淬火温度对高Ti低合金耐磨钢组织及力学性能的影响

doi:10.13251/j.issn.0254-6051.2022.04.019

摘要/Abstract

摘要： 研究了淬火温度对高Ti低合金耐磨钢组织转变、析出相和力学性能的影响,并分析了组织演变和力学性能变化的原因。结果表明:试验钢经不同温度淬火和200 ℃回火后的组织均为高位错密度板条马氏体;析出相尺寸主要为微米-亚微米-纳米三种尺度,微米级析出相呈杆棒状,亚微米以及纳米析出相呈球状,马氏体板条上分布着细小的(Ti, Mo)C析出相。随着淬火温度的升高,试验钢的屈服强度、抗拉强度和维氏硬度均先升高后降低,均在920 ℃时有最大值,分别为1248 MPa、1535 MPa和434 HV,此时伸长率为10.0%。随淬火温度升高,纳米级析出相逐渐回溶,数量减少且尺寸逐渐长大,沿轧制方向被压扁拉长的原奥氏体晶粒尺寸以及马氏体板条块尺寸略有增大,但马氏体板条宽度却无明显长大。大量的弥散分布的5～10 nm的(Ti, Mo)C粒子是促进耐磨钢硬度升高的主要因素。细小的(Ti, Mo)C析出相逐渐长大以及原奥氏体晶粒的增大都不利于耐磨钢硬度的提高。

关键词: 低合金耐磨钢, 淬火温度, 马氏体, 组织, 硬度

Abstract: Effect of quenching temperature on microstructure, precipitated phase and hardness of a high Ti low alloy wear-resistant steel was investigated, and the reasons of the change of microstructure and mechanical properties were analyzed. The results show that the microstructure after quenching and tempering is lath martensite with high dislocation density; the size of precipitated phase is mainly divided into micron-, submicron-, and nano-scales, in which the micron-sized precipitates are rod-shaped, and the sub-micron and nano-sized precipitates are spherical; fine (Ti, Mo)C precipitates are distributed on the martensite laths. As the quenching temperature increases, the yield strength, tensile strength and hardness of the steel first increases and then decreases, and reaching the maximum values of 1248 MPa, 1535 MPa and 434 HV respectively when the quenching temperature is 920 ℃, meanwhile, the elongation reaches 10%. With the increase of the quenching temperature, the nano-scale precipitates gradually dissolves and decreases in content but the size gradually increases; and the sizes of the prior austenite grain and the martensitic lath are slightly increased by flattening along the rolling direction, while the width of martensite laths does not increase significantly. The dispersed (Ti, Mo)C precipitates of 5-10 nm in large quantity are the main factor for promoting the hardness increase of the wear-resistant steel. As the quenching temperature increases, the coarsening of both the fine (Ti, Mo)C phase and the prior austenite grain are not conducive to the improvement of the hardness of the wear-resistant steel.

Key words: low alloy wear-resistant steel, quenching temperature, martensite, microstructure, hardness

中图分类号:

TG142.1

付锡彬, 陈子豪, 张可, 赵时雨, 孙新军, 朱正海, 梁小凯, 雍岐龙. 淬火温度对高Ti低合金耐磨钢组织及力学性能的影响[J]. 金属热处理, 2022, 47(4): 122-127.

Fu Xibin, Chen Zihao, Zhang Ke, Zhao Shiyu, Sun Xinjun, Zhu Zhenghai, Liang Xiaokai, Yong Qilong. Effect of quenching temperature on microstructure and mechanical properties of high Ti low alloy wear-resistant steel[J]. Heat Treatment of Metals, 2022, 47(4): 122-127.

