6063铝合金双道次热变形微观组织演变

doi:10.13251/j.issn.0254-6051.2020.05.005

金属热处理 ›› 2020, Vol. 45 ›› Issue (5): 23-28.DOI: 10.13251/j.issn.0254-6051.2020.05.005

6063铝合金双道次热变形微观组织演变

王冠^1,2, 田昌龄³, 寇琳媛^1,2, 卞东伟¹

1. 宁夏大学机械工程学院, 宁夏银川 750021;
2. 宁夏大学宁夏智能装备CAE重点实验室, 宁夏银川 750021;
3. 河南科技大学机电工程学院, 河南洛阳 471003

收稿日期:2019-10-23 出版日期:2020-05-25 发布日期:2020-09-02
作者简介:王冠(1985—),男,副教授,博士,主要研究方向为结构轻量化设计,E-mail: belonging@163.com
基金资助:
国家自然科学基金(51605234);宁夏自然科学基金(2018AAC03061,2019AAC03031);宁夏重点研发计划项目(西部之光2017);西部一流重大创新项目(ZKZD2017010)

Microstructure evolution of 6063 aluminum alloy during double-pass hot deformation

Wang Guan^1,2, Tian Changling³, Kou Linyuan^1,2, Bian Dongwei¹

1. School of Mechanical Engineering, Ningxia University, Yinchuan Ningxia 750021, China;
2. The Key Laboratory of CAE Technology for Intelligent Equipment, Ningxia University, Yinchuan Ningxia 750021, China;
3. College of Mechatronics Engineering, Henan University of Science and Technology, Luoyang Henan 471003, China

Received:2019-10-23 Online:2020-05-25 Published:2020-09-02

摘要/Abstract

摘要： 采用Gleeble-1500热模拟试验机对6063铝合金进行双道次热轧试验,分析了合金在变形温度为300~500 ℃,应变速率为0.001~0.1 s^-1,道次间停留时间10~90 s时的流变应力和微观组织。结果表明:随着道次间停留时间增长,第二道次屈服应力减小;温度与道次间停留时间对合金的静态软化率有较大的影响。低温大应变速率短道次间停留时间下试样的强化相较多,其形貌为长条状与圆形;高温低应变速率长道次间停留时间下试样的强化相数量有所减少,其形貌以圆形为主。通过能谱分析可知,试样中的强化相以AlFeSi为主,长条状强化相为6 μm左右,圆形强化相尺寸约2 μm。

关键词: 6063铝合金, 双道次, 热压缩, 流变应力, 微观组织

Abstract: Double-pass hot rolling test on 6063 aluminum alloy was carried out by using Gleeble-1500 thermal simulator. Flow stress and microstructure of the alloy when the deformation temperature was 300-500 ℃, the strain rate was 0.001-0.1 s^-1 and the residence time between passes was 10-90 s were analyzed. The results show that the yield stress of the second pass decreases with the increase of the residence time between passes, and the static softening rate of the alloy is affected by the temperature and the residence time between passes. There is more strengthening phase in the double-pass hot rolled alloy under the condition of low temperature, high strain rate and short residence time between passes, which morphology is mainly strip and round, however, when under the condition of high temperature, low strain rate and long residence time between passes, the content of the strengthening phase decreases and its morphology is mainly round. Besides, the strengthening phase in the alloy is mainly AlFeSi phase, and the strip-like phase has a length of about 6 μm and the round phase has a size of about 2 μm.

Key words: 6063 aluminum alloy, double-pass, hot compression, flow stress, microstructure

中图分类号:

TG166.3

王冠, 田昌龄, 寇琳媛, 卞东伟. 6063铝合金双道次热变形微观组织演变[J]. 金属热处理, 2020, 45(5): 23-28.

Wang Guan, Tian Changling, Kou Linyuan, Bian Dongwei. Microstructure evolution of 6063 aluminum alloy during double-pass hot deformation[J]. Heat Treatment of Metals, 2020, 45(5): 23-28.

