doi:10.13251/j.issn.0254-6051.2020.06.003

金属热处理 ›› 2020, Vol. 45 ›› Issue (6): 12-16.DOI: 10.13251/j.issn.0254-6051.2020.06.003

00Cr22Ni13Mn5Mo2N奥氏体不锈钢的精轧工艺

李兵兵^1,3, 庄飚², 陈海涛³, 郎宇平³, 屈华鹏³, 冯翰秋³, 陈清明¹

1. 昆明理工大学材料科学与工程学院, 云南昆明 650093;
2. 中国人民解放军92942部队, 北京 100161;
3. 钢铁研究总院特殊钢研究所, 北京 100081

收稿日期:2019-11-20 出版日期:2020-06-25 发布日期:2020-09-02
通讯作者: 陈海涛,高级工程师,E-mail:chenhaitao@nercast.com
作者简介:李兵兵(1992—),女,硕士研究生,E-mail:361226819@qq.com。
基金资助:
国家重点研发计划(2016YFB0300202)

Finishing rolling process of 00Cr22Ni13Mn5Mo2N austenitic stainless steel

Li Bingbing^1,3, Zhuang Biao², Chen Haitao³, Lang Yuping³, Qu Huapeng³, Feng Hanqiu³, Chen Qingming¹

1. Faculty Materials Science and Engineering, Kunming University of Science and Technology, Kunming Yunnan 650093, China;
2. Chinese People's Liberation Army 92942, Beijing 100161, China;
3. Institute for Special Steels, Central Iron and Steel Research Institute, Beijing 100081, China

Received:2019-11-20 Online:2020-06-25 Published:2020-09-02

摘要/Abstract

摘要： 为了研究00Cr22Ni13Mn5Mo2N奥氏体不锈钢的精轧工艺,使用Gleeble-3800热模拟试验机模拟00Cr22Ni13Mn5Mo2N奥氏体不锈钢在变形温度为800、850、900、950 ℃,变形量为40%、50%、60%,应变速率为50 s^-1条件下的热压缩变形行为,并对其进行1080、1120、1160 ℃的固溶热处理,观察固溶热处理前后的组织形貌。结果表明:在800~950 ℃热压缩温度下,随变形量增大,再结晶越完全,再结晶平均晶粒尺寸越细小;经固溶处理1 h后,静态再结晶就越充分。在40%~60%变形量下,随热压缩温度升高,再结晶越完全,再结晶平均晶粒尺寸越大。热压缩变形试验钢随固溶处理温度升高,再结晶平均晶粒尺寸越大。00Cr22Ni13Mn5Mo2N奥氏体不锈钢的精轧最佳轧制温度为800 ℃,压缩变形量为60%,固溶温度为1080 ℃。

关键词: 00Cr22Ni13Mn5Mo2N奥氏体不锈钢, 热压缩变形, 再结晶, 固溶处理

Abstract: In order to study the finishing rolling process of 00Cr22Ni13Mn5Mo2N austenitic stainless steel, the hot compression deformation behavior of 00Cr22Ni13Mn5Mo2N austenitic stainless steel was simulated by a Gleeble-3800 thermal simulator, with the deformation temperatures 800, 850, 900 and 950 ℃, the deformation 40%, 50%, 60%, and the strain rate 50 s^-1. Then the structural morphology before and after the solid solution heat treatment at 1080, 1120 and 1160 ℃ was observed. The results show that the recrystallization is more complete and the average recrystallization grain size is smaller with the increase of deformation at 800-950 ℃. After solution treatment for 1 h, the static recrystallization becomes more sufficient. With the increase of thermal deformation temperature under the deformation of 40%-60%, the more complete the recrystallization is, the larger the average recrystallization grain size is. The average recrystallization grain size of the steel increases with the increase of solution treatment temperature. The optimum processing of 00Cr22Ni13Mn5Mo2N austenitic stainless steel is the finishing rolling temperature 800 ℃, the compression deformation 60%, and the solution treatment temperature 1080 ℃.

