耐磨钢NM400冷弯开裂分析

doi:10.13251/j.issn.0254-6051.2021.09.047

金属热处理 ›› 2021, Vol. 46 ›› Issue (9): 262-267.DOI: 10.13251/j.issn.0254-6051.2021.09.047

耐磨钢NM400冷弯开裂分析

吴昊¹, 邓想涛¹, 李成儒¹, 隋轶², 张涛³, 纪汶伯³, 王昭东¹

1.东北大学轧制技术及连轧自动化国家重点实验室, 辽宁沈阳 110004;
2.鞍山钢铁集团公司技术中心, 辽宁鞍山 114003;
3.鞍山钢铁集团公司产品发展部, 辽宁鞍山 114003

收稿日期:2021-03-29 出版日期:2021-09-25 发布日期:2021-12-09
通讯作者: 邓想涛,副教授,博士,E-mail:Dengxiangtao123@163.com
作者简介:吴昊(1995—),男,硕士研究生,主要研究方向为低合金马氏体耐磨钢,E-mail:18202416631@163.com。

Analysis on cold bending fracture of wear-resistant steel NM400

Wu Hao¹, Deng Xiangtao¹, Li Chengru¹, Sui Yi², Zhang Tao³, Ji Wenbo³, Wang Zhaodong¹

1. State Key Laboratory of Rolling and Automation,Northeastern University, Shenyang Liaoning 110004, China;
2. Technology Center, Ansteel Co., Ltd., Anshan Liaoning 114003, China;
3. Product Development Department, Ansteel Co., Ltd., Anshan Liaoning 114003, China

Received:2021-03-29 Online:2021-09-25 Published:2021-12-09

摘要/Abstract

摘要： 厚度为20 mm的NM400钢板在冷弯过程中开裂。从冷弯工艺参数、材料拉伸性能、显微组织及夹杂物类型、尺寸分布对NM400钢板开裂原因进行了分析。结果表明:NM400钢板冷弯开裂主要由钢板中微米级TiN夹杂物引起。冷弯变形过程中,夹杂物与基体界面处应力集中,导致微裂纹在界面处形核并扩展,最终导致冷弯断裂。通过降低N含量至4×10^-5以下,耐磨钢NM400冷弯过程中无裂纹产生。

关键词: 耐磨钢NM400, 冷弯开裂, TiN夹杂物, 组织性能

Abstract: Aimed at the cold bending fracture in 20 mm thick NM400 plates, the cold bending process parameters, tensile properties, microstructure, inclusion types and size distribution were investigated to find the cause of fracture. The results show that bending fracture in NM400 plate is mainly caused by micron-size TiN inclusions. During the cold bending deformation, the stress concentration at the interface between inclusion and matrix leads to the nucleation and propagation of microcracks, and eventually leads to cold bending fracture. By reducing N content to below 4×10^-5, the cracking risk during cold bending process of NM400 steel is disappeared.

Key words: wear-resistant steel NM400, cold bending fracture, TiN inclusion, microstructure and properties

中图分类号:

TG142.1

吴昊, 邓想涛, 李成儒, 隋轶, 张涛, 纪汶伯, 王昭东. 耐磨钢NM400冷弯开裂分析[J]. 金属热处理, 2021, 46(9): 262-267.

Wu Hao, Deng Xiangtao, Li Chengru, Sui Yi, Zhang Tao, Ji Wenbo, Wang Zhaodong. Analysis on cold bending fracture of wear-resistant steel NM400[J]. Heat Treatment of Metals, 2021, 46(9): 262-267.

