固溶工艺对2A12铝合金组织与性能的影响

doi:10.13251/j.issn.0254-6051.2025.04.031

金属热处理 ›› 2025, Vol. 50 ›› Issue (4): 213-217.DOI: 10.13251/j.issn.0254-6051.2025.04.031

固溶工艺对2A12铝合金组织与性能的影响

李侠^1,2, 贾品峰³, 耿旭^1,2, 崔东卫^1,2

1.海洋装备金属材料及其应用全国重点实验室, 辽宁鞍山 114009;
2.鞍钢集团钢铁研究院, 辽宁鞍山 114009;
3.辽宁科技大学材料与冶金学院, 辽宁鞍山 114009

收稿日期:2024-10-30 修回日期:2025-01-09 发布日期:2025-06-13
作者简介:李侠(1983—),女,副研究员,主要研究方向为金属材料,E-mail:aglixia@163.com

Effect of solution treatment process on microstructure and properties of 2A12 aluminum alloy

Li Xia^1,2, Jia Pinfeng³, Geng Xu^1,2, Cui Dongwei^1,2

1. State Key Laboratory of Metallic Materials for Marine Equipment and Applications, Anshan Liaoning 114009, China;
2. Ansteel Iron & Steel Research Institues, Anshan Liaoning 114009, China;
3. College of Materials and Metallurgy, University of Science and Technology Liaoning, Anshan Liaoning 114009, China

Received:2024-10-30 Revised:2025-01-09 Published:2025-06-13

摘要/Abstract

摘要： 采用差热分析(DSC)、扫描电镜(SEM)、能谱分析(EDS)和X射线衍射(XRD)等手段,研究了2A12合金固溶过程中残余相的溶解行为。结果表明,轧制态2A12合金的过烧温度为509.6 ℃,合金中主要相为Al、Cu、Mg的非平衡凝固共晶残余相。固溶过程中,合金中的非平衡共晶相逐渐熔断并球化,偏析元素向基体中溶解;随着固溶温度的升高,试样的硬度增大,这是由于试样中的非平衡共晶相更多地溶入基体,基体固溶度提高,增加了溶质原子溶入溶剂晶格的数量,使硬度增大。

关键词: 2A12铝合金, 固溶处理, 残余相

Abstract: Dissolution behavior of residual phases at grain boundaries during the solution process of 2A12 alloy was studied by using techniques such as differential scanning calorimetry (DSC), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and X-ray diffraction (XRD). The results show that the overburning temperature of the 2A12 alloy is 509.6 ℃, and the main phases in the rolled state alloy are non-equilibrium solidification eutectic phases of Al, Cu, and Mg. During the solution treatment process, the non-equilibrium eutectic phase in the alloy gradually melts and spheroidizes, and the segregated elements dissolve into the matrix. As the solution treatment temperature increases, the hardness of the specimen increases. This is because more non-equilibrium eutectic phases in the specimen dissolve into the matrix, increasing the solubility of the matrix and increasing the number of solute atoms dissolved into the solvent lattice, resulting in an increase in hardness.

Key words: 2A12 aluminum alloy, solution treatment, residual phase

中图分类号:

TG166.3

李侠, 贾品峰, 耿旭, 崔东卫. 固溶工艺对2A12铝合金组织与性能的影响[J]. 金属热处理, 2025, 50(4): 213-217.

Li Xia, Jia Pinfeng, Geng Xu, Cui Dongwei. Effect of solution treatment process on microstructure and properties of 2A12 aluminum alloy[J]. Heat Treatment of Metals, 2025, 50(4): 213-217.