参考文献

[1]邓锋, 胡锋, 吴开明. 低合金高强度耐磨钢的发展与应用[J]. 金属材料与冶金工程, 2016, 44(2): 29-35.
Deng Feng, Hu Feng, Wu Kaiming. Development and application of low-alloy high-strength wear-resistant steels[J]. Metal Materials and Metallurgy Engineering, 2016, 44(2): 29-35.
[2]李文斌, 费静, 曹忠孝, 等. 我国低合金高强度耐磨钢的生产现状及发展方向[J]. 机械工程材料, 2012, 36(2): 6-10.
Li Wenbin, Fei Jing, Cao Zhongxiao, et al. Production status and development direction of wear resistant steel with low alloy and high strength in China[J]. Materials for Mechanical Engineering, 2012, 36(2): 6-10.
[3]麻衡, 周平, 杜军. 热处理工艺对NM500耐磨钢组织和性能的影响[J]. 金属热处理, 2015, 40(8): 159-163.
Ma Heng, Zhou Ping, Du Jun. Effect of heat treatment on mechanical properties of NM500 steel[J]. Heat Treatment of Metals, 2015, 40(8): 159-163.
[4]邓想涛, 王昭东, 张逖, 等. HB450低合金超高强耐磨钢回火过程中的组织性能演变[J]. 钢铁, 2011, 46(5): 60-63.
Deng Xiangtao, Wang Zhaodong, Zhang Ti, et al. Microstructure and properties evolution of HB450 ultra-high strength low-alloy abrasion resistant steel during tempering[J]. Iron and Steel, 2011, 46(5): 60-63.
[5]彭军, 牛亮, 郭永, 等. V、Ti对NM400钢耐磨性能的影响[J]. 金属热处理, 2016, 41(2): 19-23.
Pneg Jun, Niu Liang, Guo Yong, et al. Effect of V and Ti on wear resistance of NM400 steel[J]. Heat Treatment of Metals, 2016, 41(2): 19-23.
[6]杨瑞林, 李力军, 李玉成. 新型低合金高强韧性耐磨钢的研究[J]. 钢铁, 1999, 34(7): 43-47.
Yang Ruilin, Li Lijun, Li Yucheng. Study on a new low alloy high strength and high toughness and wear resistance steel[J]. Iron and Steel, 1999, 34(7): 43-47.
[7]王存宇, 时捷, 刘苏, 等. 淬火-配分-回火工艺处理钢的三体冲击磨损性能研究[J]. 材料研究学报, 2009, 23(3): 305-310.
Wang Cunyu, Shi Jie, Liu Su, et al. Study on three-body impact-abrasion of steel treated by quenching-partitioning-tempering process[J]. Chinese Journal of Materials Research, 2009, 23(3): 305-310.
[8]Xu L J, Xing J D, Wei S Z, et al. Study on relative wear resistance and wear stability of high-speed steel with high vanadium content[J]. Wear, 2007, 262: 253-261.
[9]梁高飞, 许振明, 李建国, 等. 抗磨钢的最新进展[J]. 特殊钢, 2002(4): 1-7.
Liang Gaofei, Xu Zenming, Li Jianguo, et al. Recent development of wear resistant steel[J]. Special Steel, 2002(4): 1-7.
[10]梁小凯, 孙新军, 雍岐龙, 等. TiC颗粒强化型马氏体耐磨钢的性能研究[J]. 钢铁钒钛, 2017, 38(1): 48-53.
Liang Xiaokai, Sun Xinjun, Yong Qilong, et al. Study on performance of TiC particle reinforced martensite wear-resistant steel[J]. Iron Steel Vanadium Titanium, 2017, 38(1): 48-53.
[11]许帅, 孙新军, 梁小凯, 等. 热轧变形量对高钛耐磨钢组织与力学性能的影响[J]. 金属学报, 2020, 56(12): 1581-1591.
Xu Suai, Sun Xinjun, Liang Xiaokai, et al. Effect of hot rolling deformation on microstructure and mechanical properties of a high-Ti wear-resistant steel[J]. Acta Metallurgica Sinica, 2020, 56(12): 1581-1591.
[12]王川, 李新宇, 于涛. 离线淬火工艺对NM400耐磨钢组织与性能的影响[J]. 山东冶金, 2020, 42(4): 43-45.
Wang Chuan, Li Xinyu, Yu Tao. Effect of off-line quenching process on microstructure and properties of NM400 wear-resistant steel[J]. Shandong Metallurgy, 2020, 42(4): 43-45.
[13]徐慧, 李天生. 回火温度对Nb微合金化NM500钢组织和性能的影响[J]. 金属热处理, 2020, 45(9): 116-120.
