退火工艺对采暖系统用耐沟状腐蚀钢带性能的影响

doi:10.13251/j.issn.0254-6051.2020.08.024

金属热处理 ›› 2020, Vol. 45 ›› Issue (8): 124-130.DOI: 10.13251/j.issn.0254-6051.2020.08.024

退火工艺对采暖系统用耐沟状腐蚀钢带性能的影响

卢军辉¹, 吴战芳¹, 王晓春², 仇圣桃¹, 干勇¹

1.钢铁研究总院连铸技术国家工程研究中心, 北京 100081;
2.通化钢铁股份公司技术中心, 吉林通化 134003

收稿日期:2020-01-26 出版日期:2020-08-25 发布日期:2020-09-07
通讯作者: 仇圣桃,教授,博士,E-mail: qiust@vip.sina.com
作者简介:卢军辉(1980—),男,博士研究生,主要研究方向为钢铁生产过程工艺设计、优化、新品种开发,E-mail: junhui0929@163.com

Effect of annealing process on properties of grooving-corrosion resistant steel strip for heating system

Lu Junhui¹, Wu Zhanfang¹, Wang Xiaochun², Qiu Shengtao¹, Gan Yong¹

1. National Engineering Research Center of Continuous Casting Technology, Central Iron and Steel Research Institute, Beijing 100081, China;
2. Technical Center, Tong-hua Iron and Steel Company, Tonghua Jilin 134003, China

Received:2020-01-26 Online:2020-08-25 Published:2020-09-07

摘要/Abstract

摘要： 通过对耐沟状腐蚀现象的研究,结合生产设备能力,设计了6种成分钢带和6种退火工艺。借助光学显微镜、扫描电镜、拉伸试验、中性盐雾试验等手段,研究了采暖系统用耐沟状腐蚀钢带生产过程中冷轧退火工艺对其性能的影响。结果发现:低于Ac₁温度(650、700 ℃)的退火不可能改变原来冷轧铁素体晶界的遗传结构,冷轧α相的再结晶长大不充分,碳化物的聚合和长大过程也不充分;当退火温度达到Ac₁左右(750 ℃),由于碳元素的固溶加剧,导致α相再结晶和析出物的聚合长大,得到极优的延展性,对深冲非常有利;退火温度位于Ac₁~Ac₃之间(850 ℃),发生α→γ相再结晶,可以取得最好的软化效果。对于含Ti的试验钢,随着退火温度的降低,其塑性应变比r值呈下降趋势。Cr的加入不利于耐沟状腐蚀性能,但是Al的加入有利于耐沟状腐蚀性能。采用两段式退火工艺进行工业化生产,可以得到外观和性能优良的采暖系统用耐沟状腐蚀产品。

关键词: 耐沟状腐蚀性, 退火, 碳化物, 再结晶, 采暖系统

Abstract: Through the research on the phenomenon of the resistance to grooving corrosion, and combining with the production equipment capacity, six kinds of steel strip chemical compositions and six kinds of annealing processes were designed. The effect of cold rolling annealing process on the properties of grooving-corrosion resistant steel strips for heating system was studied by means of metallography, SEM, tensile test, and salt spray test. The results show that the annealing at temperature lower than Ac₁(650 and 700 ℃) can not change the genetic structure of the original grain boundary of cold-rolled ferrite, under such conditions the recrystallization of cold rolled α phase does not grow sufficiently, and the polymerization and growth of carbides are also insufficient. When the annealing temperature reaches about Ac₁(750 ℃), the solid solving of carbon increases, leading to recrystallization and growth of α phase as well as the polymerization of precipitates, resulting in excellent ductility, which is very beneficial for deep drawing. When the annealing temperature is between Ac₁-Ac₃(850 ℃), α→γ phase transformation and recrystallization occur, and the best softening effect can be obtained. While for the Ti-bearing tested steel, the plastic strain ratio r value tends to decrease with the decrease of annealing temperature. The addition of Al is conducive to increase the resistance to grooving corrosion, but the Cr addition has the opposite effect. Using two-stage annealing process for industrial production can get grooving-corrosion resistant products for heating systems with excellent appearance and properties.

Key words: grooving-corrosion resistance, annealing, carbides, recrystallization, heating system

中图分类号:

TG156.25

卢军辉, 吴战芳, 王晓春, 仇圣桃, 干勇. 退火工艺对采暖系统用耐沟状腐蚀钢带性能的影响[J]. 金属热处理, 2020, 45(8): 124-130.

