渗氮后氧化处理40Cr钢的耐蚀性能

doi:10.13251/j.issn.0254-6051.2021.04.040

金属热处理 ›› 2021, Vol. 46 ›› Issue (4): 217-219.DOI: 10.13251/j.issn.0254-6051.2021.04.040

渗氮后氧化处理40Cr钢的耐蚀性能

岳佳宏, 孟璇, 姚小卫, 孔令飞, 杨阳, 秦国方

山西航天清华装备有限责任公司, 山西长治 046012

收稿日期:2020-10-02 出版日期:2021-04-25 发布日期:2021-05-08
作者简介:岳佳宏(1990—),女,工程师,主要研究方向为热表处理、焊接等,E-mail:a03583032085@163.com

Corrosion resistance of 40Cr steel after nitriding and oxidation treatment

Yue Jiahong, Meng Xuan, Yao Xiaowei, Kong Lingfei, Yang Yang, Qin Guofang

Shanxi Aerospace Qinghua Equipment Co., Ltd., Changzhi Shanxi 046012, China

Received:2020-10-02 Online:2021-04-25 Published:2021-05-08

摘要/Abstract

摘要： 通过盐雾腐蚀试验法,对不同温度渗氮+后氧化处理的40Cr钢试样及不同表面防护状态下的40Cr钢试样的耐蚀性能进行对比。结果表明,40Cr钢渗氮温度在560～580 ℃之间时,中性盐雾试验时间可达200 h以上;对渗氮后氧化处理后的40Cr钢试验件边缘保护及油封处理后,中性盐雾试验时间可达200 h,外观评级(R_A)为10。

关键词: 40Cr钢, 盐雾腐蚀试验, 渗氮后氧化, 表面防护状态, 耐蚀性能

Abstract: The corrosion resistance of 40Cr steel with different nitriding temperature and post oxidation treatment was compared, and the corrosion resistance of 40Cr steel under different surface protection conditions were compared through the salt spray corrosion test method. The results show that when the nitriding temperature of 40Cr steel is between 560 ℃ and 580 ℃, the neutral salt spray test time can reach more than 200 h; after the edge protection and oil seal treatment of the 40Cr steel trented by nitriding oxidation treatment, the neutral salt spray test time can reach 200 h, and the appearance rating (R_A) is 10.

Key words: 40Cr steel, neutral salt spray test, nitriding and oxidation treatment, surface states, corrosion resistance

中图分类号:

TG156.82

岳佳宏, 孟璇, 姚小卫, 孔令飞, 杨阳, 秦国方. 渗氮后氧化处理40Cr钢的耐蚀性能[J]. 金属热处理, 2021, 46(4): 217-219.

Yue Jiahong, Meng Xuan, Yao Xiaowei, Kong Lingfei, Yang Yang, Qin Guofang. Corrosion resistance of 40Cr steel after nitriding and oxidation treatment[J]. Heat Treatment of Metals, 2021, 46(4): 217-219.

参考文献

[1] 刘林飞,周上祺,黄玉堂.40Cr钢氮气/甲烷离子氮碳共渗后的组织和耐磨性[J].热加工工艺,2007,36(12):49-54.
Liu Linfei,Zhou Shangqi,Huang Yutang.Microstructure and wear resistance of 40Cr steel ion-nitrocarburized in nitrogen and methane[J].Hot Working Technology,2007,36(12):49-54.
[2] 商兴国,王杰.40Cr钢亚温淬火氮碳共渗工艺试验研究[J].煤矿机械,2011,32(10):142-143.
Shang Xingguo,Wang Jie.Study on sub-tempering quenching and nitrocarburizing of 40Cr steel[J].Coal Mine Machinery,2011,32(10):142-143.
[3] 赵程,刘基凯.离子氮碳共渗后的氧化处理对40Cr钢耐蚀性能的影响[J].金属热处理,2009,34(1):75-77.
Zhao Cheng,Liu Jikai.Effect of post oxidation on corrosion resistance of 40Cr steel after plasma nitrocarburizing[J].Heat Treatment of Metals,2009,34(1):75-77.
[4] 杨汉高,侯惠君,刘仲武,等.结构钢等离子氮碳共渗与氧化复合处理概述和应用[J].热加工工艺,2013,42(6):135-139.
Yang Hangao,Hou Huijun,Liu Zhongwu,et al.Summary and Application of duplex treatment of plasma nitrocarburizing and post-oxidation for structural steel[J].Hot Working Technology,2013,42(6):135-139.
[5] Hong J M,Cho Y R,Kim D J,et al.Plasma post-oxidation process fornitrocarburized layer[J].Surface and Coatings Technology,2000,131(1-3):548-552.
[6] 杨汉高,侯惠君,刘仲武,等.42CrMo钢等离子氮碳共渗厚化合物层工艺及组织性能[J].金属热处理,2012,37(12):10-13.
Yang Hangao,Hou Huijun,Liu Zhongwu,et al.Plasma nitrocarburising process and microstructure and properties for high thickness compound layer of 42CrMo steel[J].Heat Treatment of Metals,2012,37(12):10-13.
[7] 张希平,王美由,高中楠,等.氮碳共渗+后氧化复合处理的应用研究[J].金属热处理,2017,42(7):107-111.
Zhang Xiping,Wang Meiyou,Gao Zhongnan,et al.Application research of combined treatment of nitrocarburizing and post-oxidizing[J].Heat Treatment of Metals,2017,42(7):107-111.
[8] 燕来生.温度和氮势对氮碳共渗层致密性的影响[J].兵器材料科学与工程,2000,23(6):33-36.
Yan Laisheng.Influence of Temperature and nitrogen-concentration on tightness of nitrocarburizing layer[J].Ordnance Material Science and Engineering,2000,23(6):33-36.