Xu Hui, Li Tiansheng. Effect of tempering temperature on microstructure and properties of Nb microalloyed NM500 steel[J]. Heat Treatment of Metals, 2020, 45(9): 116-120.
[14]邓杰, 孙新军, 张涛, 等. 冷却速率对中锰马氏体耐磨钢微观结构及硬度的影响[J]. 材料导报, 2020, 34(10): 10126-10131.
Deng Jie, Sun Xinjun, Zhang Tao, et al. Effect of cooling rate on microstructure and hardness of medium manganese martensitic wear-resistant steel[J]. Materials Review, 2020, 34(10): 10126-10131.
[15]Du G, Liu F, Li J B. Evolution of microstructures and divorced eutectic TiC formed during solidification of the wear-resistant steel[J]. Materials Letters, 2020, 265: 127406.
[16]Haiko O, Valtonen k, Kaijalainen A, et al. Effect of tempering on the impact-abrasive and abrasive wear resistance of ultra-high strength steels[J]. Wear, 2019, 440-441: 203098.
[17]Dong C, Wu H B, Wang X T. Effect of cooling rate on microstructure, hardness, and residual stress of 0.28C-0.22Ti wear-resistant steel[J]. Journal of Iron and Steel Research International, 2019, 26(8): 866-874.
[18]Xue H, Peng W J, Yu L, et al. Effect of hardenability on microstructure and property of low alloy abrasion-resistant steel[J]. Materials Science and Engineering A, 2020, 793: 139901.
[19]Rendón J, Olsson M. Abrasive wear resistance of some commercial abrasion resistant steels evaluated by laboratory test methods[J]. Wear, 2009, 267(11): 2055-2061.
[20]孙新军, 刘罗锦, 梁小凯, 等. 高钛耐磨钢中TiC析出行为及其对耐磨粒磨损性能的影响[J]. 金属学报, 2020, 56(4): 661-672.
Sun Xinjun, Liu Luojin, Liang Xiaokai, et al. TiC precipitation behavior and its effect on abrasion resistance of high titanium wear-resistant steel[J]. Acta Metallurgica Sinica, 2020, 56(4): 661-672.
[21]王明娣, 刘东权, 武会宾. 淬火工艺对低合金耐磨钢组织与力学性能的影响[J]. 金属热处理, 2018, 43(8): 156-161.
Wang Mingdi, Liu Dongquan, Wu Huibin. Influence of quenching on microstructure and mechanical properties of low alloy wear-resistant steel[J]. Heat Treatment of Metals, 2018, 43(8): 156-161.
[22]邓想涛. 低合金耐磨钢组织性能控制及磨损机理研究[D]. 沈阳: 东北大学, 2014.
Deng Xiangtao. Microstructure and mechanical property control and wear mechanism study for low-alloy abrasion resistant steel[D]. Shenyang: Northeastern University, 2014.
[23]曹艺, 王昭东, 邓想涛, 等. 低合金耐磨钢回火过程中的碳化物析出[J]. 材料热处理学报, 2018, 39(4): 113-120.
Cao Yi, Wang Zhaodong, Deng Xiangtao, et al. Carbide precipitation during tempering of low alloy wear resistant steel[J]. Transactions of Materials and Heat Treatment, 2018, 39(4): 113-120.
[24]张可, 孙新军, 雍岐龙, 等. 回火时间对高Ti微合金化淬火马氏体钢组织及力学性能的影响[J]. 金属学报, 2015, 51(5): 553-560.
Zhang Ke, Sun Xinjun, Yong Qilong, et al. Effect of tempering time on microstructure and mechanical properties of high Ti microalloyed quenched martensitic steel[J]. Acta Metallurgica Sinica, 2015, 51(5): 553-560.
[25]Funakawa Y, Shiozaki T, Tomita K, et al. Development of high strength hot-rolled sheet steel consisting of ferrite and nanometer-sized carbides[J]. ISIJ International, 2004, 44(11): 1945-1951.
[26]Kostryzhev A G, Killmore C R, Yu D, et al. Martensitic wear resistant steels alloyed with titanium[J]. Wear, 2019, 446-447: 203203.