55SiCr弹簧钢中的残留奥氏体与碳化物

doi:10.13251/j.issn.0254-6051.2020.05.019

摘要/Abstract

摘要： 通过扫描电镜(SEM)、电子背散射衍射(EBSD)、透射电镜(TEM)、X射线衍射仪(XRD)、热膨胀仪、洛氏硬度计等手段研究了弹簧钢55SiCr的组织和相变点以及残留奥氏体和碳化物在热处理过程中的组织演变。结果表明:55SiCr弹簧钢淬火后残留奥氏体以块状分布在基体上;随回火温度的升高,残留奥氏体减少并呈粒状和薄膜状分布;C在残留奥氏体中富集,使其稳定性增强;Si抑制了碳化物的析出,提高了残留奥氏体的稳定性。低温回火时,Si延缓了渗碳体析出;高温回火时,C原子扩散速率提高,促进渗碳体析出,引起体积的收缩。慢速加热回火时,C有足够的时间扩散,从而促进渗碳体的形成,使渗碳体的形成温度提前;快速加热回火时,C来不及扩散,抑制了渗碳体的析出。回火加热速率一样时,试验钢的硬度随回火温度的提高而下降。当回火温度为400 ℃时,硬度值最大为51 HRC;当回火温度为650 ℃时,硬度值最小为37 HRC。当加热速率为0.1 ℃/s时,硬度值最小为33 HRC;当加热速率为200 ℃/s时,硬度值最大为40 HRC。

关键词: 55SiCr弹簧钢, 残留奥氏体, 碳化物, 回火温度, 加热速率, 硬度

Abstract: The microstructure and phase transition point of the spring steel 55SiCr, the microstructure evolution of retained austenite and carbide during heat treatment were studied by means of scanning electron microscopy (SEM), electron backscatter diffraction (EBSD), transmission electron microscopy (TEM), X-ray diffractometry (XRD), thermal expansion, and Rockwell hardness tester. The results show that the retained austenite of 55SiCr spring steel is distributed in blocks on the substrate after quenching. As the tempering temperature increases, the retained austenite is reduced and distributed in a granular and film form. Carbon is enriched in retained austenite, which enhances its stability. Since Si suppresses the precipitation of carbides, the stability of retained austenite is improved. Si delays the precipitation of cementite when tempered at low temperature. When the steel is tempered at high temperature, the diffusion of carbon atoms is increased, and the precipitation of cementite is promoted to cause volume shrinkage. Carbon has enough time to diffuse, which promotes the formation of cementite and advances the formation temperature of cementite when tempered at low heating rate. Carbon does not have enough time to diffuse and inhibits the precipitation of cementite when tempered at high heating rate. When the tempering heating rate is the same, the hardness of the tested steel decreases as the tempering temperature increases. The hardness value is 51 HRC when the tempering temperature is 400 ℃ and the hardness value is 37 HRC when the tempering temperature is 650 ℃. The hardness value is 33 HRC when the heating rate is 0.1 ℃/s and the hardness value is 40 HRC when the heating rate is 200 ℃/s.

Key words: 55SiCr spring steel, retained austenite, carbide, tempering temperature, heating rate, hardness

中图分类号:

TG142

陆慧, 陈银莉, 韦贺, 刘泽盛. 55SiCr弹簧钢中的残留奥氏体与碳化物[J]. 金属热处理, 2020, 45(5): 103-109.

Lu Hui, Chen Yinli, Wei He, Liu Zesheng. Retained austenite and carbide in 55SiCr spring steel[J]. Heat Treatment of Metals, 2020, 45(5): 103-109.