Lu Junhui, Wu Zhanfang, Wang Xiaochun, Qiu Shengtao, Gan Yong. Effect of annealing process on properties of grooving-corrosion resistant steel strip for heating system[J]. Heat Treatment of Metals, 2020, 45(8): 124-130.

参考文献

[1]中国钢铁工业年鉴编委会. 中国钢铁工业年鉴[M]. 北京: 冶金工业出版社, 2014: 156.
[2]中国钢铁工业年鉴编委会. 中国钢铁工业年鉴[M]. 北京: 冶金工业出版社, 2015: 105.
[3]Hou B R, Li X G, Ma X M, et al. The cost of corrosion in China[J]. NPJ Materials Degradation, 2017(1): 1-10.
[4]正村克身, 松島巖. 電縫鋼管みぞ状腐食の事例解析[J]. 防食技術, 1979, 28(6): 348-351.
Masamura Katsumi, Matsushima Iwao. Case studies of grooving corrosion of electric resistance welded pipe[J]. Corrosion Engineering, 1979, 28(6): 348-351.
[5]加藤忠一, 乙黒靖男, 門智. 電縫鋼管に生じる溝食について--耐溝食性電縫鋼管の研究(1) [J]. 防食技術, 1974, 23(8): 385-392.
Kato Chuichi, Otoguro Yasuo, Kado Satoshi. Grooving corrosion on ERW steel pipe in sea water-study on grooving corrosion resistant ERW low alloy steel pipe (Part 1)[J]. Corrosion Engineering, 1974, 23(8): 385-392.
[6]Xiao Z H, Hu S Y, Luo J L, et al. A quantitative phase-field model for crevice corrosion[J]. Computational Materials Science, 2018, 149: 37-48.
[7]Mohammed Ismail Abdulsalam. Behaviour of crevice corrosion in iron[J]. Corrosion Science, 2005, 47: 1336-1351.
[8]Rosenfeld I L, Marshakov I K. Mechanism of crevice corrosion[J]. Corrosion, 1964, 20(4): 115-125.
[9]Brigham R J. Temperature as a crevice corrosion criterion[J]. Corrosion, 1974, 30(11): 396-398.
[10]Takahashi M, Okamoto A. Effects of heating rate, chemical composition and cold reduction on deep drawability of Al-killed steel sheet[J]. Sumitomo Metals, 1975, 27(4): 40-49.
[11]刘丽萍, 李桂兰, 宋海武. 退火和平整工艺对冷轧HSLA钢组织性能的影响[J]. 金属热处理, 2019, 44(1): 64-66.
Liu Liping, Li Guilan, Song Haiwu. Effects of annealing and temper rolling on mechanical properties and microstructure of cold rolled HSLA sheet[J]. Heat Treatment of Metals, 2019, 44(1): 64-66.
[12]李小林, 李红斌, 林哲, 等. 退火工艺对冷轧低碳钢组织和性能的影响[J]. 金属热处理, 2016, 41(6): 106-111.
Li Xiaolin, Li Hongbin, Lin Zhe, et al. Effect of annealing on microstructure and mechanical properties of cold rolled low carbon steel[J]. Heat Treatment of Metals, 2016, 41(6): 106-111.
[13]Konstantin Schacht, Ulrich Prahl, Wolfgang Bleck. Material models and their capability for process and materials properties design in different forming processes[J]. Materials Science Forum, 2016, 854: 174-182.
[14]Gorni A. Steel Forming and Heat Treating Handbook[M]. Brazil: São Vicente SP, 2016: 1-87.
[15]Ushioda K, HutchinsonW B, Ågren J. Investigation of structure and texture development during annealing of low-carbon steel[J]. Materials Science and Technology, 1986, 2(8): 807-815.
[16]Hirai Y, Tai I, Tsuji N, et al. Recrystallization, texture and their application to structural control[J]. The Iron and Steel Institute of Japan, Tokyo, 1999, 265: 971-975.
[17]Ralston K D, Birbilis N. Effect of grain size on corrosion: A review[J]. Corrosion, 2010, 66(7): 1-13.
[18]Ralston K D, Birbilis N, Davies C H J. Revealing the relationship between grain size and corrosion rate of metals[J]. Scripta Materialia, 2010, 63(12): 1201-1204.
[19]El-Sayed M Sherif, Asiful H Seikh. Effects of grain refinement on the corrosion behaviour of microalloyed steel in sulphuric acid solutions [J]. International Journal of Electrochemical Science, 2012(7): 7567-7578.
[20]Shin H S, Kim S W, Kim H P, et al. Effect of decarburization heat treatment and chromium addition on corrosion behavior of carbon steel[J]. Corrosion, 2009, 65(5): 326-331.
[21]Stanistaw Mrowec. The problem of sulfur in high-temperature corrosion[J]. Oxidation of Metals, 1995, 44(1/2): 177-209.
[22]長野博夫, 幸英昭. 電縫鋼管の溝状腐食に及ぼす微量添加元素の影響[C]//Tetsu-to-Hagane日本鉄鋼協会第95回講演大会講演概要. 1978, 64(4): 298.
[23]門智, 乙黒靖男, 加藤忠一, 等. 耐溝食性電縫鋼管について[J]. 日本造船学会誌, 1973, 532: 534-539.