Key words: 00Cr22Ni13Mn5Mo2N austenitic stainless steel, hot compression deformation, recrystallization, solution treatment

中图分类号:

TG335

李兵兵, 庄飚, 陈海涛, 郎宇平, 屈华鹏, 冯翰秋, 陈清明. 00Cr22Ni13Mn5Mo2N奥氏体不锈钢的精轧工艺[J]. 金属热处理, 2020, 45(6): 12-16.

Li Bingbing, Zhuang Biao, Chen Haitao, Lang Yuping, Qu Huapeng, Feng Hanqiu, Chen Qingming. Finishing rolling process of 00Cr22Ni13Mn5Mo2N austenitic stainless steel[J]. Heat Treatment of Metals, 2020, 45(6): 12-16.

参考文献

[1]陆世英, 张廷凯, 康喜范. 不锈钢[M]. 北京: 原子能出版社, 1995: 265-268.
[2]孔玉婷, 张春玲, 杨金凤, 等. Cu-P-Cr-Ni-Mo耐候钢双相区多道次轧制模拟的组织演变[J]. 钢铁, 2014, 49(8): 81-87.
Kong Yuting, Zhang Chunling, Yang Jinfeng, et al. Microstructure evolution of Cu-P-Cr-Ni-Mo weathering steel by multi-pass rolling simulating in the intercritical region[J]. Iron and Steel, 2014, 49(8): 81-87.
[3]卢志江, 杨春光, 王帅, 等. 317L-Cu奥氏体抗菌不锈钢的热变形方程及其热加工图[J]. 钢铁, 2014, 49(5): 52-57.
Lu Zhijiang, Yang Chunguang, Wang Shuai, et al. Hot deformation equation and processing map of Cu-bearing 317L austenitic antibacterial stainless steel[J]. Iron and Steel, 2014, 49(5): 52-57.
[4]杨钢, 刘正东, 程世长, 等. 0Cr19Ni9N奥氏体不锈钢锻件的再结晶[J]. 机械工程材料, 2003, 27(3): 16-18.
Yang Gang, Liu Zhengdong, Cheng Shichang, et al. Recrystallization of forged 0Cr19Ni9N stainless steel[J]. Mechanical Engineering Materials, 2003, 27(3): 16-18.
[5]刘益民. 不同热变形条件下310S奥氏体不锈钢动态再结晶行为研究[J]. 物理测试, 2014, 32(4): 28-31.
Liu Yimin. Study on dynamic recrystallization behavior of 310S austenitic stainless steel under different heat deformation conditions[J]. Physics Examination and Testing, 2014, 32(4): 28-31.
[6]龚乾江, 梁益龙, 杨明, 等. 20CrMnTiH钢的热变形物理模型及三维加工图[J]. 钢铁, 2017, 52(7): 76-83.
Gong Qianjiang, Liang Yilong, Yang Ming, et al. Physical model and 3D thermal processing map of hot deformation of 20CrMnTiH steel[J]. Iron and Steel, 2017, 52(7): 76-83.
[7]Zener C, Hollomon J H. Problems in non-elastic deformation of metals[J]. Journal of Applied Physics, 1946, 17(2): 69-82.
[8]樊明强, 毛磊, 张雲飞, 等. H13钢高温压缩过程中温升对其变形行为及组织的影响[J]. 钢铁研究学报, 2017(9): 71-76.
Fan Mingqiang, Mao Lei, Zhang Yunfei, et al. Effect of temperature rise on deformation behavior and microstructure of H13 steel during high temperature compression process[J]. Journal of Iron and Steel Research, 2017(9): 71-76.
[9]Ghosh S, Bose S, Mandal N, et al. Dynamic recrystallization mechanisms and their transition in the Daling Thrust (DT) zone, Darjeeling-Sikkim Himalaya[J]. Tectonophysics, 2016, 674: 166-181.
[10]颜海涛, 毕洪运, 李鑫, 等. Nb对0Cr11铁素体不锈钢组织和性能的影响[J]. 钢铁, 2009, 44(1): 59-62.
Yan Haitao, Bi Hongyun, Li Xin, et al. Influence of Nb on microstructure and mechanical properties of 0Cr11 ferritic stainless steel[J]. Iron and Steel, 2009, 44(1): 59-62.
[11]叶传龙. 带钢热连轧精轧过程奥氏体组织演变的研究[D]. 武汉: 武汉科技大学, 2002.

