蒸汽氧化T-250钢的力学性能和耐蚀性能

doi:10.13251/j.issn.0254-6051.2024.01.038

金属热处理 ›› 2024, Vol. 49 ›› Issue (1): 234-241.DOI: 10.13251/j.issn.0254-6051.2024.01.038

蒸汽氧化T-250钢的力学性能和耐蚀性能

张小娟¹, 王军喜¹, 白鹭¹, 周钟平¹, 倪林彧¹, 赵雨薇², 闵永安²

1. 上海航天动力技术研究所, 上海 201109;
2. 上海大学材料科学与工程学院省部共建高品质特殊钢冶金与制备国家重点实验室, 上海 200444

收稿日期:2023-08-18 修回日期:2023-11-27 发布日期:2024-02-29
作者简介:张小娟(1987—),女,高级工程师,硕士,主要研究方向为金属材料及其热处理,E-mail: 20926061@zju.edu.cn

Mechanical properties and corrosion resistance of steam oxidized T-250 steel

Zhang Xiaojuan¹, Wang Junxi¹, Bai Lu¹, Zhou Zhongping¹, Ni Linyu¹, Zhao Yuwei², Min Yongan²

1. Shanghai Aerospace Power Technology Research Institute, Shanghai 201109, China;
2. State Key Laboratory of Advanced Special Steel, School of Materials Science & Engineering, Shanghai University, Shanghai 200444, China

Received:2023-08-18 Revised:2023-11-27 Published:2024-02-29

摘要/Abstract

摘要： 将蒸汽氧化处理及空气氧化处理后的T-250钢进行拉伸、电化学极化曲线、湿热、盐雾等试验测试,探究蒸汽氧化对T-250钢抗拉强度及伸长率等力学性能及不同环境下耐蚀性能的影响。结果表明,经蒸汽氧化处理的T-250钢具有良好的力学性能,强度能够达到1700 MPa以上,且相较于空气氧化处理具有更优良的隔绝腐蚀效果,未出现蒸汽引起的氢致延迟断裂现象。

关键词: T-250钢, 蒸汽氧化, 氧化膜, 力学性能, 耐蚀性能

Abstract: T-250 steel after steam oxidation treatment and air oxidation treatment was tested by tensile, electrochemical polarization curve, damp heat, salt spray and other tests to explore the effect of steam oxidation on mechanical properties, such as tensile strength and elongation of the T-250 steel and its corrosion resistance in different environments. The results show that the T-250 steel treated by steam oxidation has good mechanical properties and better corrosion isolation effect than that treated by air oxidation, without obvious hydrogen induced delayed fracture caused by steam.

Key words: T-250 steel, steam oxidation, oxide film, mechanical properties, corrosion resistance

中图分类号:

TG178

张小娟, 王军喜, 白鹭, 周钟平, 倪林彧, 赵雨薇, 闵永安. 蒸汽氧化T-250钢的力学性能和耐蚀性能[J]. 金属热处理, 2024, 49(1): 234-241.

Zhang Xiaojuan, Wang Junxi, Bai Lu, Zhou Zhongping, Ni Linyu, Zhao Yuwei, Min Yongan. Mechanical properties and corrosion resistance of steam oxidized T-250 steel[J]. Heat Treatment of Metals, 2024, 49(1): 234-241.

