热处理对复合铸造高铬高碳钢/碳钢耐磨材料微观组织及力学性能的影响

doi:10.13251/j.issn.0254-6051.2022.08.027

金属热处理 ›› 2022, Vol. 47 ›› Issue (8): 163-167.DOI: 10.13251/j.issn.0254-6051.2022.08.027

热处理对复合铸造高铬高碳钢/碳钢耐磨材料微观组织及力学性能的影响

高志喆¹, 陈小艳¹, 王永金², 苏盛睿², 陈俊豪¹, 李佳康², 陈正家¹

1.鞍山钢铁集团有限公司大孤山球团厂, 辽宁鞍山 114004;
2.北京科技大学材料科学与工程学院, 北京 100083

收稿日期:2022-03-25 修回日期:2022-06-27 出版日期:2022-08-25 发布日期:2022-09-19
通讯作者: 王永金,讲师,博士,E-mail:wangyongjin@ustb.edu.cn
作者简介:高志喆(1964—),男,教授级高工,学士,主要研究方向为矿山设备与工艺,E-mail:1119898759@qq.com。

Effect of heat treatment on microstructure and mechanical properties of composite cast high chromium high carbon steel/carbon steel wear-resistant materials

Gao Zhizhe¹, Chen Xiaoyan¹, Wang Yongjin², Su Shengrui², Chen Junhao¹, Li Jiakang², Chen Zhengjia¹

1. Dagushan Pelleting Plant, Anshan Iron & Steel Group Co., Ltd., Anshan Liaoning 114004, China;
2. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China

Received:2022-03-25 Revised:2022-06-27 Online:2022-08-25 Published:2022-09-19

摘要/Abstract

摘要： 采用液-固复合的方法制备铸态复合耐磨试验钢,且分别进行等温淬火和淬火-回火处理,利用扫描电镜、硬度计及冲击性能测试研究了不同的热处理对高铬高碳钢/碳钢复合铸造耐磨钢组织和性能的影响。利用JMatPro软件对试验钢不同温度下平衡相种类与含量进行了计算。结果表明,铸态高铬高碳钢/碳钢复合材料耐磨层的微观组织由网状碳化物和粒状珠光体组成;基体层为由粗大的奥氏体在较快冷速下形成的魏氏组织。等温淬火后试验钢耐磨层形成了网状碳化物+细粒状碳化物+奥氏体+铁素体的微观组织,基体层形成了块状铁素体与珠光体的微观组织;淬火-回火后试验钢耐磨层形成了网状碳化物+细粒状碳化物+马氏体的微观组织,基体层形成马氏体+上贝氏体的微观组织。经过等温淬火的试验钢耐磨层硬度为493 HBW,冲击吸收能量为2.6 J,基体层冲击吸收能量为79.2 J;经过淬火-回火的耐磨层硬度为629 HBW,冲击吸收能量为1.6 J,基体层的冲击吸收能量为20.0 J。考虑复合耐磨钢需要抵抗较高冲击载荷,880 ℃保温2 h空冷至320 ℃保温5.5 h的等温淬火为更优的热处理工艺。

关键词: 高铬高碳钢, 复合铸造, 等温淬火, 淬火-回火, 组织, 性能

Abstract: High chromium high carbon steel/carbon steel composite wear-resistant steel was prepared by using liquid-solid composite method, and the effect of different heat treatments on microstructure and properties of the composite wear-resistant steel treated by austempering and quenching-tempering was studied by means of scanning electron microscope, hardness tester and impact property test, respectively. The types and contents of the equilibrium phases in the tested steel were calculated by using JMatPro software. The results show that the microstructure of the as-cast high chromium high carbon steel/carbon steel composite wear-resistant layer is composed of network carbide and granular pearlite. The substrate layer is a widmanstatten structure formed by coarse austenite at a faster cooling rate. After austempering, the microstructure of the wear-resistant layer of the tested steel is network carbide+fine-grained carbide+austenite+ferrite, and the substrate layer consists of massive ferrite and pearlite. After quenching and tempering, the microstructure of the wear-resistant layer of the tested steel is network carbide+fine-grained carbide+martensite, and the substrate layer is martensite+upper bainite. The hardness of the wear-resistant layer after austempering is 493 HBW, the impact absorbed energy is 2.6 J, and the impact absorbed energy of the substrate layer is 79.2 J. After quenching and tempering, the hardness of the wear-resistant layer is 629 HBW, the impact absorbed energy is 1.6 J, and the impact absorbed energy of the substrate layer is 20.0 J. Considering that the composite wear-resistant steel needs to resist high impact load, the better heat treatment process is austempering: heating at 880 ℃ for 2 h then cooling to 320 ℃ and at which holding for 5.5 h.

Key words: high chromium high carbon steel, composite casting, austempering, quenching-tempering, microstructure, properties

中图分类号:

TG161

高志喆, 陈小艳, 王永金, 苏盛睿, 陈俊豪, 李佳康, 陈正家. 热处理对复合铸造高铬高碳钢/碳钢耐磨材料微观组织及力学性能的影响[J]. 金属热处理, 2022, 47(8): 163-167.

Gao Zhizhe, Chen Xiaoyan, Wang Yongjin, Su Shengrui, Chen Junhao, Li Jiakang, Chen Zhengjia. Effect of heat treatment on microstructure and mechanical properties of composite cast high chromium high carbon steel/carbon steel wear-resistant materials[J]. Heat Treatment of Metals, 2022, 47(8): 163-167.