参考文献

[1] 杨守杰, 戴圣龙. 航空铝合金的发展回顾与展望[J]. 材料导报, 2005, 19(2): 76-80.
Yang Shoujie, Dai Shenglong. A glimpse at the development and application of aluminum alloys in aviation industry[J]. Materials Reports, 2005, 19(2): 76-80.
[2] 孙建林. 有色金属及其热处理[M]. 北京: 国防工业出版社, 1981.
[3] 张君尧. 铝合金材料的新进展(1)[J]. 轻合金加工技术, 1998, 26(5): 1-6, 10.
Zhang Junyao. Recent development of aluminum alloy materials(1)[J]. Light Alloy Fabrication Technology, 1998, 26(5): 1-6, 10.
[4] 梁忠华. 2124铝合金铸态及厚板的组织分析[J]. 黑龙江大学自然科学报, 1995, 12(2): 72-76.
Liang Zhonghua. Microscopical structures analysis of cast constitution and plant in 2124 aluminum alloy[J]. Journal of Natural Science of Heilongjiang University, 1995, 12(2): 72-76.
[5] Cole G S. Inhomogeneities and their control via solidification[J]. Metall Trans, 1971, 2(2): 57-370.
[6] Cantrell M A, Anderson K R, Archibald K H. Mechod of making AA 7000 series aluminum wrought product having a modified solution heat treating process for improved exfoliation corrosion resistance: US 5785777A[P]. 1998-07-28.
[7] 周华, 肖顺华. 固溶处理对2E12铝合金显微组织和力学性能的影响[J]. 铝加工, 2011, 34(3): 25-29.
Zhou Hua, Xiao Shunhua. Effect of solution treatment on microstructure and mechanical properties of 2E12 aluminum alloy[J]. Aluminum Fabrication, 2011, 34(3): 25-29.
[8] 戴晓元, 夏长清, 刘昌斌, 等. 固溶处理及时效对7×××铝合金组织与性能的影响[J]. 材料热处理学报, 2007, 28(4): 59-63.
Dai Xiaoyuan, Xia Changqing, Liu Changbin, et al. Effects of solution treatment and aging process on microstructure and mechanical properties of 7××× aluminum alloy[J]. Transactions of Materials and Heat Treatment, 2007, 28(4): 59-63.
[9] 李海, 王芝秀, 魏修宇, 等. 固溶处理时间对2E12铝合金组织和疲劳性能的影响[J]. 航空学报, 2009, 30(1): 148-152.
Li Hai, Wang Zhixiu, Wei Xiuyu, et al. Effect of solution treatment time on microstructures and fatigue properties of aluminum alloy 2E12[J]. Acta Aeronautica et Astronautica Sinica, 2009, 30(1): 148-152.
[10] Lasa L, Rodriguez-Ibabe J M. Evolution of the main intermetallic phases in Al-Si-Cu-Mg casting alloys during solution treatment[J]. Journal of Materials Science, 2004(39): 1343-1355.
[11] Wang G Q, Bian X F, Wang K M, et al. Influence of Cu and minor elements on solution treatment of Al-Si-Mg-Cu cast alloy[J]. Materials Letters, 2003, 57(24/25): 4083-4087.
[12] Xu Xiaojing, Zhang Jie, Chen Kangming, et al. Improvement of strength in 2024 Al alloy by enhanced solution treatment[C] //Transactions of Materials and Heat Treatment proceedings of the 14^th IFHTSE Congress, 2004, 25: 297-300.
[13] 刘红卫, 陈康华, 刘允中, 等. 强化固溶对2014铝合金组织与性能的影响[J]. 湖南有色金属, 2000, 16(4): 28-30, 47.
Liu Hongwei, Chen Kanghua, Liu Yunzhong, et al. Effect of strengthening solution on the microstructure and mechanical properties of aluminum alloy 2014[J]. Hunan Nonferrous Metals, 2000, 16(4): 28-30, 47.

[1]	郭旭东, 邹仕军, 卢影峰, 龙泽熙. 固溶工艺对7C04铝合金组织与性能的影响[J]. 金属热处理, 2025, 50(3): 132-137.
[2]	房洪杰, 杨喻曾, 张智楷, 闵红, 刘振东, 沈雨欣. 含稀土Ce 7055铝合金的固溶时效处理[J]. 金属热处理, 2025, 50(2): 155-159.
[3]	刘松, 刘弢. 固溶时效处理对N03360镍铍合金组织的影响[J]. 金属热处理, 2025, 50(1): 150-154.
[4]	陈岩, 裴悦涵, 张闯, 宋华, 廉法博, 关士学, 汪洋, 王晓雪. 6063铝合金的固溶-风淬-时效工艺[J]. 金属热处理, 2024, 49(9): 125-131.
[5]	李喆, 李睿, 蔡磊, 靳军军. 固溶处理对机车车辆抱轴箱内壁堆焊层组织和力学性能的影响[J]. 金属热处理, 2024, 49(9): 226-231.
[6]	熊伟, 戴志勇. 固溶处理对50Cr-50Ni合金组织与性能的影响[J]. 金属热处理, 2024, 49(9): 260-264.
[7]	白瑞, 杜云飞, 贺秀丽, 梁红玉. Al含量对高锰高铝轻质钢组织和力学性能的影响[J]. 金属热处理, 2024, 49(8): 48-52.
[8]	孙数理, 侯小虎, 郭文霞, 张静, 王超, 赵学平, 曹宇. 单级固溶温度对喷射沉积2195铝锂合金组织演变的影响[J]. 金属热处理, 2024, 49(6): 62-68.
[9]	乔景振, 张笑闻, 张环月, 付雪松, 周文龙, 陈国清. 喷丸强化与固溶强化复合处理对2024铝合金耐蚀性能的影响[J]. 金属热处理, 2024, 49(6): 69-76.
[10]	赵忠超, 汲庆涛, 曹善鹏, 唐和壮, 李宾良, 牛博雅, 孙有政. 固溶处理对7175铝合金组织和力学性能的影响[J]. 金属热处理, 2024, 49(5): 186-192.
[11]	王亚勇, 曹喜娟, 任广笑, 刘永哲, 郑云凯. 热处理对差压铸造ZL201A铝合金壳体内部组织及性能的影响[J]. 金属热处理, 2024, 49(3): 108-111.
[12]	李海涛, 陈冬梅, 官海婷, 袁武华. Ti62A钛合金固溶过程中初生α相的球化机理[J]. 金属热处理, 2024, 49(3): 168-173.
[13]	崔毅, 曹文全, 王艳, 崔继红, 马超, 田仲杰, 张雲飞. 固溶温度及冷却方式对00Cr40Ni55Al3Ti合金组织性能的影响[J]. 金属热处理, 2024, 49(2): 142-148.
[14]	高雪鹏, 孙有政, 曹善鹏, 牛博雅, 李宾良, 王萍. 热处理工艺对7075铝合金组织及晶间腐蚀性能的影响[J]. 金属热处理, 2024, 49(2): 159-165.
[15]	王海瑞, 王锦永, 刘富强, 齐希伦, 高正磊. 超级双相不锈钢S32750轧制开裂原因分析和解决措施[J]. 金属热处理, 2024, 49(2): 291-296.

固溶工艺对2A12铝合金组织与性能的影响

Effect of solution treatment process on microstructure and properties of 2A12 aluminum alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价