渗氮温度对42CrMo钢零件表面后氧化渗层的影响

doi:10.13251/j.issn.0254-6051.2021.02.033

金属热处理 ›› 2021, Vol. 46 ›› Issue (2): 182-184.DOI: 10.13251/j.issn.0254-6051.2021.02.033

渗氮温度对42CrMo钢零件表面后氧化渗层的影响

孟璇, 岳佳宏, 孔令飞, 杨阳, 贾鹏

山西航天清华装备有限责任公司, 山西长治 046012

收稿日期:2020-07-19 出版日期:2021-02-25 发布日期:2021-05-08
作者简介:孟璇(1990—),女,工程师,硕士,主要研究方向为各种材质零件的热处理工艺,E-mail:346311233@qq.com

Effect of nitriding temperature on post-oxidating infiltrated layer of 42CrMo steel part surface

Meng Xuan, Yue Jiahong, Kong Lingfei, Yang Yang, Jia Peng

Shanxi Aerospace Qinghua Equipment Co., Ltd., Changzhi Shanxi 046012, China

Received:2020-07-19 Online:2021-02-25 Published:2021-05-08

摘要/Abstract

摘要： 采用硬度测试、显微组织观察、脆性等级和疏松等级评价等方法研究了渗氮温度对42CrMo钢零件渗氮后氧化渗层性能的影响。结果表明:在渗氮后氧化处理过程中,渗层的表面硬度随着渗氮温度的升高出现先增后降的趋势;渗层深度和疏松等级随渗氮温度的升高而增加,但脆性等级变化不大。当渗氮温度为560 ℃时,42CrMo钢零件可获得表面硬度≥600 HV、渗层(白亮层)深度≥15 μm、1级脆性等级、2级疏松等级的优秀渗层。

关键词: 42CrMo钢, 渗氮后氧化, 表面硬度, 渗层深度, 脆性等级, 疏松等级

Abstract: Effect of nitriding temperature on properties of the infiltrated layer of 42CrMo steel parts treated by the process of nitriding with post-oxidating was studied by means of hardness test, microstructure observation, and evaluation of brittleness grade and porosity grade. The results show that the thickness and porosity grade of the infiltrated layer increase with the increase of nitriding temperature, but the brittleness grade changes little. The surface hardness of the infiltrated layer increases first and then decreases with the increase of nitriding temperature. When the nitriding temperature is 560 ℃, the 42CrMo steel parts can obtain infiltrated layer with excellent properties, of which the surface hardness and the thickness of infiltrated layer is ≥600 HV and ≥15 μm respectively, the brittleness and the porosity of infiltrated layer is grade 1 and grade 2, respectively.

Key words: 42CrMo steel, nitriding with post-oxidating, surface hardness, infiltrated layer thickness, brittleness grade, porosity grade

中图分类号:

TG156.8⁺2

孟璇, 岳佳宏, 孔令飞, 杨阳, 贾鹏. 渗氮温度对42CrMo钢零件表面后氧化渗层的影响[J]. 金属热处理, 2021, 46(2): 182-184.

Meng Xuan, Yue Jiahong, Kong Lingfei, Yang Yang, Jia Peng. Effect of nitriding temperature on post-oxidating infiltrated layer of 42CrMo steel part surface[J]. Heat Treatment of Metals, 2021, 46(2): 182-184.

参考文献

[1] 杨汉高,侯惠君,刘仲武,等.42CrMo钢等离子氮碳共渗厚化合物层工艺及组织性能[J].金属热处理,2012,37(12):10-13.
Yang Hangao,Hou Huijun,Liu Zhongwu,et al.Plasma nitrocarburising process and microstructure and properties for high thickness compound layer of 42CrMo steel[J].Heat Treatment of Metals,2012,37(12):10-13.
[2] 张希平,王美由,高中楠,等.氮碳共渗+后氧化复合处理的应用研究[J].金属热处理,2017,42(7):107-111.
Zhang Xiping,Wang Meiyou,Gao Zhongnan,et al.Application research of combined treatment of nitrocarburizing and post-oxidizing[J].Heat Treatment of Metals,2017,42(7):107-111.
[3] Fares M L,Chaoui K,Coze J L.Post-oxidizing effects on surface characteristics of salt bath nitrocarburized AISI 02 tool steel type[J].Surface and Interface Analysis,2010,41(7):549-559.
[4] 杨汉高,侯惠君,刘仲武,等.结构钢等离子氮碳共渗与氧化复合处理概述和应用[J].热加工工艺,2013,42(6):135-139.
Yang Hangao,Hou Huijun,Liu Zhongwu,et al.Summary and application of duplex treatment of plasma nitrocarburizing and post-oxidation for structural steel[J].Hot Working Technology,2013,42(6):135-139.
[5] 赵程,刘基凯.离子氮碳共渗后的氧化处理对40Cr钢耐蚀性能的影响[J].金属热处理,2009,34(1):75-77.
Zhao Cheng,Liu Jikai.Effect of post oxidation on corrosion resistance of 40Cr steel after plasm a nitrocarburizing[J].Heat Treatment of Metals,2009,34(1):75-77.
[6] 赵程,孙定国,赵慧丽,等.离子氮碳共渗+离子后氧化双重复合处理的研究[J].金属热处理,2004,29(9):11-13.
Zhao Cheng,Sun Dingguo,Zhao Huili,et al.Duplex treatments of plasma nitrocarburizing and post-oxidation[J].Heat Treatment of Metals,2004,29(9):11-13.
[7] 武计强.42CrMo离子渗氮后氧化及氮氧共渗研究[D].常州:常州大学,2015.
Wu Jiqiang.Study on plasma post-oxidation after nitriding and plasma oxynitriding for AISI 4140 steel[D].Changzhou:Changzhou University,2015.
[8] Hong J M,Cho Y R,Kim D J,et al.Plasma post-oxidation process for nitrocarburized layer[J].Surface and Coatings Technology,2000,131(1/3):548-552.