退火工艺对采暖系统用耐沟状腐蚀钢带性能的影响

Effect of annealing process on properties of grooving-corrosion resistant steel strip for heating system

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	王英虎, 郑淮北, 刘庭耀, 宋令玺, 白青青. 固溶处理对53Cr21Mn9Ni4N耐热钢组织及碳化物的影响[J]. 金属热处理, 2022, 47(4): 39-45.
[2]	连轶博, 杨春雷, 王国栋, 宋威. 固溶处理对GH4080A高温合金微观组织的影响[J]. 金属热处理, 2022, 47(4): 46-52.
[3]	宿鹏吉, 麻永林, 董丽丽, 杨雪峰. 磁场预退火处理对CGO钢组织与织构的影响[J]. 金属热处理, 2022, 47(4): 128-132.
[4]	章建军, 庄晓伟, 汤晓峰. 提高低碳钢磁性能的球化退火工艺试验[J]. 金属热处理, 2022, 47(4): 182-184.
[5]	章军, 赵四新. 冷锻齿轮用16MnCrS5钢的球化退火工艺[J]. 金属热处理, 2022, 47(4): 185-188.
[6]	戴建科, 韩顺, 厉勇, 刘宪民, 王春旭, 庞学东, 李建新. 航空齿轮钢C69高温渗碳后的组织性能[J]. 金属热处理, 2022, 47(4): 219-225.
[7]	苏勇, 王帅, 王吉星, 于兴福, 刘洪秀, 刘金玲. 复合化学热处理对G13Cr4Mo4Ni4V钢组织和硬度的影响[J]. 金属热处理, 2022, 47(4): 226-230.
[8]	王国迪, 景然, 张曼雪, 冯甜, 余国庆, 解念锁. 冷轧变形量及再结晶对TC4合金组织与性能的影响[J]. 金属热处理, 2022, 47(3): 48-52.
[9]	刘志桥, 冯庆晓, 李化龙, 李腾飞. 退火工艺对低碳贝氏体钢组织与力学性能的影响[J]. 金属热处理, 2022, 47(3): 53-56.
[10]	王方军, 刘应龙, 时瑶, 万红, 刘斌斌. 等温退火处理对Inconel 625合金箔材组织和性能的影响[J]. 金属热处理, 2022, 47(3): 77-81.
[11]	余世伦, 张孝军, 孔玢, 刘正乔, 余伟, 蒋孟玲. 退火工艺对冷轧工业纯钛带卷各向异性的影响[J]. 金属热处理, 2022, 47(3): 82-87.
[12]	田亚强, 蔡志新, 徐海卫, 张宏军, 韩赟, 狄国标, 陈连生. 中锰钢ART工艺C、Mn元素配分的热力学研究[J]. 金属热处理, 2022, 47(3): 159-164.
[13]	吴方俊, 邓小云, 揭晓华, 郑开宏, 骆智超. 热作模具用H13和Dievar钢的热疲劳性能[J]. 金属热处理, 2022, 47(3): 165-172.
[14]	李阔, 孙明月, 徐斌, 李殿中. 稀土H13模具钢横向冲击性能影响因素分析[J]. 金属热处理, 2022, 47(3): 181-185.
[15]	张世进, 李凯, 易丹青, 刘会群. 冷轧TA5钛合金退火过程的再结晶行为及织构演变[J]. 金属热处理, 2022, 47(2): 1-8.