不同热处理条件下亚共晶高铬铸铁的组织和性能

doi:10.13251/j.issn.0254-6051.2021.08.011

金属热处理 ›› 2021, Vol. 46 ›› Issue (8): 56-60.DOI: 10.13251/j.issn.0254-6051.2021.08.011

不同热处理条件下亚共晶高铬铸铁的组织和性能

于洪军¹, 宋传颂馨², 程福超¹, 高志喆¹, 陈小艳¹, 王永金², 张应超²

1.鞍山钢铁集团有限公司大孤山球团厂, 辽宁鞍山 114004;
2.北京科技大学材料科学与工程学院, 北京 100083

收稿日期:2021-03-24 出版日期:2021-08-25 发布日期:2021-12-09
通讯作者: 王永金,讲师,博士,E-mail:wangyongjin@ustb.edu.cn
作者简介:于洪军(1966—),男,高级工程师,主要研究方向为矿山设备与工艺,E-mail:17801063363@163.com。

Microstructure and properties of a hypoeutectic high-Cr cast iron under different heat treatment conditions

Yu Hongjun¹, Song Chuansongxin², Cheng Fuchao¹, Gao Zhizhe¹, Chen Xiaoyan¹, Wang Yongjin², Zhang Yingchao²

1. Dagushan Pelleting Plant, Anshan Iron & Steel Group Co., Ltd., Anshan Liaoning 114004, China;
2. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China

Received:2021-03-24 Online:2021-08-25 Published:2021-12-09

摘要/Abstract

摘要： 利用光学显微镜、扫描电镜、X射线能谱仪以及力学性能测试等方法,对不同热处理条件下的亚共晶高铬铸铁进行微观结构表征以及性能测试,研究不同热处理条件对亚共晶高铬铸铁组织及性能的影响。亚共晶高铬铸铁的硬度和冲击吸收能量随淬火温度的升高和保温时间的延长先升高后下降,淬火回火后的最大硬度可达到58 HRC,最大冲击吸收能量可达到15 J。

关键词: 亚共晶高铬铸铁, 热处理, 显微组织, 硬度, 冲击性能

Abstract: Effects of different heat treatment condition on microstructure and properties of a hypoeutectic high chromium cast iron were studied by means of optical microscope, scanning electron microscope, X-ray energy dispersive spectrometer and mechanical properties test. The results show that the hardness and impact absorbed energy of the tested cast iron firstly increases and then decreases with the increase of quenching temperature and time. The maximum hardness and impact absorbed energy of the tested cast iron can reach 58 HRC and 15 J after quenching plus tempering, respectively.

Key words: hypoeutectic high chromium cast iron, heat treatment, microstructure, hardness, impact property

中图分类号:

TG161

于洪军, 宋传颂馨, 程福超, 高志喆, 陈小艳, 王永金, 张应超. 不同热处理条件下亚共晶高铬铸铁的组织和性能[J]. 金属热处理, 2021, 46(8): 56-60.

Yu Hongjun, Song Chuansongxin, Cheng Fuchao, Gao Zhizhe, Chen Xiaoyan, Wang Yongjin, Zhang Yingchao. Microstructure and properties of a hypoeutectic high-Cr cast iron under different heat treatment conditions[J]. Heat Treatment of Metals, 2021, 46(8): 56-60.