[1]	杨杰, 汪西, 周杰, 武建祥, 屈志远, 代合平, 彭海军. 转向节锻件枝丫结构淬火裂纹形成机理[J]. 金属热处理, 2022, 47(4): 263-267.
[2]	吴辉, 林升垚, 李新凯, 龚玉辉, 魏德强. 感应淬火对42CrMo钢曲轴连杆轴颈组织性能的影响[J]. 金属热处理, 2022, 47(2): 119-124.
[3]	王自力, 陈荣发, 郑志伟, 何玉龙, 史敏杰, 王锴, 周晓进. 42CrMo钢活塞杆表面氧氮复合渗层的显微组织和耐磨性能[J]. 金属热处理, 2021, 46(8): 225-229.
[4]	孟璇, 姚小卫, 孔令飞. 渗氮后氧化技术的适用性分析[J]. 金属热处理, 2021, 46(6): 126-128.
[5]	焦丽, 商海昆, 何剑丰, 赵英军, 张伟民, 李卫民, 周兰梅. 柴油机用42CrMo钢高强度螺栓断裂失效分析[J]. 金属热处理, 2021, 46(6): 245-249.
[6]	彭则, 李萌蘖, 卜恒勇, 李其. 42CrMo钢加热过程中的奥氏体晶粒尺寸演变[J]. 金属热处理, 2021, 46(5): 25-31.
[7]	马晓锋, 马宁. 真空压强对小模数花键离子渗氮性能的影响[J]. 金属热处理, 2021, 46(5): 190-192.
[8]	潘虹吉, 罗德福, 陈甥怡. 氮碳氧复合处理(QPQ)对MPS700A钢组织与性能的影响[J]. 金属热处理, 2021, 46(4): 83-87.
[9]	岳佳宏, 孟璇, 姚小卫, 孔令飞, 杨阳, 秦国方. 渗氮后氧化处理40Cr钢的耐蚀性能[J]. 金属热处理, 2021, 46(4): 217-219.
[10]	焦咏翔, 邓德伟, 孙奇, 李天澍, 杨树华, 张勇, 马玉山. 工艺参数对42CrMo钢激光淬火效果的影响[J]. 金属热处理, 2021, 46(11): 90-96.
[11]	张青, 曹培. 回火温度对42CrMo钢棒感应调质组织及力学性能的影响[J]. 金属热处理, 2021, 46(11): 182-185.
[12]	高志喆, 陈小艳, 程福超, 李佳康, 苏盛睿, 王永金. 中间高温回火工艺对15MnNi4MoA渗碳钢微观组织及性能的影响[J]. 金属热处理, 2021, 46(10): 178-181.
[13]	原瑞泽, 闫献国, 陈峙, 郭蕊, 兰东生, 苏杭, 姚永超. 深冷处理对YG8硬质合金/42CrMo钢钎焊接头残余应力的影响[J]. 金属热处理, 2021, 46(10): 204-208.
[14]	吕超然, 史超, 蒋伟斌, 刘进德, 徐乐, 王毛球. 回火温度对42CrMo钢组织和力学性能的影响[J]. 金属热处理, 2021, 46(1): 32-37.
[15]	张海东, 闫献国, 陈峙, 赵敏娜, 高源, 李俊吉, 李晋峰, 高丽梅. 冷处理对42CrMo钢硬度和耐磨性的影响[J]. 金属热处理, 2020, 45(9): 96-98.

渗氮温度对42CrMo钢零件表面后氧化渗层的影响

Effect of nitriding temperature on post-oxidating infiltrated layer of 42CrMo steel part surface

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价