参考文献

[1]Chamanfar A, Alamoudi M T, Nanninga N E, et al. Analysis of flow stress and microstructure during hot compression of 6099 aluminum alloy (AA6099)[J]. Materials Science and Engineering: A, 2019, 743: 684-696.
[2]Gang X, Yang Q, Li L. Modeling constitutive relationship of 6013 aluminum alloy during hot plane strain compression based on Kriging method[J]. Transactions of Nonferrous Metals Society of China, 2016, 26(4): 1096-1104.
[3]Sun Y, Cao Z, Wan Z, et al. 3D processing map and hot deformation behavior of 6A02 aluminum alloy[J]. Journal of Alloys and Compounds, 2018, 742: 356-368.
[4]蒋福林, 张辉. 7150铝合金等温多道次热压缩流变应力和静态软化规律[J]. 中国科技论文, 2015, 10(4): 394-398.
Jiang Fulin, Zhang Hui. Flow stress and static softening of 7150 aluminum alloy during isothermal multistage hot compression[J]. China Sciencepaper, 2015, 10(4): 394-398.
[5]闫亮明, 沈健, 李周兵, 等. Al-Zn-Mg-Cu-Zr合金多道次热轧模拟[J]. 中国有色金属学报, 2012(4): 1013-1018.
Yan Liangming, Shen Jian, Li Zhoubing, et al. Multi-pass hot rolling simulation of Al-Zn-Mg-Cu-Zr alloy[J]. The Chinese Journal of Nonferrous Metals, 2012(4): 1013-1018.
[6]Falkinger G, Simon P. Static recovery of an AlMg4.5Mn aluminium alloy during multi-pass hot-rolling[J]. Procedia Engineering, 2017, 207: 31-36.
[7]Yang Shengli, Shen Jian, Li Xiwu, et al. Mechanical behavior and microstructure evolution of Al-Cu-Li alloy during multi-pass hot deformation[J]. Rare Metal Materials and Engineering, 2017, 46(10): 2825-2830.
[8]吴凯, 韩维群, 张铁军, 等. 2A12铝合金的热压缩行为及热加工图[J]. 金属热处理, 2017, 42(4): 12-17.
Wu Kai, Han Weiqun, Zhang Tiejun, et al. Hot compression behavior and processing map of 2A12 aluminum alloy[J]. Heat Treatment of Metals, 2017, 42(4): 12-17.
[9]Jiang F, Zhang H, Ji X, et al. Comparative hot deformation characters of Al-Mn-Mg-RE alloy and Al-Mn-Mg-RE-Ti alloy[J]. Materials Science and Engineering: A, 2014, 595: 10-17.
[10]Doherty R D, Hughes D A, Humphreys F J, et al. Current issues in recrystallization: A review[J]. Materials Science and Engineering: A, 1997, 238(2): 219-274.

[1]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[2]	陈东俊, 李广阳, 刘刚. 时效处理对AlSi9Cu3压铸铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 53-56.
[3]	王庆娟, 田云飞, 高贝特, 史佳敏, 吴欢, 蔡军. 工业纯钛TA1的双道次热压缩变形及软化行为[J]. 金属热处理, 2022, 47(4): 75-79.
[4]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[5]	张骥俊, 邢彦锋, 曹菊勇. 超声振动对CMT电弧增材制造铝合金组织与性能的影响[J]. 金属热处理, 2022, 47(4): 159-164.
[6]	杨春苗, 王珊, 王淑慧, 李延珍, 刘文文. RRA过程中预时效时间对7A85铝合金组织性能的影响[J]. 金属热处理, 2022, 47(3): 44-47.
[7]	陈善勇, 王快社, 乔柯, 王文. 碱热处理对搅拌摩擦加工AZ31镁合金耐腐蚀性能的影响[J]. 金属热处理, 2022, 47(3): 61-66.
[8]	梅金娜, 姜凤阳, 卫娜, 刘浪浪, 思芳, 刘松涛, 王俊勃, 刘江南. 轧制变形对高熵合金微观组织和力学性能的影响[J]. 金属热处理, 2022, 47(3): 67-71.
[9]	叶拓, 唐明, 刘吉兆, 刘伟, 吴远志, 刘巍, 徐文. 固溶温度对7075铝合金板材组织与力学性能的影响[J]. 金属热处理, 2022, 47(3): 119-123.
[10]	叶拓, 何玉兵, 何文鹏, 刘巍, 袁浩登, 吴远志, 刘伟, 刘吉兆. 轧制态6082-T6铝合金的热压缩力学行为及微观组织分析[J]. 金属热处理, 2022, 47(2): 26-30.
[11]	闵旭东, 黄元春, 肖政兵, 刘宇, 任贤魏, 邹倜. 预处理对汽车用Al-Mg-Si合金组织和晶间腐蚀行为的影响[J]. 金属热处理, 2022, 47(2): 78-85.
[12]	刘跃, 韩顺, 厉勇, 王春旭, 严晓红, 李建新. 淬火温度对GE1014超高强度钢组织及性能的影响[J]. 金属热处理, 2022, 47(2): 125-129.
[13]	董瑞, 陈林, 岑耀东, 包喜荣. 不同热处理条件下贝氏体钢的微观组织和疲劳裂纹扩展[J]. 金属热处理, 2022, 47(2): 153-158.
[14]	崔聪, 高飞, 高野, 刘振宇. 21Cr节镍型双相不锈钢高温形变过程的静态软化分析[J]. 金属热处理, 2022, 47(1): 79-87.
[15]	谭皎, 张伯岩, 朱文光, 孙巧艳. 时效温度对Ti-5Al-4Zr-10Mo-3Cr钛合金微观组织及力学性能的影响[J]. 金属热处理, 2022, 47(1): 217-225.

6063铝合金双道次热变形微观组织演变

Microstructure evolution of 6063 aluminum alloy during double-pass hot deformation

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价