参考文献

[1]周菲. 时效工艺对3D打印18Ni300马氏体时效钢组织及性能的影响[D]. 上海: 上海工程技术大学, 2020.
Zhou Fei. Effect of aging treatment on microstructure and properties of 18Ni300 maraging steel by 3D printing[D]. Shanghai: Shanghai University of Engineering Science Shanghai, 2020.
[2]尹航, 李金许, 宿彦京, 等. 马氏体时效钢的研究现状与发展[J]. 钢铁研究学报, 2014, 26(3): 1-4, 9.
Yin Hang, Li Jinxu, Su Yanjing, et al. Current situation and development of maraging steel[J]. Journal of Iron and Steel Research, 2014, 26(3): 1-4, 9.
[3]李虎, 赵伟江, 李瑞迪, 等. 增材制造马氏体时效钢的研究进展[J]. 中国激光, 2022, 49(14): 23-36.
Li Hu, Zhao Weijiang, Li Ruidi, et al. Progress on additive manufacturing of maraging steel[J]. Chinese Journal of Laser, 2022, 49(14): 23-36.
[4]姜越, 尹钟大, 朱景川, 等. 超高强度马氏体时效钢的发展[J]. 特殊钢, 2004, 25(2): 1-5.
Jiang Yue, Yin Zhongda, Zhu Jingchuan, et al. Development of ultra-high strength maraging steel[J]. Special Steel, 2004, 25(2): 1-5.
[5]刘福广, 席守谋, 张建国, 等. 无钴马氏体时效钢的研究与应用[J]. 金属热处理, 2007, 32(2): 7-11.
Liu Fuguang, Xi Shoumou, Zhang Jianguo, et al. Research application of cobalt free maraging steel[J]. Heat Treatment of Metals, 2007, 32(2): 7-11.
[6]李坤, 单际国, 王春旭, 等. T250马氏体时效钢激光焊接-时效处理接头的强韧性[J]. 金属学报, 2015, 51(8): 904-912.
Li Kun, Shan Jiguo, Wang Chunxu, et al. Strength and toughness of T250 maraging steel joint hybrid-treated with laser welding and aging[J]. Journal of Acta Metallurgica Sinica, 2015, 51(8): 904-912.
[7]徐东东, 陈旸, 许昊, 等. 超高强度马氏体时效钢研究进展[J]. 精密成形工程, 2021, 13(5): 100-108.
Xu Dongdong, Chen Yang, Xu Hao, et al. Research progress of ultra-high strength maraging steel[J]. Journal of Netshape Forming Engineering, 2021, 13(5): 100-108.
[8]Wang G, Yan Y, Li J X, et al. Microstructure effect on hydrogen-induced cracking in TM210 maraging steel[J]. Materials Science and Engineering A, 2013, 586: 142-148.
[9]Andréiad S M C, Hugo R d I, Garcia P S P, et al. Structural characterization of iron oxide grown on 18% Ni-Co-Mo-Ti ferrous base alloy aged under superheated steam atmosphere[J]. The International Journal of Advanced Manufacturing Technology, 2021, 12(21): 1757-1768.
[10]刘忠国, 张景海. 不同热处理制度对T250钢性能的影响[J]. 宝钢技术, 2007, 4(5): 71-74.
Liu Zhongguo, Zhang Jinghai. Effects of different heat treatment system on properties of T250 steel[J]. Journal of Baosteel Technology, 2007, 4(5): 71-74.
[11]Meng F Y, Su T F, Guan J D, et al. Intermediate-temperature oxidation of Fe-Cr-Ni-Mo stainless maraging steel in air[J]. Applied Mechanics and Materials, 2015, 426: 185-189.
[12]门蒙蒙, 杨卓越, 丁雅莉, 等. 时效温度对马氏体时效不锈钢延迟断裂行为的影响[J]. 钢铁研究学报, 2015, 27(2): 60-63.
Men Mengmeng, Yang Zhuoyue, Ding Yali, et al. Effect of aging temperature on delayed facture behavior of maraing stainless steel[J]. Journal of Iron and Steel Research, 2015, 27(2): 60-63.
[13]郑春雷, 张福成, 吕博, 等. 辙叉用贝氏体钢的氢脆特性及去氢退火工艺[J]. 材料热处理学报, 2008, 5(2): 71-75.
Zheng Chunlei, Zhang Fucheng, Lü Bo, et al. Susceptibillity to hydrogen embrittlement and dehydrogenation annealing process of bainite steel used for crossing[J]. Transaction of Materials and Heat Treatment, 2008, 5(2): 71-75.
[14]刘宗昌, 杨慧, 李文学, 等. 去氢退火工艺的设计及应用[J]. 金属热处理, 2003, 28(3): 51-53.
Liu Zongchang, Yang Hui, Li Wenxue, et al. Design applacatin of dehydrogenation annealing process[J]. Heat Treatment of Metals, 2003, 28(3): 51-53.
[15]雷永永, 张宏玉. 金属点蚀行为综述[J]. 全面腐蚀控制, 2016, 30(8): 11-15.
Lei Yongyong, Zhang Hongyu. Summarize the research of metal corrosion behavior[J]. Total Crorrosion Control, 2016, 30(8): 11-15.