参考文献

[1]王昭东, 邓想涛, 曹艺, 等. 新型低成本超高强低合金耐磨钢研究及其工业化应用[J]. 钢铁, 2010, 45(8): 61-64.
Wang Zhaodong, Deng Xiangtao, Cao Yi, et al. Development and industrial application of new low alloy abrasion steel with low cost and ultra-high strength[J]. Iron and Steel, 2010, 45(8): 61-64.
[2]邓想涛, 王昭东, 王日清, 等. 低合金超高强耐磨钢在线热处理工艺研究[C]// 2009年全国高品质热轧板带材控轧控冷与在线、离线热处理生产技术交流研讨会文集. 2009: 106-109.
Deng Xiangtao, Wang Zhaodong, Wang Riqing, et al. On-line hot treatment process study of super high strength low alloy abrasion steel[C]// Proceedings of the 2009 National Symposium on Controlled Rolling and Cooling of High Quality Hot Rolled Plates and Strips and On-line and Off-line Heat Treatment Production Technology Exchange. 2009: 106-109.
[3]崔风平. 中厚钢板冷弯裂纹与开裂原因分析[J]. 宽厚板, 2017, 23(1): 42-45.
Cui Fengping. Causes analysis on cold bend cracking and opening of medium steel plate[J]. Wide and Heavy Plate, 2017, 23(1): 42-45.
[4]Saeidi N, Ashrafizadeh F, Niroumand B. Evaluation of fracture micromechanisms in a fine-grained dual phase steel during uniaxial tensile deformation[J]. Steel Research International, 2015, 85(9): 1386-1392.
[5]覃登攀. 组织结构及夹杂物对高强结构厚板冷弯开裂影响的研究[J]. 冶金分析, 2018, 38(9): 41-45.
Tan Dengpan. Investigation on the influence of structure and inclusion on cold bending cracking of high strength structural thick plate[J]. Metallurgical Analysis, 2018, 38(9): 36-40.
[6]康伟, 方恩俊, 李超, 等. Q345B钢直装轧制厚板冷弯裂纹分析[J]. 炼钢, 2014, 30(3): 16-19.
Kang Wei, Fang Enjun, Li Chao, et al. Analysis of cold bending crack on Q345B direct rolling thick plate[J]. Steelmaking, 2014, 30(3): 16-19
[7]吴石新, 陈登福, 汪勤政, 等. 钛微合金钢连铸中TiN与TiC析出热力学研究[J]. 连铸, 2019, 44(1): 28-34.
Wu Shixin, Chen Dengfu, Wang Qinzheng, et al. Thermodynamic study on precipitation of TiN and TiC in continuous casting of titanium microalloyed steel[J]. Continuous Casting, 2019, 44(1): 28-34.

[1]	黄龙, 邓想涛, 王昭东. 回火温度对颗粒增强型低合金耐磨钢组织和性能的影响[J]. 金属热处理, 2022, 47(3): 1-6.
[2]	李敏娜, 马保飞, 郭金明, 吴晨, 肖松涛. 高强韧TB8钛合金的热处理制度[J]. 金属热处理, 2021, 46(9): 116-119.
[3]	花思明, 张平则, 刘子利. CuCr1合金接触线的时效工艺及组织性能[J]. 金属热处理, 2021, 46(5): 143-149.
[4]	王思成, 周丹, 柴希阳, 佟石, 杨洋, 王天琪. 控轧控冷工艺对440 MPa级船体钢组织与性能的影响[J]. 金属热处理, 2021, 46(4): 138-142.
[5]	陈卓, 王诚斯, 靳斌, 刘靖宝, 郝雷, 邝霜, 王金荣. 980 MPa级冷轧复相钢力学性能的多元调控[J]. 金属热处理, 2021, 46(4): 157-160.
[6]	石晓霞, 任慧平, 李晓, 王超, 宫鑫. 26CrMoVNbRE钢高效热处理调质工艺边界探索[J]. 金属热处理, 2021, 46(3): 39-45.
[7]	王科强, 刘仁东, 郭金宇, 付薇, 黄秋菊, 孙荣生. 汽车用800 MPa级冷轧低合金高强钢的研制[J]. 金属热处理, 2021, 46(1): 120-124.
[8]	王润勋, 王宝峰, 李岩, 定巍, 潘红波. 0.2C-5Mn-1.5Al中锰TRIP钢的显微组织及力学性能[J]. 金属热处理, 2020, 45(4): 63-68.
[9]	杨跃辉, 苑少强, 郭继富, 韩会杰, 张艳龙. 回火温度对锯片用复合钢板组织性能的影响[J]. 金属热处理, 2020, 45(2): 214-217.
[10]	陈伟, 侯兴慧, 徐锟. 不同制备工艺对锻造高速钢轧辊组织和性能的影响[J]. 金属热处理, 2020, 45(11): 167-170.
[11]	綦秀玲1,2，孙琳琳1，张勇1. 磁场频率对AZ91合金焊接接头直接时效的组织和性能的影响[J]. 金属热处理, 2016, 41(5): 149-152.
[12]	郝志勇，张凤嘉，岳立新. 27SiMn钢的Ni-Ce-P化学镀工艺及镀层性能[J]. 金属热处理, 2016, 41(11): 140-144.
[13]	吝章国1,2，唐荻1，江海涛1，段晓鸽1，吴彦欣3. 淬火温度对中锰Q&P钢组织性能的影响[J]. 金属热处理, 2016, 41(10): 123-127.
[14]	张利平1，刘艳林1，韩杰1，李俊玉2，许荣昌1. 冷却工艺对Ti微合金高强钢组织和性能的影响[J]. 金属热处理, 2016, 41(1): 74-78.
[15]	刘腾轼，杨弋涛. 多元低合金耐磨铸钢热处理过程中碳化物析出行为的研究[J]. 金属热处理, 2015, 40(9): 33-39.

耐磨钢NM400冷弯开裂分析

Analysis on cold bending fracture of wear-resistant steel NM400

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价