2507超级双相不锈钢中σ相的析出行为

doi:10.13251/j.issn.0254-6051.2022.04.017

金属热处理 ›› 2022, Vol. 47 ›› Issue (4): 108-115.DOI: 10.13251/j.issn.0254-6051.2022.04.017

2507超级双相不锈钢中σ相的析出行为

白青青^1,2, 张志宏^1,2, 郑淮北^1,2, 王英虎^1,2

1.成都先进金属材料产业技术研究院有限公司, 四川成都 610303;
2.海洋装备用金属材料及其应用国家重点实验室, 辽宁鞍山 114009

收稿日期:2021-10-19 修回日期:2021-12-28 出版日期:2022-04-25 发布日期:2022-05-19
作者简介:白青青(1986—),女,高级工程师,主要研究方向为不锈钢的开发,E-mail:89447535@qq.com

Precipitation behavior of σ phase in 2507 super duplex stainless steel

Bai Qingqing^1,2, Zhang Zhihong^1,2, Zheng Huaibei^1,2, Wang Yinghu^1,2

1. Chengdu Advanced Metal Materials Industry Technology Research Institute Co., Ltd., Chengdu Sichuan 610303, China;
2. State Key Laboratory of Metal Material for Marine Equipment and Application,Anshan Liaoning 114009, China

Received:2021-10-19 Revised:2021-12-28 Online:2022-04-25 Published:2022-05-19

摘要/Abstract

摘要： 利用扫描电镜、透射电镜、X射线衍射仪、电化学工作站等试验及手段,研究了2507(S32750)超级双相不锈钢经700～1000 ℃时效不同时间后σ相的析出规律及其对冲击性能和腐蚀性能的影响规律。结果表明:σ相析出速度很快,析出量随时效时间的延长先增加后逐步减少,在850~900 ℃时效后σ相的析出量最大。σ相的析出严重降低材料的冲击及腐蚀性能,建议时效温度不低于950 ℃。

关键词: 2507超级双相不锈钢, σ相, 冲击性能, 腐蚀性能

Abstract: Precipitation of σ phase in 2507 (S32750) super duplex stainless steel aged at 700-1000 ℃ for different time and its influence to impact property and corrosion resistance were studied by means of scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and electrochemical workstation. The results show that the precipitation rate of σ phase is very fast in 2507 super duplex stainless steel, and the precipitation amount increases first and then decreases gradually with the extension of aging time. Precipitation of σ phase is the fastest after aging at 850-900 ℃, which leads to the serious reduction of impact toughness and corrosion resistance of the steel. It is recommended that the aging temperature should not be lower than 950 ℃.

Key words: 2507 super duplex stainless steel, σ phase, impact property, corrosion resistance

中图分类号:

TG142.71

白青青, 张志宏, 郑淮北, 王英虎. 2507超级双相不锈钢中σ相的析出行为[J]. 金属热处理, 2022, 47(4): 108-115.

Bai Qingqing, Zhang Zhihong, Zheng Huaibei, Wang Yinghu. Precipitation behavior of σ phase in 2507 super duplex stainless steel[J]. Heat Treatment of Metals, 2022, 47(4): 108-115.

