提高Cr-Ni-Mo-Ti马氏体时效不锈钢超低温韧性的固溶处理工艺

doi:10.13251/j.issn.0254-6051.2022.01.008

金属热处理 ›› 2022, Vol. 47 ›› Issue (1): 44-48.DOI: 10.13251/j.issn.0254-6051.2022.01.008

提高Cr-Ni-Mo-Ti马氏体时效不锈钢超低温韧性的固溶处理工艺

邱旭扬帆, 杨卓越, 丁雅莉

钢铁研究总院特殊钢研究院, 北京 100081

收稿日期:2021-06-16 修回日期:2021-09-27 出版日期:2022-01-25 发布日期:2022-02-18
通讯作者: 杨卓越,教授级高工,博士,E-mail:Yangzhuoyue@nercast.com
作者简介:邱旭扬帆(1995—),男,硕士研究生,主要研究方向为超低温用高强不锈钢韧化工艺,E-mail:18401669210@163.com。

Solid solution treatment for improving cryogenic temperature toughness of Cr-Ni-Mo-Ti maraging stainless steel

Qiu Xuyangfan, Yang Zhuoyue, Ding Yali

Research Institute of Special Steels, Central Iron and Steel Research Institute, Beijing 100081, China

Received:2021-06-16 Revised:2021-09-27 Online:2022-01-25 Published:2022-02-18

摘要/Abstract

摘要： 研究了12Cr-10Ni-Mo-Ti马氏体时效不锈钢在1000 ℃固溶处理+750 ℃重复低温固溶处理+不同温度时效处理后的显微组织、室温强度和低温冲击性能,并用XRD分析了不同固溶和时效工艺下的残留奥氏体/逆转变奥氏体含量,对比分析了不同固溶处理工艺下时效响应强度逆转变奥氏体的析出和时效强化规律。结果表明,Cr-Ni-Mo-Ti马氏体时效不锈钢经1000 ℃固溶处理后再进行750 ℃低温固溶处理时以α′→γ剪切逆相变形成奥氏体,不仅遗传奥氏体的晶粒形态和尺寸,且形成的奥氏体内高密度缺陷增大马氏体相变抗力,同时显著降低逆转变奥氏体的形成温度,使750 ℃固溶处理两次时残留16.4%奥氏体,再经460 ℃峰时效形成了30%以上的残留奥氏体+逆转变奥氏体,液氮温度冲击吸收能量极高,达80 J以上,并且奥氏体的高缺陷密度遗传到马氏体内增强时效强化效应,因此显著改善低温冲击性能的同时并未明显降低抗拉和屈服强度。

关键词: 马氏体时效不锈钢, 固溶处理, 残留奥氏体, 逆转变奥氏体, 超低温韧性

Abstract: Microstructure, room temperature strength and cryogenic temperature toughness of 12Cr-10Ni-Mo-Ti maraging stainless steel after solution treatment at 1000 ℃, repeated low temperature solution treatment at 750 ℃ and aging at different temperature were investigated. The amount of retained austenite/reverse transformation austenite under different solution and aging treatment conditions were analyzed by using XRD. The precipitation and aging strengthening rules of reverse transformation austenite in different solution treatment processes were compared and analyzed. The results show that the Cr-Ni-Mo-Ti maraging stainless steel after solution treatment at 1000 ℃ and followed low temperature solution treatment at 750 ℃ forms austenite by α′→γ shear reverse transformation, which not only inherits the grain morphology and size of austenite, but also increases the martensitic transformation resistance and significantly reduces the formation temperature of reverse transformation austenite due to the high density of defects in austenite, resulting in 16.4% retained austenite after double solid solution treatment at 750 ℃, more than 30% retained austenite/reverse transformation austenite is formed after peak value aging at 460 ℃, and the impact absorbed energy at cryogenic temperature is extremely high, reaching above 80 J. Moreover, the high density of defect in austenite is inherited into the martensite, which enhances the aging strengthening effect. Therefore, the low temperature impact property is significantly improved without significantly reducing the tensile strength and yield strength.

Key words: maraging stainless steel, solution treatment, retained austenite, reversed austenite, cryogenic temperature toughness

中图分类号:

TG142.1

邱旭扬帆, 杨卓越, 丁雅莉. 提高Cr-Ni-Mo-Ti马氏体时效不锈钢超低温韧性的固溶处理工艺[J]. 金属热处理, 2022, 47(1): 44-48.

Qiu Xuyangfan, Yang Zhuoyue, Ding Yali. Solid solution treatment for improving cryogenic temperature toughness of Cr-Ni-Mo-Ti maraging stainless steel[J]. Heat Treatment of Metals, 2022, 47(1): 44-48.

