高磁感取向硅钢27QG090的常化退火工艺

doi:10.13251/j.issn.0254-6051.2023.01.032

金属热处理 ›› 2023, Vol. 48 ›› Issue (1): 186-189.DOI: 10.13251/j.issn.0254-6051.2023.01.032

高磁感取向硅钢27QG090的常化退火工艺

卢晓禹¹, 董磊², 黄利¹, 刘宝志³

1.内蒙古包钢钢联股份有限公司技术中心, 内蒙古包头 014010;
2.内蒙古包钢稀土钢板材有限责任公司, 内蒙古包头 014010;
3.包头市威丰稀土电磁材料股份有限公司, 内蒙古包头 014010

收稿日期:2022-08-17 修回日期:2022-11-11 出版日期:2023-01-25 发布日期:2023-02-03
作者简介:卢晓禹(1985—),男,高级工程师,硕士,主要研究方向为硅钢新产品研发,E-mail: 18747297991@163.com。

Normalizing annealing process of 27QG090 high magnetic induction oriented silicon steel

Lu Xiaoyu¹, Dong Lei², Huang Li¹, Liu Baozhi³

1. Technology Center, Inner Mongolia Baotou Steel Union Co., Ltd., Baotou Inner Mongolia 014010, China;
2. Rare Rarth Steel Plate Co.,Ltd. of Inner Mongolia Baotou Steel Union Co., Ltd., Baotou Inner Mongolia 014010, China;
3. Baotou Weifeng Rare Earth Electromagnetic Materials Co., Ltd., Baotou Inner Mongolia 014010, China

Received:2022-08-17 Revised:2022-11-11 Online:2023-01-25 Published:2023-02-03

摘要/Abstract

摘要： 采用中试试验平台完成高磁感取向硅钢27QG090实验室常化退火工艺过程,利用光学显微镜、X射线衍射仪、透射电镜和能谱仪分析常化退火处理后试样的显微组织和宏观织构。结果表明,高磁感取向硅钢27QG090常化退火后的显微组织为铁素体,宏观织构主要是以α织构、α^*织构、铜型织构为主,兼有微弱的高斯织构,常化退火后的析出物主要是AlN,其平均尺寸约为40 nm。综合分析得出最优的常化退火工艺为1120 ℃×3 min+920 ℃×3 min,100 ℃水淬。

关键词: 取向硅钢, 常化退火, 显微组织, 织构

Abstract: Normalizing annealing of 27QG090 high magnetic induction oriented silicon steel was completed in laboratory by using pilot-scale test platform, and the microstructure and macro texture were analyzed by means of optical microscope, X-ray diffractometer, TEM and EDS. The results show that the microstructure of the 27QG090 steel after normalizing annealing is ferrite, the macro texture is mainly α, α^* and copper texture, and with weak Gauss texture. The precipitate after normalizing annealing is mainly AlN, whose average size is about 40 nm. Comprehensive analysis shows that the optimal normalizing annealing process is heating at 1120 ℃ for 3 min and at 920 ℃ for 3 min, then 100 ℃ water quenching.

Key words: oriented silicon steel, normalizing annealing, microstructure, texture

中图分类号:

TG142

卢晓禹, 董磊, 黄利, 刘宝志. 高磁感取向硅钢27QG090的常化退火工艺[J]. 金属热处理, 2023, 48(1): 186-189.

Lu Xiaoyu, Dong Lei, Huang Li, Liu Baozhi. Normalizing annealing process of 27QG090 high magnetic induction oriented silicon steel[J]. Heat Treatment of Metals, 2023, 48(1): 186-189.

参考文献

[1]张继舜, 任慧平, 金自力, 等. 含铜低温取向硅钢轧制过程中的组织及织构演变[J]. 金属热处理, 2020, 45(4): 80-84.
Zhang Jishun, Ren Huiping, Jin Zili, et al. Microstructure and texture evolution of Cu-containing low temperature oriented silicon steel during rolling process[J]. Heat Treatment of Metals, 2020, 45(4): 80-84.
[2]王忠亮. 包钢取向硅钢(CGO)热轧钢带的研制与开发[D]. 包头: 内蒙古科技大学, 2019.
Wang Zhongliang. Development of hot rolled silicon oriented steel(CGO) strip at Baotou Steel[D]. Baotou: Inner Mongolia University of Science and Technology, 2019.
[3]何忠治. 电工钢[M]. 北京: 冶金工业出版社, 1996: 23.
[4]刘璐, 张宁, 杨平, 等. 高硅钢近柱状晶初始组织的形变、再结晶行为及磁性能[J]. 工程科学学报, 2015, 37(7): 919-923.
Liu Lu, Zhang Ning, Yang Ping, et al. Deformation, recrystallization behaviors and magnetic properties of high silicon steel with an initial near columnar-grained structure[J]. Chinese Journal of Engineering, 2015, 37(7): 919-923.
[5]毛卫民, 杨平. 电工钢的材料学原理[M]. 北京: 冶金工业出版社, 2013: 346-371.
[6]毕娜, 张宁, 杨平. 取向硅钢薄带形变再结晶组织及织构演变[J]. 工程科学学报, 2015, 37(1): 50-54.
Bi Na, Zhang Ning, Yang Ping. Deformation and recrystallization texture and microstructure evolution of thin grain-oriented silicon steel sheets[J]. Chinese Journal of Engineering, 2015, 37(1): 50-54.
[7]何忠治, 赵宇, 罗海文. 电工钢[M]. 北京: 冶金工业出版社, 2012: 409.
[8]付勇军, 蒋奇武, 杨平, 等. 脱碳退火保温时间对取向硅钢组织、织构及磁性能的影响[J]. 材料热处理学报, 2015, 36(7): 157-161.
Fu Yongjun, Jiang Qiwu, Yang Ping, et al. Effect of holding time of decarburization annealing on microstructure, textures and magnetic properties of grain oriented silicon steel[J]. Transactions of Materials and Heat Treatment, 2015, 36(7): 157-161.

