固溶处理对GH4080A高温合金微观组织的影响

doi:10.13251/j.issn.0254-6051.2022.04.007

金属热处理 ›› 2022, Vol. 47 ›› Issue (4): 46-52.DOI: 10.13251/j.issn.0254-6051.2022.04.007

固溶处理对GH4080A高温合金微观组织的影响

连轶博¹, 杨春雷², 王国栋², 宋威¹

1.国机金属江苏有限公司, 江苏江阴 214000;
2.江苏省产业技术研究院先进金属材料及应用技术研究所, 江苏常熟 215506

收稿日期:2021-12-30 修回日期:2022-01-28 出版日期:2022-04-25 发布日期:2022-05-19
作者简介:连轶博(1981—),男,工程师,主要研究方向为镍基高温合金,E-mail:13913685671@163.com

Effect of solution treatment on microstructure of GH4080A superalloy

Lian Yibo¹, Yang Chunlei², Wang Guodong², Song Wei¹

1. SINOMACH Jiangsu Co., Ltd., Jiangyin Jiangsu 214000, China;
2. Institute of Novel Metals and Applied Technologies, Jiangsu Industrial Technology Research Institute, Changshu Jiangsu 215506, China

Received:2021-12-30 Revised:2022-01-28 Online:2022-04-25 Published:2022-05-19

摘要/Abstract

摘要： 利用电子背散射衍射(EBSD)技术,研究了不同固溶处理工艺对GH4080A高温合金微观组织的影响。结果表明,初始热轧棒材在轧制过程中动态再结晶不充分,残留有未再结晶的晶粒,晶粒内部有较多的小角度晶界。当固溶温度为1020 ℃时,主要以再结晶的形核为主,随着固溶温度的升高,再结晶形核基本结束,开始进入晶粒长大阶段。再结晶过程伴随着小角度取向差向大角度取向差的转变,且再结晶过程中发现了薄片状的{111}孪晶组织以及大量的Σ3晶界。

关键词: GH4080A合金, 再结晶, 孪晶, 取向差, 晶粒尺寸

Abstract: Effect of different solution treatment on microstructure of GH4080A superalloy was studied by using electron backscatter diffraction (EBSD) technology. The results show that the dynamic recrystallization during the rolling process of the initial hot-rolled bar is insufficient, and there are unrecrystallized grains as well as many inside-grain small-angle grain boundaries. When the solution treatment temperature is 1020 ℃, the recrystallization is mainly in the stage of nucleation. With the increase of solution treatment temperature, the recrystallization nucleation is completed basically and the grain growth stage begins. The recrystallization process is accompanied by the transformation from small-angle misorientation to large-angle misorientation, and lamellar {111} twin structure and a large number of Σ3 grain boundaries are found during the recrystallization process.

Key words: GH4080A alloy, recrystallization, twins, misorientation, grain size

中图分类号:

TG156.1

连轶博, 杨春雷, 王国栋, 宋威. 固溶处理对GH4080A高温合金微观组织的影响[J]. 金属热处理, 2022, 47(4): 46-52.

Lian Yibo, Yang Chunlei, Wang Guodong, Song Wei. Effect of solution treatment on microstructure of GH4080A superalloy[J]. Heat Treatment of Metals, 2022, 47(4): 46-52.

参考文献

[1]郭建亭. 高温合金材料学[M]. 北京: 科学出版社, 2008: 3-16.
[2]刘永长, 郭倩颖, 李冲, 等. Inconel 718高温合金中析出相演变研究进展[J]. 金属学报, 2016, 52(10): 1259-1266.
Liu Yongchang, Guo Qianying, Li Chong, et al. Recent progress on evolution of precipitates in Inconel 718 superalloy[J]. Acta Metallurgica Sinica, 2016, 52(10): 1259-1266.
[3]张文竹, 许周烽, 蒋力. 固溶热处理对GH3535合金组织和性能的影响[J]. 稀有金属材料与工程, 2016, 45(6): 1583-1587.
Zhang Wenzhu, Xu Zhoufeng, Jiang Li. Effect of solution heat treatment on microstructure and properties of GH3535 superalloy[J]. Rare Metal Materials and Engineering, 2016, 45(6): 1583-1587.
[4]夏鹏成, 于金江, 孙晓峰, 等. 热处理对定向镍基高温合金DZ951 γ′相的影响[J]. 稀有金属材料与工程, 2006, 35(5): 779-782.
Xia Pengcheng, Yu Jinjiang, Sun Xiaofeng, et al. Influence of heat treatments on the γ' phase of directionally solidified DZ951 nickel base superalloy[J]. Rare Metal Materials and Engineering, 2006, 35(5): 779-782.
[5]Mandal S, Jayalakshmi M, Bhaduri A, et al. Effect of strain rate on the dynamic recrystallization behavior in a nitrogen-enhanced 316L (N)[J]. Metallurgical and Materials Transactions A, 2014, 45(12): 5645-5656.
[6]檀校, 郝玉朋, 于晓东, 等. 退火温度对冷轧气相沉积高纯钨再结晶行为的影响[J]. 金属热处理, 2021, 46(3): 33-38.
Tan Xiao, Hao Yupeng, Yu Xiaodong, et al. Effect of annealing temperature on recrystallization behaviors of cold-rolled high-purity CVD tungsten[J]. Heat Treatment of Metals, 2021, 46(3): 33-38.
[7]米大为. 固溶温度对GH5605高温合金组织和力学性能的影响[J]. 金属热处理, 2018, 43(12): 191-194.
Mi Dawei. Effect of solution treatment temperature on microstructure and mechanical properties of GH5605 superalloy[J]. Heat Treatment of Metals, 2018, 43(12): 191-194.
[8]李小兵, 李伟. 固溶温度对高温合金GH3600 微观组织与硬度的影响[J]. 金属热处理, 2020, 45(6): 51-55.
Li Xiaobing, Li Wei. Effect of solution temperature on microstructure and hardness of GH3600 superalloy[J]. Heat Treatment of Metals, 2020, 45(6): 51-55.
[9]毛卫民, 赵新兵. 金属的再结晶与晶粒长大[M]. 北京: 冶金工业出版社, 1994.
[10]王蓬书, 李琴敏, 韦贤毅, 等. 固溶对GH4169合金晶粒尺寸与力学性能的影响[J]. 热加工工艺, 2018, 47(4): 245-249.
Wang Pengshu, Li Qinmin, Wei Xianyi, et al. Effect of solid solution on grain size and mechanical properties of GH4169 alloy[J]. Hot Working Technology, 2018, 47(4): 245-249.
[11]Bouaziz O, Allain S, Scott C. Effect of grain and twin boundaries on the hardening mechanisms of twinning-induced plasticity steels[J]. Scripta Materialia, 2008, 58(6): 484-487.

