含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响

doi:10.13251/j.issn.0254-6051.2022.04.004

金属热处理 ›› 2022, Vol. 47 ›› Issue (4): 24-29.DOI: 10.13251/j.issn.0254-6051.2022.04.004

含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响

祁晓亮¹, 李岩¹, 定巍², 赵增武¹

1.内蒙古科技大学内蒙自治区白云鄂博矿多金属资源综合利用重点实验室, 内蒙古包头 014010;
2.内蒙古科技大学材料与冶金学院, 内蒙古包头 014010

收稿日期:2021-11-29 修回日期:2022-01-14 出版日期:2022-04-25 发布日期:2022-05-19
通讯作者: 李岩,教授,博士,E-mail: kenshin110@163.com
作者简介:祁晓亮(1995—),男,硕士研究生,主要研究方向为先进高强度钢的组织调控,E-mail: 865927119@qq.com。
基金资助:
内蒙古自然科学基金(2019MS05014,2020LH05026)

Effect of original microstructure of medium manganese TRIP steel containing Al on microstructure and mechanical properties after intercritical annealing

Qi Xiaoliang¹, Li Yan¹, Ding Wei², Zhao Zengwu¹

1. Key Laboratory of Integrated Exploitation of Bayan Obo Multi-Metal Resources, Inner Mongolia University of Science and Technology, Baotou Inner Mongolia 014010, China;
2. School of Materials and Metallurgy Engineering, Inner Mongolia University of Science and Technology, Baotou Inner Mongolia 014010, China

Received:2021-11-29 Revised:2022-01-14 Online:2022-04-25 Published:2022-05-19

摘要/Abstract

摘要： 利用Factsage软件、SEM、XRD等研究了不同原始组织的0.2C-5.0Mn-0.5Si-1.0Al中锰TRIP钢经临界区退火处理后的显微组织与力学性能。结果表明,经热力学计算、设计的不同预处理工艺处理后试验钢的组织分别为:铁素体+块状残留奥氏体(700 ℃预处理10 min)、铁素体+马氏体+少量残留奥氏体 (800 ℃预处理5 min) 和马氏体+少量碳化物 (900 ℃预处理5 min)。不同预处理工艺处理后试样能获得不同形貌的残留奥氏体,700 ℃预处理+临界退火试样得到块状残留奥氏体,其他两种工艺下为膜状残留奥氏体。800 ℃预处理+临界退火试样拥有最佳力学性能,屈服强度为840 MPa,抗拉强度为1121.5 MPa,伸长率为33.25%,强塑积达到37.29 GPa·%。残留奥氏体形貌对中锰钢的加工硬化性能有显著影响,700 ℃预处理+临界退火试样的块状残留奥氏体稳定性较差,表现出高的加工硬化率,但持续区间较短;而800 ℃预处理+临界退火试样的膜状残留奥氏体稳定性更好,试样呈现较高的加工硬化率且持续区间较长。

关键词: 含Al中锰TRIP钢, 原始组织, 力学性能, 残留奥氏体

Abstract: Microstructure and mechanical properties of 0.2C-5.0Mn-0.5Si-1.0Al TRIP steel with different original microstructure after intercritical annealing were studied by Factsage software, SEM, XRD, etc. The results show that the microstructure of the steel treated by different pretreatment processes are as follows: ferrite+blocky type retained austenite (pretreatment at 700 ℃ for 10 min), ferrite+martensite+small amount of retained austenite (pretreatment at 800 ℃ for 5 min), and martensite+small amount of carbides (pretreatment at 900 ℃ for 5 min). The residual austenite with different morphologies can be obtained by different pretreatment processes. By pretreatment at 700 ℃ and intercritical annealing, blocky-type retained austenite is obtained, and the film-type one can be obtained by the other processes. The specimen pretreated at 800 ℃+intercritical annealing has the best mechanical properties with the yield strength of 840 MPa, the tensile strength of 1121.5 MPa, the elongation of 33.25 %, and the product of strength and plasticity of 37.29 GPa·%. The morphology of retained austenite has a significant impact on the work hardening performance. The blocky-type retained austenite pretreated at 700 ℃ and intercritical annealing has poor stability, showing high work hardening rate, but the continuous interval is short. However, the stability of film retained austenite pretreated at 800 ℃ and intercritical annealing is better, showing higher work hardening rate and longer duration.

