30CrNi3MoV钢的热变形行为及热加工图

doi:10.13251/j.issn.0254-6051.2020.10.005

摘要/Abstract

摘要： 采用Gleeble-3500热模拟试验机对30CrNi3MoV钢进行单向热压缩试验,研究了其在变形温度950~1150 ℃、应变速率0.01~10 s^-1的热变形行为,构建了应变补偿型流变应力本构方程,并绘制出该钢的热加工图。结果表明,30CrNi3MoV钢真应力-真应变曲线有3种不同特征:高温小应变速率时,表现为典型的动态再结晶过程;低温小应变速率时,曲线为动态回复特征;应变速率较大时,应力随应变的增大而增大,无明显的峰值应力。采用5次多项式拟合构建的应变耦合流变应力本构方程具有高的精确度,采用该方程获得的预测值与试验值的平均相对误差为3.2%,相关性系数R值为0.993。从热加工图中得到试验钢最佳的热加工工艺参数范围是:变形温度为1020~1150 ℃、应变速率为0.03~0.35 s^-1。

关键词: 30CrNi3MoV钢, 热变形行为, 真应力-真应变曲线, 本构方程, 热加工图

Abstract: Unidirectional thermal compression tests on 30CrNi3MoV steel were carried out by using Gleeble-3500 thermal-mechanical simulator, the hot deformation behaviors at deformation temperatures of 950-1150 ℃ and strain rates of 0.01-10 s^-1 were studied, the strain-compensated flow stress constitutive equation and the processing map were established for the 30CrNi3MoV steel. The results show that the true stress-strain curves of the 30CrNi3MoV steel have three characteristics:(i)under conditions of high temperature and small strain rate, being typical dynamic recrystallization process; (ii) under conditions of low temperature and small strain rate,characterized as dynamic recovery; and (iii) when the strain rate is large, the stress increases with the increase of strain, and there is no obvious peak stress. The modified strain coupled flow stress constitutive equation displays highest accuracy when constructed by using the 5-degree polynomial fitting, by which the obtained mean relative error between the predicted and the experimental values is 3.2%, and the correlation coefficient R is 0.993.The hot processing map shows that the optimum deformation temperature and strain rate ranges for the 30CrNi3MoV steel are 1020-1150 ℃ and 0.03-0.35 s^-1, respectively.

Key words: 30CrNi3MoV steel, hot deformation behavior, true stress-strain curve, constitutive equation, hot processing map

中图分类号:

TG142.1⁺2

储滔, 沈慧, 斯庭智. 30CrNi3MoV钢的热变形行为及热加工图[J]. 金属热处理, 2020, 45(10): 24-30.

Chu Tao, Shen Hui, Si Tingzhi. Hot deformation behavior and hot processing map of 30CrNi3MoV steel[J]. Heat Treatment of Metals, 2020, 45(10): 24-30.