[1]	陈刚, 罗小兵, 柴锋, 杨才福, 张正延, 杨丽. 轧制加热温度对高强度低合金钢组织及冲击性能的影响[J]. 金属热处理, 2022, 47(4): 116-121.
[2]	宿鹏吉, 麻永林, 董丽丽, 杨雪峰. 磁场预退火处理对CGO钢组织与织构的影响[J]. 金属热处理, 2022, 47(4): 128-132.
[3]	王国迪, 景然, 张曼雪, 冯甜, 余国庆, 解念锁. 冷轧变形量及再结晶对TC4合金组织与性能的影响[J]. 金属热处理, 2022, 47(3): 48-52.
[4]	王方军, 刘应龙, 时瑶, 万红, 刘斌斌. 等温退火处理对Inconel 625合金箔材组织和性能的影响[J]. 金属热处理, 2022, 47(3): 77-81.
[5]	张世进, 李凯, 易丹青, 刘会群. 冷轧TA5钛合金退火过程的再结晶行为及织构演变[J]. 金属热处理, 2022, 47(2): 1-8.
[6]	郝天赐, 吴雍壕, 阴树标, 曹建春, 罗瀚宇. Zr对Ti-Mo复合微合金化钢形变奥氏体静态再结晶动力学和析出相的影响[J]. 金属热处理, 2022, 47(2): 41-47.
[7]	李永顺, 玄伟东, 段方苗, 赵玉娟, 李俊杰, 王保军, 任兴孚, 任忠鸣. 应力对单晶高温合金再结晶的影响[J]. 金属热处理, 2022, 47(2): 48-52.
[8]	杨劼, 任慧平, 刘宗昌. 15Cr12CuSiMoMn钢的奥氏体晶粒长大动力学[J]. 金属热处理, 2022, 47(2): 53-58.
[9]	舒玮, 宋丽强, 张威. 热变形对含铌奥氏体不锈钢07Cr18Ni11Nb再结晶行为的影响[J]. 金属热处理, 2022, 47(2): 59-64.
[10]	冯运动, 邹宇明, 丁桦. Ti含量对IF钢再结晶温度及力学性能的影响[J]. 金属热处理, 2022, 47(2): 70-73.
[11]	代永娟, 武祥祥, 李佳坤, 国栋, 王波. 退火温度对Fe-24.38Mn-0.44C TWIP钢组织性能的影响[J]. 金属热处理, 2022, 47(2): 146-152.
[12]	张涛, 郑文杰, 李才巨. 冷拔后退火对Monel 400合金丝材的再结晶过程及力学性能的影响[J]. 金属热处理, 2022, 47(1): 56-62.
[13]	范合合, 金自力, 任慧平, 游兴华. 高Nb-Ti新能源汽车用无取向硅钢热轧过程的再结晶行为[J]. 金属热处理, 2022, 47(1): 88-93.
[14]	李昂, 高坤元, 文胜平, 黄晖, 聂祚仁. 冷却条件对5E83铝合金搅拌摩擦焊接头组织与性能的影响[J]. 金属热处理, 2022, 47(1): 130-134.
[15]	强菲, 王文, 张婷, 杨娟, 蔡军, 王快社. Al-Zn-Mg-Cu铝合金厚板搅拌摩擦焊接头搅拌区微观组织[J]. 金属热处理, 2022, 47(1): 135-141.

固溶处理对GH4080A高温合金微观组织的影响

Effect of solution treatment on microstructure of GH4080A superalloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价