Key words: medium manganese TRIP steel containing Al, original microstructure, mechanical properties, retained austenite

中图分类号:

TG142.1

祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.

Qi Xiaoliang, Li Yan, Ding Wei, Zhao Zengwu. Effect of original microstructure of medium manganese TRIP steel containing Al on microstructure and mechanical properties after intercritical annealing[J]. Heat Treatment of Metals, 2022, 47(4): 24-29.

参考文献

[1]Lee Y K, Han J. Current opinion in medium manganese steel[J]. Materials Science and Technology, 2015, 31(7): 843-856.
[2]王润勋, 王宝峰, 李岩, 等. 0.2C-5Mn-1.5Al中锰TRIP钢的显微组织及力学性能[J]. 金属热处理, 2020, 45(4): 63-68.
Wang Runxun, Wang Baofeng, Li Yan, et al. Microstructure and mechanical properties of 0.2C-5Mn-1.5Al medium manganese TRIP steel[J]. Heat Treatment of Metals, 2020, 45(4): 63-68.
[3]Deng Z, Zhu M, Zhou Y, et al. Attachment of alumina on the wall of submerged entry nozzle during continuous casting of Al-killed steel[J]. Metallurgical and Materials Transactions B, 2016, 47(3): 2015-2025.
[4]徐海峰. 0.2C-5Mn钢中奥氏体稳定性调控及力学性能的研究[D]. 武汉: 华中科技大学, 2012.
[5]田超. Fe-0.2C-5Mn-1.5Al中锰钢的奥氏体稳定性调控及组织性能研究[D]. 沈阳: 东北大学, 2014.
[6]Liu C, Peng Q, Xue Z, et al. Effect of different heat treatment processes on microstructure evolution and tensile properties of hot-rolled medium-Mn steel[J]. Transactions of the Indian Institute of Metals, 2020, 73(9): 2221-2229.
[7]邵成伟, 王俊涛, 赵晓丽, 等. 两相区退火处理含铝中锰钢的组织和力学性能[J]. 钢铁, 2020, 55(5): 87-93.
Shao Chengwei, Wang Juntao, Zhao Xiaoli, et al. Microstructure and mechanical properties of intercritically annealed Al-contain medium Mn steel[J]. Iron and Steel, 2020, 55(5): 87-93.
[8]Takanobu Adachi, Atsushi Ito, Hiroki Adachi, et al. Effect of prior structure to intercritical annealing on rapid formation of ultrafine ferrite+austenite structure and mechanical properties in 0.1%C-2%Si-5%Mn steels[J]. ISIJ International, 2020, 60(4): 764-773.
[9]Ding Ran, Dai Zongbiao, Huang Mingxin, et al. Effect of pre-existed austenite on austenite reversion and mechanical behavior of an Fe-0.2C-8Mn-2Al medium Mn steel[J]. Acta Materialia, 2018, 147: 59-69.
[10]Cullity B D, Stock S R. Elements of X-ray Diffraction[M]. 3rd edition. Upper Saddle River: Prentice-Hall, 2001.
[11]Moor E De, Matlock D K, Speer J G, et al. Austenite stabilization through manganese enrichment[J]. Scripta Materialia, 2011, 64(2): 185-188.
[12]Wei Ding, Runxun Wang, Yan Li, et al. High elongation of medium-manganese steel containing 1.0wt.% Al after a short intercritical annealing time[J]. Journal of Materials Research and Technology, 2020, 9(4): 7262-7272.
[13]Chiang J, Lawrence B, Boyd J D, et al. Effect of microstructure on retained austenite stability and work hardening of TRIP steels[J]. Materials Science and Engineering A, 2011, 528(13/14): 4516-4521.
[14]Shao Chengwei, Hui Weijun, Zhang Yongjian, et al. Microstructure and mechanical properties of hot-rolled medium-Mn steel containing 3% aluminum[J]. Materials Science and Engineering A, 2017, 682: 45-53.
[15]定巍, 龚志华, 唐荻, 等. 低硅含铝TRIP钢残余奥氏体变形过程中稳定性研究[J]. 材料工程, 2013(12): 68-73.