参考文献

[1]刘丽娟. 大锻件材料内部空洞型缺陷高温焊合过程的研究[D]. 上海: 上海交通大学, 2010.
Liu Lijuan. Study on the bonding process of inner void defects in heavy forging at high temperature[D]. Shanghai: Shanghai Jiao Tong University, 2010.
[2]任运来. 大型锻件内部缺陷修复条件和修复方法研究[D]. 秦皇岛: 燕山大学, 2003.
Ren Yunlai. Study on healing condition and method of internal defect of large forgings[D]. Qinhuangdao: Yanshan University, 2003.
[3]黄倩, 温彤, 刘清, 等. 大型锻件组织与性能的影响因素及其控制技术[J]. 热加工工艺, 2015, 44(13): 6-8.
Huang Qian, Wen Tong, Liu Qing, et al. Affecting factors and control technology of microstructure and properties of large forgings[J]. Hot Working Technology, 2015, 44(13): 6-8.
[4]李凯强, 杨银辉, 钱昊, 等. 03Cr18NiMoN节镍双相不锈钢的热变形行为及热加工图[J]. 钢铁研究学报, 2019, 31(6): 563-572.
Li Kaiqiang, Yang Yinhui, Qian Hao, et al. Hot deformation behavior and hot working drawing of 03Cr18NiMoN low-nickel duplex stainless steel[J]. Journal of Iron and Steel Research, 2019, 31(6): 563-572.
[5]Quan G Z, Shi R J, Zhao J, et al. Modeling of dynamic recrystallization volume fraction evolution for AlCu4SiMg alloy and its application in FEM[J]. Transactions of Nonferrous Metals Society of China, 2019, 29(6): 1138-1151.
[6]马潇, 徐乐, 王毛球, 等. 25Cr3Mo3NiNbZr钢热变形行为及微观组织研究[J]. 热加工工艺, 2019, 48(19): 23-29.
Ma Xiao, Xu Le, Wang Maoqiu, et al. Study on hot deformation behavior and microstructure of 25Cr3Mo3NiNbZr steel[J]. Hot Working Technology, 2019, 48(19): 23-29.
[7]蔡薇, 高鹏哲, 陈辉明, 等. Cu-Cr-Zr-Ti合金高温热变形行为及热加工图[J]. 金属热处理, 2019, 44(8): 147-154.
Cai Wei, Gao Pengzhe, Chen Huiming, et al. High temperature deformation behavior and hot processing map of Cu-Cr-Zr-Ti alloy[J]. Heat Treatment of Metals, 2019, 44(8): 147-154.
[8]乔志霞, 刘永长, 严泽生, 等. 30CrNi3MoV低合金超高强钢中的马氏体相变[J]. 材料科学与工艺, 2012, 20(5): 138-142.
Qiao Zhixia, Liu Yongchang, Yan Zesheng, et al. Martensitic transformation in the 30CrNi3MoV low-alloy ultra-high strength steel[J]. Materials Science and Technology, 2012, 20(5): 138-142.
[9]李强, 马常祥, 赖祖涵. 30CrNi3MoV钢绝热剪切带中微观组织的演变[J]. 钢铁研究学报, 1996(1): 25-28.
Li Qiang, Ma Changxiang, Lai Zuhan. Microstructural change during adiabatic shear band formation in 30CrNi3MoV steel[J]. Journal of Iron and Steel Research, 1996(1): 25-28.
[10]赵洛凯, 要玉宏. 工程机械用30CrNi3MoV钢的热处理与组织性能[J]. 金属热处理, 2019, 44(7): 125-130.
Zhao Luokai, Yao Yuhong. Heat treatment of construction machinery steel 30CrNi3MoV and its microstructure and properties[J]. Heat Treatment of Metals, 2019, 44(7): 125-130.
[11]Jonas J J, Sellars C M, Tegart W J M. Strength and structure under hot-working conditions[J]. International Materials Reviews, 1969, 14(1): 1-24.
[12]刘建军, 王克鲁, 鲁世强, 等. Ti-Nb合金热变形行为及应变耦合本构模型[J]. 材料热处理学报, 2019, 40(5): 156-161.
Liu Jianjun, Wang Kelu, Lu Shiqiang, et al. Hot deformation behavior and strain compensation constitutive model of Ti-Nb alloy[J]. Transactions of Materials and Heat Treatment, 2019, 40(5): 156-161.
[13]赵宏禹, 刘荣佩, 王长军, 等. 9Ni马氏体不锈钢的热变形行为及其能量耗散图[J]. 钢铁, 2018, 53(9): 74-79.
Zhao Hongyu, Liu Rongpei, Wang Changjun, et al. Hot deformation behavior and energy dissipation diagram of 9Ni martensite stainless steel[J]. Iron and Steel, 2018, 53(9): 74-79.
[14]袁武华, 龚雪辉, 孙永庆, 等. 0Cr16Ni5Mo低碳马氏体不锈钢的热变形行为其热加工图[J]. 材料工程, 2016, 44(5): 8-14.
Yuan Wuhua, Gong Xuehui, Sun Yongqing, et al. Hot deformation behavior and processing map of 0Cr16Ni5Mo low carbon martensitic stainless steel[J]. Journal of Materials Engineering, 2016, 44(5): 8-14.
[15]张威, 闫东娜, 邹德宁, 等. 超低碳13Cr-5Ni-2Mo马氏体不锈钢热变形行为及本构关系[J]. 钢铁, 2012, 47(5): 69-74.
Zhang Wei, Yan Dongna, Zou Dening, et al. Hot deformation behavior and constitutive relationship for super-low carbon 13Cr-5Ni-2Mo martensitic stainless steel[J]. Iron and Steel, 2012, 47(5): 69-74.
[16]Zener C, Hollomon J H. Effect of strain rate upon plastic flow of steel[J]. Journal of Applied Physics, 1944, 15(1): 22-32.
[17]程晓农, 桂香, 罗锐, 等. 核电装备用奥氏体不锈钢的高温本构模型及动态再结晶[J]. 材料导报, 2019, 33(11): 1775-1781.
Cheng Xiaonong, Gui Xiang, Luo Rui, et al. Constitutive equation and dynamic recrystallization behavior of 316L austenitic stainless steel for nuclear power equipment[J]. Materials Reports, 2019, 33(11): 1775-1781.
[18]罗锐, 程晓农, 徐桂芳, 等. 新型Fe-20Cr-30Ni-0.6Nb-2Al-Mo合金热变形行为及本构模型[J]. 稀有金属, 2017, 41(2): 132-140.
Luo Rui, Cheng Xiaonong, Xu Guifang, et al. Constitutive modeling for elevated temperature flow behavior of Fe-20Cr-30Ni-0.6Nb-2Al-Mo alloy[J]. Chinese Journal of Rare Metals, 2017, 41(2): 132-140.
[19]Prasad Y V R K. Processing maps: A status report[J]. Journal of Materials Engineering and Performance, 2003, 12(6): 638-645.
[20]Prasad Y V R K. Dynamic materials model: Basis and principles[J]. Metallurgical and Materials Transactions A, 1996, 27(1): 235-236.
[21]Prasad Y V R K, Seshacharyulu T. Modelling of hot deformation for microstructural control[J]. International Materials Reviews, 1998, 43(6): 243-258.
[22]Prasad Y V R K, Rso K P. Effect of homogenization on the hot deformation behavior of cast AZ31 magnesium alloy[J]. Materials and Design, 2009, 30(9): 3723-3730.