参考文献

[1]徐德祥, 尹钟大. 高强度弹簧钢的发展现状和趋势[J]. 钢铁, 2004, 39(1): 67-71.
Xu Dexiang, Yin Zhongda. The tendency to high strength of spring steel and the effect of alloying elements[J]. Iron and Steel, 2004, 39(1): 67-71.
[2]张继明, 杨振国, 李守新, 等. 汽车用高强度弹簧钢54SiCrV6和54SiCr6的超高周疲劳行为[J]. 金属学报, 2006, 42(3): 259-264.
Zhang Jiming, Yang Zhenguo, Li Shouxin, et al. Ultra high cycle fatigue behavior of automotive high strength spring steels 54SiCrV6 and 54SiCr6[J]. Acta Metallurgica Sinica, 2006, 42(3): 259-264.
[3]洪国华, 杨顺虎, 肖波, 等. 国内外弹簧钢的生产现状和发展前景[J]. 现代冶金, 2009(1): 1-4.
Hong Guohua, Yang Shunhu, Xiao Bo, et al. Production status and development prospects of spring steel at home and abroad[J]. Modern Metallurgy, 2009(1): 1-4.
[4]杨才福, 苏航, 惠卫军, 等. 高速列车用车轮钢、轴承钢和弹簧钢的发展[J]. 机车电传动, 2003(S1): 32-36.
Yang Caifu, Su Hang, Hui Weijun, et al. Development of wheel steel, bearing wheel and spring steel for high speed train[J]. Electric Drive for Locomotives, 2003(S1): 32-36.
[5]申勇, 申斌, 吴静, 等. 弹簧钢的技术发展及生产工艺现状[J]. 金属制品, 2009, 35(3): 22-25.
Shen Yong, Shen Bing, Wu Jing, et al. Technology development and production process situation of spring steel[J]. Metal Products, 2009, 35(3): 22-25.
[6]徐德祥, 尹钟大. 热处理工艺对弹簧钢组织和性能的影响[J]. 特殊钢, 2003, 24(6): 1-4.
Xu Dexiang, Yin Zhongda. Effect of high treatment process on structure and properties of spring steel[J]. Special Steel, 2003, 24(6): 1-4.
[7]李富生, 李亚峰, 康喜英, 等. 55SiCr弹簧钢弯曲疲劳试验断裂原因分析[J]. 热加工工艺, 2018, 47(5): 252-256.
Li Fusheng, Li Yafeng, Kang Xiying, et al. Reason analysis of the facture in fatigue bending test of 55SiCr spring steel[J]. Hot Working Technology, 2018, 47(5): 252-256.
[8]赵红光, 周雪娇, 王桥, 等. 冷却速度对Si-Cr型55SiCr弹簧钢组织和性能的影响[J]. 热加工工艺, 2017(8): 89-90, 93.
Zhao Hongguang, Zhou Xuejiao, Wang Qiao, et al. Influences of cooling rate on microstructure and properties of Si-Cr type 55SiCr spring steel[J]. Hot Working Technology, 2017(8): 89-90, 93.
[9]戚文, 周涛, 金方杰, 等. 55SiCr弹簧钢低温渗氮的组织和性能研究[J]. 热加工工艺, 2016(2): 180-182.
Qi Wen, Zhou Tao, Jin Fangjie, et al. Study on microstructure and properties of 55SiCr spring steel after low temperature nitriding[J]. Hot Working Technology, 2016(2): 180-182.
[10]肖金福, 刘雅政, 孙小军, 等. 弹簧钢55SiCrA轴向疲劳行为的试验研究[J]. 钢铁, 2011, 46(1): 80-85.
Xiao Jinfu, Liu Yazheng, Sun Xiaojun, et al. Axial tension and compression load fatigue behavior and mechanism of spring steel 55SiCrA[J]. Iron and Steel, 2011, 46(1): 80-85.
[11]孟耀青, 王昆鹏, 郑永瑞. 1950 MPa级弹簧钢55SiCrA疲劳断口夹杂物来源分析[J]. 钢铁研究学报, 2017, 29(10): 859-864.
Meng Yaoqing, Wang Kunpeng, Zheng Yongrui. Analysis of sources of inclusions induced fatigue failure in 1950 MPa-grade spring steel 55SiCrA[J]. Journal of Iron and Steel Research, 2017, 29(10): 859-864.
[12]邓素怀, 佟倩, 张玮, 等. 弹簧钢55SiCr组织精细结构分析[J]. 物理测试, 2016, 34(4): 12-16.
Deng Suhuai, Tong Qian, Zhang Wei, et al. Analysis of fine microstructure of spring steel 55SiCr[J]. Physics Examination and Testing, 2016, 34(4): 12-16.
[13]王晓峰, 陈伟庆. 冷却速率对55CrSi弹簧钢的相变组织和显微硬度的影响[J]. 上海金属, 2010, 32(6): 13-15.
Wang Xiaofeng, Chen Weiqing. Influence of cooling rate on transformation structure and micro-hardness of spring steel 55CrSi[J]. Shanghai Metals, 2010, 32(6): 13-15.
[14]袁宏梅, 王军艺, 刘新宽, 等. 高强度悬架弹簧钢丝的组织结构[J]. 金属热处理, 2018, 43(2): 106-110.
Yuan Hongmei, Wang Junyi, Liu Xinkuan, et al. Microstructure of high strength suspension spring steel wire[J]. Heat Treatment of Metals, 2018, 43(2): 106-110.