Ding Wei, Gong Zhihua, Tang Di, et al. Stability of retained austenite of low Si containing Al TRIP steel during deformation[J]. Journal of Materials Engineering, 2013(12): 68-73.
[16]Wang X G, Wang L, Huang M X. In-situ evaluation of Lüders band associated with martensitic transformation in a medium Mn transformation-induced plasticity steel[J]. Materials Science and Engineering A, 2016, 674: 59-63.
[17]Zhang Y, Ding H. Ultrafine also can be ductile: On the essence of Lüders band elongation in ultrafine-grained medium manganese steel[J]. Materials Science and Engineering A, 2018, 733: 220-223.
[18]Wang H, Zhang Y, Yuan G, et al. Significance of cold rolling reduction on Lüders band formation and mechanical behavior in cold-rolled intercritically annealed medium-Mn steel[J]. Materials Science and Engineering A, 2018, 737: 176-181.
[19]张岩, 万德成, 王亚婷, 等. 一步QP处理低碳中锰钢的微观组织和力学性能[J]. 热加工工艺, 2019, 48(6): 219-222.
Zhang Yan, Wan Decheng, Wang Yating, et al. Microstructure and mechanical properties of low carbon medium Mn steel treated by one-step quenching and paititioning process[J]. Hot Working Technology, 2019, 48(6): 219-222.
[20]Zambrano O A. A general perspective of Fe-Mn-Al-C steels[J]. Journal of Materials Science, 2018, 53(20): 14003-14062.
[21]Singon Kang, John G Speer, Daniel Krizan, et al. Prediction of tensile properties of intercritically annealed Al-containing 0.19C-4.5Mn (wt%) TRIP steels[J]. Materials and Design, 2016, 97: 138-146.
[22]Sun B, Fazeli F, Scott C, et al. The influence of silicon additions on the deformation behavior of austenite-ferrite duplex medium manganese steels[J]. Acta Materialia, 2018, 145: 249-262.
[23]Hu B, Luo H W. A strong and ductile 7Mn steel manufactured by warm rolling and exhibiting both transformation and twinning induced plasticity[J]. Journal of Alloys and Compounds, 2017, 725: 684-693.
[24]Shi J, Sun X J, Wang M Q, et al. Enhanced work-hardening behavior and mechanical properties in ultrafine-grained steels with large fractioned metastable austenite[J]. Scripta Materialia, 2010, 63: 815-818.

含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响

Effect of original microstructure of medium manganese TRIP steel containing Al on microstructure and mechanical properties after intercritical annealing

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[2]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[3]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[4]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[5]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[6]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.
[7]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[8]	张骥俊, 邢彦锋, 曹菊勇. 超声振动对CMT电弧增材制造铝合金组织与性能的影响[J]. 金属热处理, 2022, 47(4): 159-164.
[9]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[10]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[11]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.
[12]	陈强, 陈林芳, 杨明华. 18CrNiMo7-6钢的可控气氛高温渗碳工艺[J]. 金属热处理, 2022, 47(4): 231-239.
[13]	刘乃瑜, 曹磊, 郑少梅. 不同沉积温度下CrCN涂层的力学性能[J]. 金属热处理, 2022, 47(4): 240-244.
[14]	陈连生, 房宁, 曹仲乾, 杨子旋, 李红斌, 潘红波, 田亚强. 压下率对两相区温轧淬火配分中锰钢组织性能的影响[J]. 金属热处理, 2022, 47(3): 28-33.
[15]	刘志桥, 冯庆晓, 李化龙, 李腾飞. 退火工艺对低碳贝氏体钢组织与力学性能的影响[J]. 金属热处理, 2022, 47(3): 53-56.