[1]	邓煜华, 黎振华, 姚碧波, 滕宝仁, 李颢. 热处理对选区激光熔化钴铬合金组织与性能的影响[J]. 金属热处理, 2023, 48(1): 23-28.
[2]	顾海, 张捷, 孙健华, 吴国庆, 孙中刚. 激光熔化沉积2195铝锂合金微观组织演变及力学性能[J]. 金属热处理, 2023, 48(1): 52-59.
[3]	赵政翔, 李静媛, 廖露海, 徐芳泓, 张威. 超级奥氏体不锈钢654SMO在900 ℃下的时效析出行为[J]. 金属热处理, 2023, 48(1): 68-74.
[4]	胡帅, 金自力, 吴忠旺, 李涛, 李玮, 胡雨晴, 白金. 含稀土取向硅钢高温铁素体区的再结晶及抑制剂析出行为[J]. 金属热处理, 2023, 48(1): 75-79.
[5]	陈晶阳, 任晓冬, 张明军, 张丽辉, 汤鑫, 肖程波. 铸造镍基高温合金K439B的组织及典型性能[J]. 金属热处理, 2023, 48(1): 100-104.
[6]	吴跃. Super304H耐热钢时效过程中的奥氏体晶粒长大及力学性能[J]. 金属热处理, 2023, 48(1): 105-111.
[7]	王文正, 马永福, 马劲红, 张桂营, 田亚强, 程新超, 李红斌, 陈连生. Q355D热轧H型钢的CCT曲线及冲击性能[J]. 金属热处理, 2023, 48(1): 127-132.
[8]	元亚莎, 汪雨昌, 王文焱, 石如星, 元莎, 张玉栋. 回火温度对55NiCrMoV7热作模具钢组织和性能的影响[J]. 金属热处理, 2023, 48(1): 133-138.
[9]	张家豪, 陈连生, 高天洋, 徐海卫, 韩赟, 李红斌, 田亚强. 过时效温度对连续退火制备DP1180钢组织性能的影响[J]. 金属热处理, 2023, 48(1): 149-154.
[10]	戴建科, 韩顺, 厉勇, 刘雨, 雷斯敏, 王春旭. 淬火温度对新型齿轮钢组织及力学性能的影响[J]. 金属热处理, 2023, 48(1): 163-168.
[11]	赵培林, 杨栋, 吴会亮, 刘超, 李超, 李春传, 郑力. 正火处理对建筑结构用超厚规格H型钢抗层状撕裂性能的影响[J]. 金属热处理, 2023, 48(1): 175-180.
[12]	李鸿娟, 向成功, 吴琼, 王正才. 淬火与回火工艺对42CrMo钢显微组织和奥氏体晶粒长大规律的影响[J]. 金属热处理, 2023, 48(1): 181-185.
[13]	杨胶溪, 黄凯, 武飞宇, 孙宏波, 阳代军, 李曙光, 葛学元, 王淼辉. Mg-Gd-Y-Zr镁合金高速激光熔覆Al-Si涂层的组织与性能[J]. 金属热处理, 2023, 48(1): 217-223.
[14]	高星, 张宁, 丁燕, 蒋波. 热处理时间对激光选区成形TC4钛合金组织及力学性能的影响[J]. 金属热处理, 2022, 47(9): 12-17.
[15]	潘冉, 刘宝胜, 曾元松, 曲海涛, 王东, 慕延宏. 深冷处理对15%SiC_p/2009铝基复合材料组织与力学性能的影响[J]. 金属热处理, 2022, 47(9): 65-70.

高磁感取向硅钢27QG090的常化退火工艺

Normalizing annealing process of 27QG090 high magnetic induction oriented silicon steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价