固溶前预退火处理对6111铝合金组织与性能的影响

doi:10.13251/j.issn.0254-6051.2021.10.028

金属热处理 ›› 2021, Vol. 46 ›› Issue (10): 163-167.DOI: 10.13251/j.issn.0254-6051.2021.10.028

固溶前预退火处理对6111铝合金组织与性能的影响

李大林^1,2, 朱鹏程¹, 王萍¹, 吕正风³, 张善顺¹

1.烟台南山学院材料科学与工程学院, 山东烟台 265713;
2.烟台南山学院山东省高校轻合金加工成形重点实验室, 山东烟台 265700;
3.烟台市高性能铝合金材料加工成形及检测工程实验室, 山东烟台 265700

收稿日期:2021-04-24 出版日期:2021-10-25 发布日期:2021-12-08
作者简介:李大林(1984—),男,讲师,硕士,主要研究方向为高性能铝合金的组织性能控制,E-mail:lidalin3@nanshan.edu.cn
基金资助:
山东省高等学校青创科技计划(2019KJA019)

Influence of pre-annealing before solution on microstructure and properties of 6111 aluminum alloy

Li Dalin^1,2, Zhu Pengcheng¹, Wang Ping¹, Lü Zhengfeng³, Zhang Shanshun¹

1. School of Materials Science and Engineering, Yantai Nanshan University, Yantai Shandong 265713, China;
2. Light Alloy Processing Laboratory of High-University of Shandong Province, Yantai Nanshan University, Yantai Shandong 265700, China;
3. Yantai High Performance Aluminum Alloy Material Processing and Testing Engineering Laboratory, Yantai Shandong 265700, China

Received:2021-04-24 Online:2021-10-25 Published:2021-12-08

摘要/Abstract

摘要： 系统研究了固溶前预退火温度对6111铝合金冷轧板和T4P态组织和力学性能的影响。测试了力学性能,计算了LDR值;表征了显微组织、SEM组织和XRD织构构成。结果表明:预退火温度对6111铝合金的屈服强度影响较小;经300 ℃×2 h预退火处理后,抗拉强度发生明显降低,由245 MPa降低到230 MPa;当预退火温度高于100 ℃后,伸长率呈直线下降。n值和r值均随预退火温度先升高后降低,n值在200 ℃时达到最大值0.289,r值在100 ℃时达到最大值0.958。200 ℃×2 h预退火处理后,LDR值达到最大值2.005。经300 ℃×2 h预退火处理后,T4P态基体晶粒尺寸明显长大,在60~150 μm范围。200 ℃×2 h预退火处理试样,T4P态Cube织构体积分数最高,达到了13.5%。

关键词: 预退火, 6111铝合金, 微观组织, 性能

Abstract: Influence of pre-annealing before solution treatment on microstructure and mechanical properties of cold rolled and T4P state 6111 aluminum was investigated. The mechanical properties were tested, the LDR value was calculated, and microstructure was characterized by means of optical microscopy and scanning electronic microscopy (SEM). The texture was tested by using XRD. The results indicate that pre-annealing temperature has little effect on yield strength, but the tensile strength decreases from 245 MPa to 230 MPa after annealing at 300 ℃ for 2 h. The elongation decreases sharply when pre-annealing temperature is higher than 100 ℃. The n and r value increase first and then decrease with the increase of pre-annealing temperature. n value reaches the peak(0.289) at 200 ℃ and r value reaches the peak (0.958) at 100 ℃. LDR value reaches the peak value of 2.005 after 200 ℃×2 h pre-annealing. The grain size of T4P state alloy after pre-annealing at 300 ℃ for 2 h ranges from 60 μm to 150 μm. The volume fraction of Cube texture of T4P state alloy after pre-annealing at 200 ℃ for 2 h reaches the peak value of 13.5%.

Key words: pre-annealing, 6111 aluminum alloy, microstructure, properties

中图分类号:

TG156.1

李大林, 朱鹏程, 王萍, 吕正风, 张善顺. 固溶前预退火处理对6111铝合金组织与性能的影响[J]. 金属热处理, 2021, 46(10): 163-167.

