发动机用SCM435钢的组织与疲劳性能

doi:10.13251/j.issn.0254-6051.2024.03.027

金属热处理 ›› 2024, Vol. 49 ›› Issue (3): 159-163.DOI: 10.13251/j.issn.0254-6051.2024.03.027

发动机用SCM435钢的组织与疲劳性能

江畅¹, 陆恒昌^1,2, 韦习成^1,2, 董瀚^1,2

1.上海大学材料科学与工程学院, 上海 200444;
2.上海大学 (浙江)高端装备基础件材料研究院, 浙江嘉善 314113

收稿日期:2023-09-21 修回日期:2023-12-29 出版日期:2024-03-25 发布日期:2024-04-24
通讯作者: 陆恒昌,博士,讲师,E-mail:luhengchang@shu.edu.cn
作者简介:江畅(1998—),女,硕士研究生,主要研究方向为汽车发动机关键紧固件用SCM435钢,E-mail:jiangchang0210@163.com。
基金资助:
上海市军民融合发展专项资金(2020-jmrh1-kj31)

Microstructure and fatigue properties of SCM435 steel for engines

Jiang Chang¹, Lu Hengchang^1,2, Wei Xicheng^1,2, Dong Han^1,2

1. School of Materials and Science Engineering, Shanghai University, Shanghai 200444, China;
2. Zhejiang Institute of Advanced Materials, Shanghai University, Jiashan Zhejiang 314113, China

Received:2023-09-21 Revised:2023-12-29 Online:2024-03-25 Published:2024-04-24

摘要/Abstract

摘要： 采用SEM、TEM以及拉伸测试等研究SCM435钢在870 ℃淬火、350~650 ℃回火后的组织和力学性能。结果表明,回火温度为350 ℃时,其组织是板条马氏体及少量碳化物;随着回火温度的升高,马氏体的板条形态逐渐消失,碳化物沿板条方向析出长大,其中525 ℃回火后的组织尚有明显的马氏体板条形态并弥散分布着短棒状渗碳体。在试验回火温度范围内调控SCM435钢的力学性能,可以满足8.8~12.9级紧固件的力学性能要求。试验验证了870 ℃淬火+525 ℃回火钢的疲劳性能,中值疲劳极限σ_a50为425 MPa,具有较好的疲劳性能。

关键词: SCM435钢, 回火温度, 微观组织, 力学性能, 疲劳性能

Abstract: Microstructure and mechanical properties of SCM435 steel quenched at 870 ℃ and tempered at 350-650 ℃ were studied by means of SEM, TEM and tensile test. The results show that when tempering temperature is 350 ℃, the structure is martensite lath and a small amount of carbide. With the increase of tempering temperature, the lath morphology of martensite gradually disappears, and carbides precipitate and grow along the direction of lath. The microstructure tempered at 525 ℃ still has obvious martensite lath morphology and short rod cementite is dispersed. By controlling the mechanical properties of the SCM435 steel within the studied tempering temperature range, it can meet the mechanical performance requirements of 8.8-12.9 level fasteners. The fatigue properties of the steel quenched at 870 ℃ and tempered at 525 ℃ is experimentally verified, with a median fatigue limit of 425 MPa, indicating good fatigue properties.

Key words: SCM435 steel, tempering temperature, microstructure, mechanical properties, fatigue properties

中图分类号:

TG156.5

江畅, 陆恒昌, 韦习成, 董瀚. 发动机用SCM435钢的组织与疲劳性能[J]. 金属热处理, 2024, 49(3): 159-163.

Jiang Chang, Lu Hengchang, Wei Xicheng, Dong Han. Microstructure and fatigue properties of SCM435 steel for engines[J]. Heat Treatment of Metals, 2024, 49(3): 159-163.