参考文献

[1]杨帆, 张志浩, 索忠源, 等. 退火工艺对高碳高铬铸铁组织及硬度的影响[J]. 金属热处理, 2018, 43(10): 104-106.
Yang Fan, Zhang Zhihao, Suo Zhongyuan, et al. Influence of annealing process on microstructure and hardness of high carbon high chromium cast iron[J]. Heat Treatment of Metals, 2018, 43(10): 104-106.
[2]刘秀华. 热处理对高铬铸铁硬度与冲击韧性的影响[J]. 热加工工艺, 2020, 49(12): 157-159.
Liu Xiuhua. Effects of Heat treatment on hardness and impact toughness of high chromium cast iron[J]. Hot Working Technology, 2020, 49(12): 157-159.
[3]索忠源, 付立铭, 张志浩, 等. 热处理对Cr20高铬铸铁组织及性能的影响[J]. 金属热处理, 2018, 43(7): 184-187.
Suo Zhongyuan, Fu Liming, Zhang Zhihao, et al. Influence of heat treatment on microstructure and properties of Cr20 high chromium cast iron[J]. Heat Treatment of Metals, 2018, 43(7): 184-187.
[4]宋建勇. 烧结亚共晶高铬铸铁的制备以及组织与性能研究[D]. 长沙: 湖南大学, 2016.
Song Jianyong. Study on the fabrication and the microstructure-property of sintered hypoeutectic high chromium cast iron[D]. Changsha: Hunan University, 2016.
[5]董阳阳, 欧阳海青, 蒋业华, 等. 热处理对含钨过共晶高铬铸铁组织与性能影响[J]. 金属热处理, 2016, 41(2): 150-155.
Dong Yangyang, Ouyang Haiqing, Jiang Yehua, et al. Effect of heat treatment on microstructure and properties of hypereutectic high chromium cast iron with tungsten addition[J]. Heat Treatment of Metals, 2016, 41(2): 150-155.
[6]梁秀娟, 嵇海旭. 淬火工艺对Cr26高铬耐磨铸铁组织与硬度的影响[J]. 金属热处理, 2020, 45(4): 141-143.
Liang Xiujuan, Ji Haixu. Effect of quenching process on microstructure and hardness of Cr26 high chromium wear resistant cast iron[J]. Heat Treatment of Metals, 2020, 45(4): 141-143.
[7]肖平安, 肖璐琼, 顾景洪, 等. 15Cr系亚共晶高铬铸铁的烧结制备与性能研究[J]. 湖南大学学报(自然科学版), 2019, 46(12): 58-64.
Xiao Ping'an, Xiao Luqiong, Gu Jinghong, et al. Study on sintering preparation and properties of 15Cr hypoeutectic high-chromium cast iron[J]. Journal of Hunan University(Natural Sciences), 2019, 46(12): 58-64.

[1]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[2]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[3]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[4]	陈思君, 陈送义, 陈庚, 袁丁玲, 陈康华. Mg含量对2A14铝合金组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 86-92.
[5]	白青青, 张志宏, 郑淮北, 王英虎. 2507超级双相不锈钢中σ相的析出行为[J]. 金属热处理, 2022, 47(4): 108-115.
[6]	陈刚, 罗小兵, 柴锋, 杨才福, 张正延, 杨丽. 轧制加热温度对高强度低合金钢组织及冲击性能的影响[J]. 金属热处理, 2022, 47(4): 116-121.
[7]	付锡彬, 陈子豪, 张可, 赵时雨, 孙新军, 朱正海, 梁小凯, 雍岐龙. 淬火温度对高Ti低合金耐磨钢组织及力学性能的影响[J]. 金属热处理, 2022, 47(4): 122-127.
[8]	李立, 曾艳, 吴晓春. 4Cr5Mo2VCo钢的热处理工艺优化[J]. 金属热处理, 2022, 47(4): 133-140.
[9]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[10]	孙凯, 陈研, 杨绍斌. 时效温度对激光选区熔化TC21钛合金微观组织及硬度的影响[J]. 金属热处理, 2022, 47(4): 155-158.
[11]	章军, 赵四新. 冷锻齿轮用16MnCrS5钢的球化退火工艺[J]. 金属热处理, 2022, 47(4): 185-188.
[12]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[13]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[14]	王方军, 王东哲, 万红, 时瑶, 沈涛. 热处理和冷变形量对定膨胀合金4J32C线膨胀系数的影响[J]. 金属热处理, 2022, 47(4): 199-203.
[15]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.

不同热处理条件下亚共晶高铬铸铁的组织和性能

Microstructure and properties of a hypoeutectic high-Cr cast iron under different heat treatment conditions

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价