参考文献

[1]吴玖. 双相不锈钢[M]. 北京: 冶金工业出版社, 2000: 1-2.
[2]陈万里. 2707双相不锈钢中σ相析出行为及其对性能的影响[D]. 太原: 太原理工大学, 2018.
[3]Nilsson J O. Super duplex stainless steels[J]. Materials Science and Technology, 1992, 8(8): 685-700.
[4]吴忠忠, 宋志刚, 郑文杰, 等. 固溶温度对超级双相不锈钢00Cr25Ni7Mo4N组织和性能的影响[J]. 特殊钢, 2006, 27(4): 11-13.
Wu Zhongzhong, Song Zhigang, Zheng Weijie, et al. Influence of solution temperature on structure and properties of super duplex stainless steel 00Cr25Ni7Mo4N[J]. Special Steel, 2006, 27(4): 11-13.
[5]刘雄, 丁秀平, 何燕霖, 等. 2205双相不锈钢高温下σ相析出的原位观察[J]. 上海金属, 2010(2): 8-11.
Liu Xiong, Ding Xiuping, He Yanlin, et al. In situ observations of σ phase precipitation at high temperature in 2205 duplex stainless steel[J]. Shanghai Metal, 2010(2): 8-11
[6]陈嘉砚, 杨卓越, 杨武, 等. 双相不锈钢中σ相的形成特点及其对性能的影响[J]. 钢铁研究学报, 2006, 18(8): 1-4.
Chen Jiayan, Yang Zhuoyue, Yang Wu, et al. Characteristic of phase σ precipitation and its effects on behavior in duplex stainless steel[J]. Journal of Iron and Steel Research, 2006, 18(8): 1-4.
[7]王东. 254SMo和2507不锈钢中σ析出相研究[J]. 材料热处理学报, 2016, 37(5): 103-109.
Wang Dong. Precipitation of σ-phase in 254SMo and 2507 super stainless steels[J]. Transactions of Materials and Heat Treatment, 2016, 37(5): 103-109.
[8]宾远红, 李培芬, 李志铮, 等. 不同固溶温度对双相不锈钢σ相析出及冲击韧性的影响[J]. 材料热处理学报, 2013(8): 136-141.
Bin Yuanhong, Li Peifen, Li Zhizheng, et al. Precipitation of σ-phase and its effect on impact toughness of a duplex stainless steel solution-treated at different temperatures[J]. Transactions of Material and Heat Treatment, 2013 (8): 136-141.
[9]Zhang Zhiqiang, Jing Hongyang, Xu Lianyong, et al. Influence of microstructure and elemental partitioning on pitting corrosion resistance of duplex stainless steel welding joints[J]. Applied Surface Science, 2017, 394(1): 297-314.
[10]Magnabosco R, Falleiros N A. Pit morphology and its relation to microstructure of 850 ℃ aged duplex stainless steel[J]. Corrosion, 2005, 61(2): 130-136.

[1]	陈思君, 陈送义, 陈庚, 袁丁玲, 陈康华. Mg含量对2A14铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 86-92.
[2]	陈刚, 罗小兵, 柴锋, 杨才福, 张正延, 杨丽. 轧制加热温度对高强度低合金钢组织及冲击性能的影响[J]. 金属热处理, 2022, 47(4): 116-121.
[3]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[4]	陈志杰, 崔彤. Mg-4.0Zn-2.0Sr-0.4Ca合金复合涂层的耐腐蚀性能[J]. 金属热处理, 2022, 47(4): 213-218.
[5]	赵子硕, 武美萍, 缪小进, 崔宸, 龚玉玲. 激光功率对FeCoNiCrMo高熵合金/氧化石墨烯复合涂层组织及耐腐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 251-257.
[6]	罗迪强, 余音宏, 张真铭, 冯小明, 刘敏, 赖朝彬. 钇基稀土对高强船板钢夹杂物及低温冲击性能的影响[J]. 金属热处理, 2022, 47(3): 142-146.
[7]	李阔, 孙明月, 徐斌, 李殿中. 稀土H13模具钢横向冲击性能影响因素分析[J]. 金属热处理, 2022, 47(3): 181-185.
[8]	吴迎飞, 孙中华, 王育飞, 王程明, 张雲飞, 彭会芬. 均匀化退火处理对因瓦合金铸锭组织及性能的影响[J]. 金属热处理, 2022, 47(2): 130-136.
[9]	李德君, 高华, 孔祥路, 杨小平, 李塔, 董照远, 张小佳. 20钢等径三通失效分析[J]. 金属热处理, 2022, 47(2): 262-266.
[10]	何婵, 邹德宁, 赵洁, 陈兴润, 钱张信. 2507超级双相不锈钢的流变应力本构关系及热加工图[J]. 金属热处理, 2022, 47(1): 94-99.
[11]	韩晓虎, 田林海, 王振霞, 黄天阳, 郑家圣, 王居庄, 唐宾, 吴玉程. 钨表面WTaTiVCr高熵合金层的组织与性能[J]. 金属热处理, 2022, 47(1): 185-191.
[12]	朱林, 程向龙, 邹喜洋. 26CrMo4钢的热处理工艺[J]. 金属热处理, 2022, 47(1): 271-275.
[13]	丁轩, 甘玉荣, 蒋爱娟, 李辉, 杨明球. 时效处理对7A55铝合金微观组织和性能的影响[J]. 金属热处理, 2021, 46(9): 120-123.
[14]	于洪军, 宋传颂馨, 程福超, 高志喆, 陈小艳, 王永金, 张应超. 不同热处理条件下亚共晶高铬铸铁的组织和性能[J]. 金属热处理, 2021, 46(8): 56-60.
[15]	王玲奇, 何燕霖, 潘乐. 回火温度对高氮不锈轴承钢显微组织与力学性能的影响[J]. 金属热处理, 2021, 46(6): 8-13.

2507超级双相不锈钢中σ相的析出行为

Precipitation behavior of σ phase in 2507 super duplex stainless steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价