蒸汽氧化T-250钢的力学性能和耐蚀性能

Mechanical properties and corrosion resistance of steam oxidized T-250 steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	宋体杰, 王长宇, 王珏, 于妍妍, 卢增威, 金冬岩. 热暴露对Ti55合金显微组织及力学性能的影响[J]. 金属热处理, 2024, 49(1): 15-21.
[2]	朱嘉武, 欧阳晟. 退火对FeCoNi_2-xMnGa_x高熵合金微观组织、力学性能和磁性能的影响[J]. 金属热处理, 2024, 49(1): 22-31.
[3]	孙宁, 徐志远, 杨立民, 李星辉, 张浩, 李延成, 李涛. 不同装炉卷数6016铝合金板材组织性能对比[J]. 金属热处理, 2024, 49(1): 39-47.
[4]	邸抑非, 李佳, 李勇, 赵荣达, 相珺, 伍复发. 固溶时效处理对AlMg5Si2Mn铝合金组织与性能的影响[J]. 金属热处理, 2024, 49(1): 148-153.
[5]	田少鲲, 金圆平, 王萍, 杨堃, 刘晓霏, 郭占, 郁瑞兴, 范庆利. 时效处理对低压铸造ZL114A合金力学性能及显微组织的影响[J]. 金属热处理, 2024, 49(1): 179-185.
[6]	肖昌乐, 吴红艳, 陈伟, 康吉昌, 陈雨楠, 刘鹏举, 王义仁, 王秀宾. 退火温度对8111铝箔微观组织和性能的影响[J]. 金属热处理, 2024, 49(1): 186-192.
[7]	李志平, 王宏霞, 赵刚, 王俊海. 退火工艺对T4003高强度铁素体不锈钢组织和性能的影响[J]. 金属热处理, 2024, 49(1): 198-201.
[8]	赵志刚, 陈建礼, 张锦文, 王松伟, 王育田. 回火工艺对铁路用A3车轴钢组织及力学性能的影响[J]. 金属热处理, 2024, 49(1): 202-205.
[9]	石佩斐, 张辉. 淬火介质对7050铝合金热锻件组织和性能的影响[J]. 金属热处理, 2024, 49(1): 290-295.
[10]	孙博, 聂佳民, 李晓丹, 何长树. 强制冷却和低温时效对2198-T3/7A04-T6异种铝合金FSW接头组织及性能的影响[J]. 金属热处理, 2023, 48(9): 8-13.
[11]	王毅, 韩杰, 刘超, 邓玲蕊, 李辉, 许荣昌. DQ-T工艺对1000 MPa级高强钢组织和性能的影响[J]. 金属热处理, 2023, 48(9): 30-34.
[12]	王建, 宋蕾, 王艺卓, 张全福, 任乃栋, 武维康, 王红霞, 罗小萍. 固溶处理对Mg-1Zn-1Ca合金组织和耐蚀性能的影响[J]. 金属热处理, 2023, 48(9): 48-53.
[13]	韩伟松, 杜峰, 李建锋, 朱宝辉, 沈立华, 刘意, 王鹏. 变形量对Ti80G合金力学性能的影响[J]. 金属热处理, 2023, 48(9): 95-98.
[14]	宋操, 王晓东, 包喜荣, 陈林, 汤雪娇. Ce对30MnNbRE钢淬火回火微观组织和力学性能的影响[J]. 金属热处理, 2023, 48(9): 143-149.
[15]	李文刚, 炊鹏飞, 程尊鹏, 李春梅, 景然, 李江华, 廖仲尼. 硼含量对Ti-Zr-Nb-B合金显微组织及性能的影响[J]. 金属热处理, 2023, 48(9): 157-164.