参考文献

[1]Xiong B W, Cai C C, Wan H, et al. Fabrication of high chromium cast iron and medium carbon steel bimetal by liquid-solid casting in electromagnetic induction field[J]. Materials and Design, 2011, 32(5): 2978-2982.
[2]崔鹏杰, 钟黎声, 白海强, 等. 铸造在层状双金属复合材料中的应用[J]. 热加工工艺, 2020, 49(19): 1-6.
Cui Pengjie, Zhong Lisheng, Bai Haiqiang, et al. Application of casting in layered bimetallic composite materials[J]. Hot Working Technology, 2020, 49(19): 1-6.
[3]Li Y C, Gong M Y, Wang K, et al. Diffusion behavior and mechanical properties of high chromium cast iron/low carbon steel bimetal[J]. Materials Science and Engineering A, 2018, 718: 260-266.
[4]Berski S, Dyja H, Maranda A, et al. Analysis of quality of bimetallic rod after extrusion process[J]. Journal of Materials Processing Technology, 2006, 177(1-3): 582-586.
[5]Krishnaiah A, Chakkingal U, Venugopal P. Applicability of the groove pressing technique for grain refinement in commercial purity copper[J]. Materials Science and Engineering A, 2005, 410: 337-340.
[6]刘宗昌, 计云萍. 贝氏体组织结构辨识方法(一)[J]. 热处理技术与装备, 2018, 39(5): 1-7.
Liu Zongchang, Ji Yunping. Identification methods of bainitic microstructure(I)[J]. Heat Treatment Technology and Equipment, 2018, 39(5): 1-7.
[7]刘宗昌, 计云萍. 贝氏体组织结构辨识方法(二)[J]. 热处理技术与装备, 2018, 39(6): 1-6.
Liu Zongchang, Ji Yunping. Identification methods of bainitic microstructure(II)[J]. Heat Treatment Technology and Equipment, 2018, 39(6): 1-6.
[8]石宁, 李晨. 40CrNiMoA钢轮缘堆焊层裂纹产生原因分析[J]. 理化检验(物理分册), 2016, 52(3): 202-205.
Shi Ning, Li Chen. Formation causes analysis on surfacing layer cracks of the 40CrNiMoA steel rim[J]. Physical Testing and Chemical Analysis (Part A: Physical Testing), 2016, 52(3): 202-205.

[1]	杨晓斌, 董纪, 田春英, 宁保群, 赵倩, 乔志霞, 刘永长. 磁场对25CrMo48V超高强度钢回火组织与力学性能的影响[J]. 金属热处理, 2022, 47(8): 24-33.
[2]	何博, 彭天恩, 胡学文, 蒋波, 郭锐, 石践, 汪飞, 王海波. Nb对高Ti耐候钢连续冷却后显微组织及硬度的影响[J]. 金属热处理, 2022, 47(8): 46-51.
[3]	姜越, 朱柏祥, 李秀明, 谭亚平. CrFeCoNiB_0.05Ti_x高熵合金的显微组织和力学性能[J]. 金属热处理, 2022, 47(8): 58-62.
[4]	刘德佳, 扎学安, 王伟雄, 唐延川, 赵龙志, 徐宏明. 304/Q235复合板多主元高熵化焊缝的组织与性能[J]. 金属热处理, 2022, 47(8): 63-70.
[5]	孟静竹, 刘仁东, 郭金宇, 徐荣杰, 王科强, 潘勇. Fe-Mn-Al-C系轻质钢中含铝碳化物的析出规律[J]. 金属热处理, 2022, 47(8): 71-76.
[6]	秦铁玉, 宋春燕, 马汝成, 张学峰, 郝威, 贵永亮. Si含量对Fe-Cr-Si系合金组织与耐蚀性能的影响[J]. 金属热处理, 2022, 47(8): 77-82.
[7]	胡耕辅, 田玉新, 朱银存, 陆建生, 王福明. 耐蚀软磁合金FeCr16中σ相的析出行为[J]. 金属热处理, 2022, 47(8): 83-87.
[8]	池海涛, 刘馥兵, 胡晓光. 7A41铝合金的力学性能和耐蚀性能[J]. 金属热处理, 2022, 47(8): 88-94.
[9]	张明玉, 运新兵, 伏洪旺. 热处理冷却方式对TC10钛合金组织与性能的影响[J]. 金属热处理, 2022, 47(8): 98-104.
[10]	宋宁宏, 林超, 毕文珍, 王武荣, 韦习成. 回火时间对1800 MPa级热成形钢组织和性能的影响[J]. 金属热处理, 2022, 47(8): 112-117.
[11]	郭文一, 焦海涛, 谢信祥, 赵龙志, 赵明娟, 胡勇. 退火过程中无取向电工钢的晶粒长大行为及磁性能演变[J]. 金属热处理, 2022, 47(8): 123-128.
[12]	陈俭兰, 赵莫迪, 韩福生. 退火对冷轧Cu-Ag合金组织及性能的影响[J]. 金属热处理, 2022, 47(8): 129-134.
[13]	李金波, 吴红艳, 高秀华, 陈红卫, 李绍杰, 朱子颖, 杜林秀. 热处理工艺对高铁耐蚀60Si2Mn弹簧钢组织和性能的影响[J]. 金属热处理, 2022, 47(8): 135-140.
[14]	魏海霞, 潘吉祥, 纪显斌, 李照国, 徐斌. 热处理对经济型高碳马氏体不锈钢J50Cr13组织和硬度的影响[J]. 金属热处理, 2022, 47(8): 148-151.
[15]	冯凌宵, 金浩, 杨丽. PCrNi3Mo钢真空渗铬层的组织与性能[J]. 金属热处理, 2022, 47(8): 168-172.

热处理对复合铸造高铬高碳钢/碳钢耐磨材料微观组织及力学性能的影响

Effect of heat treatment on microstructure and mechanical properties of composite cast high chromium high carbon steel/carbon steel wear-resistant materials

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价