44(4): 171-174.
Li Xinmei, Zhang Zhongwen, Du Baoshuai, et al. Microstructure of S31042 austenite heat resistant steel after long-term service under high temperature[J]. Heat Treatment of Metals, 2019, 44(4): 171-174.
[6] Lseda A, Okada H, Semba H, et al. Long term creep properties and microstructure of SUPER304H, TP347HFG and HR3C for A-USC boilers[J]. Energy Materials, 2007, 2(4): 199-206.
[7] Viswanathan R, Coleman K, Rao U. Materials for ultra-supercritical coal-fired power plant boilers[J]. International Journal of Pressure Vessels and Piping, 2006, 83(11): 778-783.
[8] 杜宝帅, 刘睿, 张忠文, 等. 高温长时服役HR₃C钢焊接接头的组织与性能[J]. 金属热处理, 2015, 40(2): 52-55.
Du Baoshuai, Liu Rui, Zhang Zhongwen, et al. Microstructure and properties of HR3C steel weld joint exposed to elevated temperature for long-term[J]. Heat Treatment of Metals, 2015, 40(2): 52-55.
[9] 张文华. 不锈钢及其热处理[M]. 沈阳: 辽宁科学技术出版社, 2010.
[10] 杜伟, 孙全社, 江来珠, 等. 铌与钛对铁素体不锈钢析出和成形性的影响[J]. 钢铁研究学报, 2010, 22(3): 48-51.
Du Wei, Sun Quanshe, Jiang Laizhu, et al. Effect of Nb and Ti on precipitation and formability of ferritic stainless steel[J]. Journal of Iron and Steel Research, 2010, 22(3): 48-51.
[11] 康永海, 李具仓. 304L和321不锈钢耐腐蚀性能研究[J]. 热加工工艺, 2015, 44(6): 81-88.
Kang Yonghai, Li Jucang. Corrosion resistance of 304L and 321 stainless steel[J]. Hot Working Technology, 2015, 44(6): 81-88.
[12] 张泽磊, 姚正军, 张平则, 等. 冷弯加工对国产301L不锈钢耐点蚀性能的影响[J]. 中国冶金, 2015, 25(7): 5-9.
Zhang Zelei, Yao Zhengjun, Zhang Pingze, et al. Influence of cold bending process on pitting corrosion resistance of domestic 301L stainless steel[J]. China Metallurgy, 2015, 25(7): 5-9.
[13] 孙涛, 邓博, 徐菊良, 等. 氮、铌添加对奥氏体不锈钢电化学腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2010, 30(6): 421-425.
Sun Tao, Deng Bo, Xu Juliang, et al. Influence of niobium and nitrogen on the resistance to pitting and intergranular corrosion of 304 austenitic stainless steel[J]. Journal of Chinese Society for Corrosion and Protection, 2010, 30(6): 421-425.
[14] 宁小智, 邢长军, 雍歧龙, 等. 氮含量对无镍奥氏体不锈钢理化性能的影响[J]. 中国冶金, 2019, 29(6): 34-37.
Ning Xiaozhi, Xing Changjun, Yong Qilong, et al. Effects of nitrogen content on physical and chemical properties of nickel-free austenitic stainless steels[J]. China Metallurgy, 2019, 29(6): 34-37.

[1]	王玉岱, 刘洋, 朱言言, 田象军, 程序, 冉先喆, 钱婷婷. 热处理对复合制造AerMet100超高强度钢组织均匀性与拉伸性能的影响[J]. 金属热处理, 2022, 47(4): 1-9.
[2]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[3]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[4]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[5]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[6]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[7]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[8]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[9]	陈思君, 陈送义, 陈庚, 袁丁玲, 陈康华. Mg含量对2A14铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 86-92.
[10]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[11]	白青青, 张志宏, 郑淮北, 王英虎. 2507超级双相不锈钢中σ相的析出行为[J]. 金属热处理, 2022, 47(4): 108-115.
[12]	陈刚, 罗小兵, 柴锋, 杨才福, 张正延, 杨丽. 轧制加热温度对高强度低合金钢组织及冲击性能的影响[J]. 金属热处理, 2022, 47(4): 116-121.
[13]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[14]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.
[15]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.