Li Dalin, Zhu Pengcheng, Wang Ping, Lü Zhengfeng, Zhang Shanshun. Influence of pre-annealing before solution on microstructure and properties of 6111 aluminum alloy[J]. Heat Treatment of Metals, 2021, 46(10): 163-167.

参考文献

[1]Cole G S, Sherman A M. Light weight materials for automotive applications[J]. Materials Characterization, 1995, 35(1): 3-9.
[2]Hirsch J. Recent development in aluminium for automotive applications[J]. Transactions of Nonferrous Metals Society of China, 2014, 24(7): 1995-2002.
[3]Miller W S, Zhuang L, Bottema J, et al. Recent development in aluminium alloys for the automotive industry[J]. Materials Science and Engineering: A, 2000, 280(1): 37-49.
[4]Hirsch J, Al-Samman T. Superior light metals by texture engineering: Optimized aluminum and magnesium alloys for automotive applications[J]. Acta Materialia, 2013, 61(3): 818-843.
[5]刘秋平, 刘志勇, 赵俊, 等. Zn含量及回归热处理对7075铝合金性能的影响[J]. 金属热处理, 2016, 41(2): 11-15.
Liu Qiuping, Liu Zhiyong, Zhao Jun, et al. Effect of Zn content and retrogression and re-aging treatment on properties of 7075 aluminum alloy[J]. Heat Treatment of Metals, 2016, 41(2): 11-15.
[6]Pogatscher S, Antrekowitsch H, Leitner H, et al. Mechanisms controlling the artificial aging of Al-Mg-Si alloys[J]. Acta Materialia, 2011, 59(9): 3352-3363.
[7]李辉, 李铸铁, 晋宏炎, 等. 预时效及烤漆硬化处理对6016铝合金显微组织及硬度的影响[J]. 金属热处理, 2017, 42(11): 148-151.
Li Hui, Li Zhutie, Jin Hongyan, et al. Influence of pre-aging and bake hardening on microstructure and hardness of 6016 aluminum alloy[J]. Heat Treatment of Metals, 2017, 42(11): 148-151.
[8]Yin D Y, Xiao Q, Chen Y Q, et al. Effect of natural ageing and pre-straining on the hardening behaviour and microstructural response during artificial ageing of an Al-Mg-Si-Cu alloy[J]. Materials & Design, 2016, 95: 329-339.
[9]Takaki Y, Aruga Y, Kozuka M, et al. Effects of pre-aging and natural aging on bake hardening behavior in Al-Mg-Si alloys[J]. Materials Science Forum, 2014, 794: 1026-1031.
[10]Matsuda K, Sakaguchi Y, Miyata Y, et al. Precipitation sequence of various kinds of metastable phases in Al-1.0mass%Mg₂Si-0.4mass%Si alloy[J]. Journal of Materials Science, 2000, 35(1): 179-189.
[11]Muhammad W, Ali U, Brahme A P, et al. Experimental analyses and numerical modeling of texture evolution and the development of surface roughness during bending of an extruded aluminum alloy using a multiscale modeling framework[J]. International Journal of Plasticity, 2017, 117: 93-121.

[1]	王玉岱, 刘洋, 朱言言, 田象军, 程序, 冉先喆, 钱婷婷. 热处理对复合制造AerMet100超高强度钢组织均匀性与拉伸性能的影响[J]. 金属热处理, 2022, 47(4): 1-9.
[2]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[3]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[4]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[5]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[6]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[7]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[8]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[9]	陈思君, 陈送义, 陈庚, 袁丁玲, 陈康华. Mg含量对2A14铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 86-92.
[10]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[11]	白青青, 张志宏, 郑淮北, 王英虎. 2507超级双相不锈钢中σ相的析出行为[J]. 金属热处理, 2022, 47(4): 108-115.
[12]	陈刚, 罗小兵, 柴锋, 杨才福, 张正延, 杨丽. 轧制加热温度对高强度低合金钢组织及冲击性能的影响[J]. 金属热处理, 2022, 47(4): 116-121.
[13]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[14]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.
[15]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.

固溶前预退火处理对6111铝合金组织与性能的影响

Influence of pre-annealing before solution on microstructure and properties of 6111 aluminum alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价