参考文献

[1]Sun Y, Qingbo Y U. Study on microstructure and properties of cold heading steel SCM435[J]. Hot Working Technology, 2011, 40(24): 60-63.
[2]黄传明, 罗永华. 热处理工艺对35CrMo钢组织及性能的影响分析[J]. 中国金属通报, 2018(3): 189-190.
[3]董瀚, 廉心桐, 胡春东, 等. 钢的高性能化理论与技术进展[J]. 金属学报, 2020, 56(4): 558-582.
Dong Han, Lian Xintong, Hu Chundong, et al. High performance steels: The scenario of theory and technology[J]. Acta Metallurgica Sinica, 2020, 56(4): 558-582.
[4]徐海峰, 李海, 李凤敏, 等. 淬火及回火处理对新型槽帮钢30MnSiCrMo组织性能的影响[J]. 特殊钢, 2023, 44(1): 105-110.
Xu Haifeng, Li Hai, Li Fengmin, et al. Effect of quenching and tempering heat treatment on microstructure and properties of new-type slot edge steel 30MnSiCrMo[J]. Special Steel, 2023, 44(1): 105-110.
[5]成慧梅, 冯俊鹏, 孙电强, 等. 调质处理工艺对微合金化Q960E钢70 mm板组织性能的影响[J]. 特殊钢, 2022, 43(5): 78-81.
Cheng Huimei, Feng Junpeng, Sun Dianqiang, et al. Effect of quenching-tempering process on microstructure and properties of micro-alloying Q960E steel 70 mm thickness plate[J]. Special Steel, 2022, 43(5): 78-81.
[6]董瑞, 陈林, 岑耀东, 等. 不同热处理条件下贝氏体钢的微观组织和疲劳裂纹扩展[J]. 金属热处理, 2022, 47(2): 153-158.
Dong Rui, Chen Lin, Cen Yaodong, et al. Microstructure and fatigue crack growth of a bainitic steel under different heat treatments[J]. Heat Treatment of Metals, 2022, 47(2): 153-158.
[7]林文政, 田荣斌, 贾礼, 等. 回火温度对20SiMnMo高强度钢微观组织与力学性能的影响[J]. 特殊钢, 2022, 43(3): 74-78.
Lin Wenzheng, Tian Rongbin, Jia Li, et al. Effect of tempering temperature on microstructure and mechanical properties of 20SiMnMo high strength steel[J]. Special Steel, 2022, 43(3): 74-78.
[8]张旭, 何文超, 李东辉, 等. 热作模具钢热疲劳机理及性能改善的研究现状[J]. 金属热处理, 2020, 45(9): 10-20.
Zhang Xu, He Wenchao, Li Donghui, et al. Research status of thermal fatigue mechanisms and performance improvement of hot work die steel[J]. Heat Treatment of Metals, 2020, 45(9): 10-20.
[9]Kathikeyan M K, Gupta R K, Kumar V A, et al. Development of hardening and tempering cycle for high strength low alloy fastener grade steel[J]. Materials Science Forum, 2012, 710: 506-510.
[10]Wang L J, Cai Q W, Wu H B, et al. Effects of tempering temperature on the microstructure and mechanical properties of 1500 MPa grade steel directly quenched[J]. Journal of University of Science and Technology Beijing, 2010, 32(9): 1150-1156, 1162.
[11]苏磊, 刘海红. 热处理工艺对35CrMo钢组织及性能的影响[J]. 金属热处理, 2016, 41(6): 73-78.
Su Lei, Liu Haihong. Influence of heat treatment on microstructure and mechanical properties of 35CrMo steel[J]. Heat Treatment of Metals, 2016, 41(6): 73-78.
[12]代发明, 蒋欣, 王凌旭, 等. 回火温度对35CrMo钢显微组织和力学性能的影响[J]. 机械工程材料, 2018, 42(9): 73-77.
Dai Faming, Jiang Xin, Wang Lingxu, et al. Effect of tempering temperature on microstructure and mechanical properties of 35CrMo steel[J]. Materials for Mechanical Engineering, 2018, 42(9): 73-77.
[13]李永义, 顾海龙. 35CrMo钢的调质工艺控制[J]. 材料开发与应用, 2012, 27(5): 20-22.
Li Yongyi, Gu Hailong. Quenching and tempering process control of 35CrMo steel[J]. Development and Application of Materials, 2012, 27(5): 20-22.
[14]陈继林, 张育明, 孟一, 等. 发动机缸盖螺栓疲劳断裂失效分析[J]. 金属热处理, 2023, 48(2): 308-313.
Chen Jilin, Zhang Yuming, Meng Yi, et al. Failure analysis of fatigue fracture of engine cylinder head bolts[J]. Heat Treatment of Metals, 2023, 48(2): 308-313.
[15]Smoljan B. Prediction of mechanical properties and microstructure distribution of quenched and tempered steel shaft[J]. Journal of Materials Processing Technology, 2006, 175(1/3): 393-397.
[16]Gao C, Yang M Q, Pang J C, et al. Abnormal relation between tensile and fatigue strengths for a high-strength low-alloy steel[J]. Materials Science and Engineering A, 2022, 832: 142418.
[17]石虹. 高强度螺栓失效若干因素的研究[D]. 沈阳: 东北大学, 2012.
Shi Hong. Research of high strength bolt failure caused by several factors[D]. Shenyang: Northeast University, 2012.
[18]Liu S, Liu D, Liu S. Effect of heat treatment on fatigue resistance of spring steel 60Si2CrVAT[J]. Metal Science and Heat Treatment, 2010, 52(1/2): 57-60.
[19]顾晓勇, 刘洪武, 刘浩然, 等. 回火温度对NHL10耐候高强度螺栓钢组织和力学性能的影响[J]. 上海金属, 2020, 42(2): 44-49, 56.
Gu Xiaoyong, Liu Hongwu, Liu Haoran, et al. Effect of tempering temperature on microstructure and mechanical properties of NHL10 weatherpoof steel for high-strength bolt[J]. Shanghai Metals, 2020, 42(2): 44-49, 56.
[20]Yang L, Gao S, Huang Y, et al. Effect of microstructure on tensile and fatigue properties of laser-welded DP780 and DP980 high-strength steel joints[J]. Materials Science and Engineering, 2019, 754(29): 535-555.