[15]黄文克, 王雷, 彭天兰, 等. 回火温度对弹簧钢55SiCrA组织与性能的影响[J]. 金属制品, 2011, 37(1): 61-65.
Huang Wenke, Wang Lei, Peng Tianlan, et al. Effect of tempering temperature on microstructure and properties of spring steel 55SiCrA[J]. Steel Wire Products, 2011, 37(1): 61-65.
[16]肖金福, 刘雅政, 孙小军, 等. 变形温度对弹簧钢55SICRA组织和性能的影响[J]. 特殊钢, 2010, 31(2): 60-62.
Xiao Jinfu, Liu Yazheng, Sun Xiaojun, et al. Effect of deforming temperature on structure and properties of spring steel 55SiCrA[J]. Special Steel, 2010, 31(2): 60-62.
[17]宋维锡. 金属学[M]. 2版. 北京: 冶金工业出版社, 1989.
[18]王立军, 余伟, 武会宾, 等. Si对超高强钢残留奥氏体回火稳定性与力学性能的影响[J]. 材料热处理学报, 2010, 31(10): 30-36.
Wang Lijun, Yu Wei, Wu Huibin, et al. Effect of Si on tempering stability of retained austenite and mechanical properties of ultra-high strength steel[J]. Transactions of Materials and Heat Treatment, 2010, 31(10): 30-36.
[19]Xiong X C, Chen B, Huang M X, et al. The effect of morphology on the stability of retained austenite in a quenched and partitioned steel[J]. Scripta Materialia, 2013, 68(5): 321-324.
[20]江海涛, 唐荻, 刘强, 等. TRIP钢中残余奥氏体及其稳定性的研究[J]. 上海金属, 2007, 42(5): 155-159.
Jiang Haitao, Tang Di, Liu Qiang, et al. Investigation of retained austenite and its stabilization in trip steel[J]. Shanghai Metals, 2007, 42(5): 155-159.
[21]刘耀中, 左传付. 轴承钢零件淬回火后的残余奥氏体[J]. 轴承, 2008(6): 4-7.
Liu Yaozhong, Zuo Chuanfu. Retained austenite after quenching and tempering of bearing steel parts[J]. Bearing, 2008(6): 4-7.
[22]Zhu K, Shi H, Chen H, et al. Effect of Al on martensite tempering: Comparison with Si[J]. Journal of Materials Science, 2018, 53(9): 6951-6967.
[23]Kim B, Celada C, San Martín D, et al. The effect of silicon on the nanoprecipitation of cementite[J]. Acta Materialia, 2013, 61(18): 6983-6992.
[24]Jacques P, Girault E, Catlin T, et al. Bainite transformation of low carbon Mn-Si TRIP-assisted multiphase steels: Influence of silicon content on cementite precipitation and austenite retention[J]. Materials Science and Engineering: A, 1999, 273/275: 475-479.
[25]Wu H, Ju B, Tang D, et al. Effect of Nb addition on the microstructure and mechanical properties of an 1800 MPa ultrahigh strength steel[J]. Materials Science and Engineering: A, 2015, 622: 61-66.
[26]许黎明, 陈银莉, 牛刚, 等. 回火温度对Si-Mn系中碳弹簧钢组织及性能的影响[J]. 轧钢, 2016, 33(3): 29-32.
Xu Liming, Chen Yinli, Niu Gang, et al. Influence of tempering temperature on mechanical properties and microstructure of Si-Mn medium carbon spring steel[J]. Steel Rolling, 2016, 33(3): 29-32.
[27]王轩, 陈银莉, 许黎明, 等. 合金元素Mn、Cr、V对中碳弹簧钢回火组织及力学性能的影响[J]. 热加工工艺, 2016, 45(12): 183-186.
Wang Xuan, Chen Yinli, Xu Liming, et al. Influence of alloying element Cr, Mn and V on microstructure and mechanical properties of medium carbon spring steel after tempering[J]. Hot Working Technology, 2016, 45(12): 183-186.
[28]朱杰, 杨春林, 姜云, 等. 回火温度对60Si2CrVAT弹簧钢组织及性能的影响[J]. 金属热处理, 2016, 41(3): 54-57.
Zhu Jie, Yang Chunlin, Jiang Yun, et al. Influence of tempering temperature on microstructure and properties of 60Si2CrVAT spring steel[J]. Heat Treatment of Metals, 2016, 41(3): 54-57.
[29]樊艳秋, 蔡庆伍, 张杰. 快速加热条件下加热速率对E690海洋用钢显微硬度及析出物的影响[J]. 金属热处理, 2012, 37(5): 15-19.
Fan Yanqiu, Cai Qingwu, Zhang Jie. Effects of heating rate on microstructure and precipitation of E690 marine steel under rapid heating[J]. Heat Treatment of Metals, 2012, 37(5): 15-19.