[1]	王英虎, 郑淮北, 刘庭耀, 宋令玺, 白青青. 固溶处理对53Cr21Mn9Ni4N耐热钢组织及碳化物的影响[J]. 金属热处理, 2022, 47(4): 39-45.
[2]	连轶博, 杨春雷, 王国栋, 宋威. 固溶处理对GH4080A高温合金微观组织的影响[J]. 金属热处理, 2022, 47(4): 46-52.
[3]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[4]	孙建, 黄贞益, 李景辉, 王萍. 固溶和时效处理对Fe-Mn-Al-C轻质钢组织和硬度的影响[J]. 金属热处理, 2022, 47(3): 34-38.
[5]	王国迪, 景然, 张曼雪, 冯甜, 余国庆, 解念锁. 冷轧变形量及再结晶对TC4合金组织与性能的影响[J]. 金属热处理, 2022, 47(3): 48-52.
[6]	王方军, 刘应龙, 时瑶, 万红, 刘斌斌. 等温退火处理对Inconel 625合金箔材组织和性能的影响[J]. 金属热处理, 2022, 47(3): 77-81.
[7]	程体娟, 甘斌, 于鸿垚, 周海晶, 郭彩玉, 毕中南, 杜金辉. 固溶处理对新型镍基高温合金组织及性能的影响[J]. 金属热处理, 2022, 47(3): 107-112.
[8]	叶拓, 唐明, 刘吉兆, 刘伟, 吴远志, 刘巍, 徐文. 固溶温度对7075铝合金板材组织与力学性能的影响[J]. 金属热处理, 2022, 47(3): 119-123.
[9]	张世进, 李凯, 易丹青, 刘会群. 冷轧TA5钛合金退火过程的再结晶行为及织构演变[J]. 金属热处理, 2022, 47(2): 1-8.
[10]	郝天赐, 吴雍壕, 阴树标, 曹建春, 罗瀚宇. Zr对Ti-Mo复合微合金化钢形变奥氏体静态再结晶动力学和析出相的影响[J]. 金属热处理, 2022, 47(2): 41-47.
[11]	李永顺, 玄伟东, 段方苗, 赵玉娟, 李俊杰, 王保军, 任兴孚, 任忠鸣. 应力对单晶高温合金再结晶的影响[J]. 金属热处理, 2022, 47(2): 48-52.
[12]	舒玮, 宋丽强, 张威. 热变形对含铌奥氏体不锈钢07Cr18Ni11Nb再结晶行为的影响[J]. 金属热处理, 2022, 47(2): 59-64.
[13]	冯运动, 邹宇明, 丁桦. Ti含量对IF钢再结晶温度及力学性能的影响[J]. 金属热处理, 2022, 47(2): 70-73.
[14]	邱旭扬帆, 杨卓越, 丁雅莉. 提高Cr-Ni-Mo-Ti马氏体时效不锈钢超低温韧性的固溶处理工艺[J]. 金属热处理, 2022, 47(1): 44-48.
[15]	张涛, 郑文杰, 李才巨. 冷拔后退火对Monel 400合金丝材的再结晶过程及力学性能的影响[J]. 金属热处理, 2022, 47(1): 56-62.

00Cr22Ni13Mn5Mo2N奥氏体不锈钢的精轧工艺

Finishing rolling process of 00Cr22Ni13Mn5Mo2N austenitic stainless steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价