发动机用SCM435钢的组织与疲劳性能

Microstructure and fatigue properties of SCM435 steel for engines

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	徐开泰, 刘骐升, 尤凯司, 刘照宇, 张峻嘉. 低温冷轧与时效处理对Cu-Ni-Co-Si合金组织性能的影响[J]. 金属热处理, 2024, 49(3): 1-6.
[2]	李晓亮, 程晓英, 王兆丰, 任毓文, 曾繁宇. 回火温度对Nb、V合金化低合金高强度钢氢脆敏感性的影响[J]. 金属热处理, 2024, 49(3): 7-14.
[3]	赵鑫磊, 袁晓飞, 乔珺威. 固溶温度对K424合金显微组织与力学性能的影响[J]. 金属热处理, 2024, 49(3): 15-21.
[4]	张禹, 于金瑞, 于鑫泓, 冯以盛, 张云山, 赵而团. 等温淬火温度对50CrVA钢组织与性能的影响[J]. 金属热处理, 2024, 49(3): 28-32.
[5]	张立生, 王小巩. 热轧变形对高铝316L不锈钢微观组织与性能的影响[J]. 金属热处理, 2024, 49(3): 33-36.
[6]	谢谱, 赵吉庆, 颜廷亭. 回火工艺对HT9钢组织和力学性能的影响[J]. 金属热处理, 2024, 49(3): 44-49.
[7]	王亚勇, 曹喜娟, 任广笑, 刘永哲, 郑云凯. 热处理对差压铸造ZL201A铝合金壳体内部组织及性能的影响[J]. 金属热处理, 2024, 49(3): 108-111.
[8]	王娇娇, 赵林林, 高云哲, 石帅, 武晓龙, 赵燕青, 周玉青, 弓俊杰. 回火温度对深井石油套管用钢组织性能的影响[J]. 金属热处理, 2024, 49(3): 112-115.
[9]	张瑞, 唐恩, 袁清, 任杰, 莫家璇. 快速退火对冷轧超低碳钢组织和性能的影响[J]. 金属热处理, 2024, 49(3): 116-121.
[10]	刘鹏飞, 关琳, 刘建, 陈宇, 刘宏亮. 退火工艺对低成本980 MPa级冷轧双相钢组织和性能的影响[J]. 金属热处理, 2024, 49(3): 122-127.
[11]	汪英芝, 郑留伟, 杨飞, 聂豫晋, 孟立鑫, 尹磊, 梁伟. 选区激光熔化Inconel 718合金的沉淀析出行为及力学性能[J]. 金属热处理, 2024, 49(3): 141-146.
[12]	黄志国, 李艳艳, 蒋波. 连续油管用低碳微合金钢控轧控冷显微组织与疲劳性能[J]. 金属热处理, 2024, 49(3): 153-158.
[13]	张浩, 迟宏宵, 王成蹊, 马党参, 林鹏. V含量对高氮马氏体不锈钢组织及性能的影响[J]. 金属热处理, 2024, 49(3): 215-221.
[14]	唐贝, 王海丽, 付金龙, 胥珊娜. 微量Ce对热挤压态Mg-2Zn-0.4Ca-0.2Mn合金微观组织、力学性能及导热性的影响[J]. 金属热处理, 2024, 49(3): 222-229.
[15]	刘禹, 孙迎建. 合金元素Si、V、Ti对40Cr13马氏体不锈钢组织与性能的影响[J]. 金属热处理, 2024, 49(3): 256-261.