[1]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[2]	王荣, 龚玉辉, 殷学俊, 魏德强. 多道电子束扫描搭接率对40Cr钢组织与性能的影响[J]. 金属热处理, 2022, 47(3): 191-197.
[3]	孟璇, 姚小卫, 孔令飞. 渗氮后氧化技术的适用性分析[J]. 金属热处理, 2021, 46(6): 126-128.
[4]	杨亚杰, 常远, 郭胤, 周玉宁, 林冰涛, 杨三龙, 孙晓霞. 固溶处理对ZG40Cr25Ni20Si2耐热钢耐蚀性能的影响[J]. 金属热处理, 2021, 46(5): 175-179.
[5]	田芳, 纪秀林, 赵立娟, 赵建华. CO₂气氛和喷涂距离对电弧喷涂铁基非晶涂层组织及耐蚀性能的影响[J]. 金属热处理, 2021, 46(5): 218-223.
[6]	孟璇, 岳佳宏, 孔令飞, 杨阳, 贾鹏. 渗氮温度对42CrMo钢零件表面后氧化渗层的影响[J]. 金属热处理, 2021, 46(2): 182-184.
[7]	李苗苗, 邹德宁, 佟立波, 庞阳. N含量对13Cr超级马氏体不锈钢耐蚀性的影响[J]. 金属热处理, 2021, 46(12): 107-112.
[8]	程源, 胡芳忠, 杨少朋, 汪开忠, 金国忠, 陈世杰, 王良林. 汽车前轴用40Cr钢锻件开裂失效分析[J]. 金属热处理, 2021, 46(12): 294-297.
[9]	康学勤, 许正茂, 林恩波, 陈亮. “零保温”淬火工艺对40Cr钢组织与性能的影响[J]. 金属热处理, 2020, 45(8): 105-107.
[10]	雷丰荣, 李晖. 40Cr钢TD盐浴渗钒制备VC渗层的组织形貌[J]. 金属热处理, 2020, 45(7): 177-182.
[11]	李晶, 张丽凤, 王社则. 汽车发动机用AZ91D合金的表面喷涂与性能[J]. 金属热处理, 2020, 45(1): 228-233.
[12]	张　琪，罗丽蓉，刘　涛，秦子兰. 船舶海水管系TC4钛合金的表面涂层与耐蚀性能[J]. 金属热处理, 2019, 44(1): 185-189.
[13]	曹韩学1,2，唐浩兴1,2，贾从波1,2，高永帅1,2，雷佳乐3. 表面处理对模具钢耐蚀性能的影响[J]. 金属热处理, 2016, 41(7): 66-69.
[14]	乔静飞1，张明明1，张小麟2，张克冰1，张圣麟1. 氧化钇纳米颗粒对无铬达克罗涂层耐蚀性能的影响[J]. 金属热处理, 2016, 41(7): 178-181.
[15]	吴勉，潘邻，张良界，李朋，杨闽红，马飞，陈亚平. 气体氧-氮碳复合处理40Cr钢硬化层的组织及耐蚀性[J]. 金属热处理, 2016, 41(5): 156-159.

渗氮后氧化处理40Cr钢的耐蚀性能

Corrosion resistance of 40Cr steel after nitriding and oxidation treatment

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价