参考文献

[1]Stepanov G A, Stanotina V V. Properties of steel 12Kh18N10T tested for tensile strength in liquid helium cooled to 2. 4 K[J]. Metal Science and Heat Treatment, 2003, 45(9/10): 373-375.
[2]Saucedo-Munoz M L, Watanabe Y, Shoji T, et al. Effect of microstructure evolution on fracture toughness in isothermally aged austenitic stainless steels for cryogenic application[J]. Cryogenics, 2000, 40(11): 693-700.
[3]Tarasenko L V, Shal'Kevich A B. Phase composition and hardening of steels of the Fe-Cr-Ni-Co-Mo system with martensite-austenite structure[J]. Metal Science and Heat Treatment, 2007, 49(3/4): 188-193.
[4]Anoop C R, Prakash A, Murty S V S N, et al. Origin of low temperature toughness in a 12Cr-10Ni martensitic precipitation hardenable stainless steel[J]. Materials Science and Engineering A, 2018, 709(1): 1-8.
[5]Kagan E S, Potak Ya M, Sachkov V V, et al, High-strength steel for cryogenic temperatures[J]. Metal Science and Heat Treatment, 1971, 13(10): 821-822.
[6]Lee S J, Park Y M, Lee Y K. Reverse transformation mechanism of martensite to austenite in a metastable austenitic alloy[J]. Materials Science and Engineering A, 2009, 515(1/2): 32-37.
[7]Vasudevan V K, Kim S J, Wayman C M. Precipitation reactions and strengthening behavior in 18 Wt Pct nickel maraging steels[J]. Metallurgical Transactions A, 1990, 21(10): 2655-2668.
[8]Luo Haiwen, Wang Xiaohui, Liu Zhenbao, et al. Influence of refined hierarchical martensitic microstructures on yield strength and impact toughness of ultra-high strength stainless steel[J]. Journal of Materials Science and Technology, 2020, 51: 130-136.
[9]Li X, Fan Y, Ma X, et al. Influence of martensite-austenite constituents formed at different intercritical temperatures on toughness[J]. Materials and Design, 2015, 67: 457-463.
[10]Carlos García-Mateo, Francisca G Caballero. The role of retained austenite on tensile properties of steels with bainitic microstructures[J]. Materials Transactions, 2005, 46(8): 1839-1846.

[1]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[2]	王英虎, 郑淮北, 刘庭耀, 宋令玺, 白青青. 固溶处理对53Cr21Mn9Ni4N耐热钢组织及碳化物的影响[J]. 金属热处理, 2022, 47(4): 39-45.
[3]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[4]	陈连生, 房宁, 曹仲乾, 杨子旋, 李红斌, 潘红波, 田亚强. 压下率对两相区温轧淬火配分中锰钢组织性能的影响[J]. 金属热处理, 2022, 47(3): 28-33.
[5]	孙建, 黄贞益, 李景辉, 王萍. 固溶和时效处理对Fe-Mn-Al-C轻质钢组织和硬度的影响[J]. 金属热处理, 2022, 47(3): 34-38.
[6]	程体娟, 甘斌, 于鸿垚, 周海晶, 郭彩玉, 毕中南, 杜金辉. 固溶处理对新型镍基高温合金组织及性能的影响[J]. 金属热处理, 2022, 47(3): 107-112.
[7]	叶拓, 唐明, 刘吉兆, 刘伟, 吴远志, 刘巍, 徐文. 固溶温度对7075铝合金板材组织与力学性能的影响[J]. 金属热处理, 2022, 47(3): 119-123.
[8]	刘韬, 吴红艳, 高秀华, 秦岽烊, 杜林秀. 临界区回火温度对Fe-4Mn-1.2Cr-0.3Cu-0.6Ni中锰钢微观组织和力学性能的影响[J]. 金属热处理, 2022, 47(2): 91-98.
[9]	董瑞, 陈林, 岑耀东, 包喜荣. 不同热处理条件下贝氏体钢的微观组织和疲劳裂纹扩展[J]. 金属热处理, 2022, 47(2): 153-158.
[10]	侯雅青, 张宇, 于明光, 王静静, 杨丽, 苏航. Q&P钢残留奥氏体含量的热动力学计算[J]. 金属热处理, 2022, 47(1): 25-31.
[11]	高亚平, 师仲然, 贾涓, 罗小兵, 宋新莉. 热处理工艺对疏浚工程用船体钢组织及磨粒磨损性能的影响[J]. 金属热处理, 2022, 47(1): 32-37.
[12]	巩芳源, 冯翰秋, 郎宇平, 陈海涛, 王曼, 朱雄明, 冷崇燕. 氮及热处理制度对028合金微观组织的影响[J]. 金属热处理, 2021, 46(9): 36-41.
[13]	邓彪, 陈蓬, 王国栋. 回火温度对二次硬化马氏体不锈钢组织和性能的影响[J]. 金属热处理, 2021, 46(9): 65-71.
[14]	齐祥羽, 严玲, 李广龙, 李文斌, 杜林秀. 逆转变奥氏体稳定性对中锰钢强韧性的影响[J]. 金属热处理, 2021, 46(9): 205-210.
[15]	张慧云, 孟宪明, 郑留伟, 梁伟. 敏化处理对不同状态304奥氏体不锈钢氢脆敏感性的影响[J]. 金属热处理, 2021, 46(8): 164-169.

提高Cr-Ni-Mo-Ti马氏体时效不锈钢超低温韧性的固溶处理工艺

Solid solution treatment for improving cryogenic temperature toughness of Cr-Ni-Mo-Ti maraging stainless steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价