Ce对50W400无取向硅钢常化组织及织构的影响

doi:10.13251/j.issn.0254-6051.2025.03.027

金属热处理 ›› 2025, Vol. 50 ›› Issue (3): 167-173.DOI: 10.13251/j.issn.0254-6051.2025.03.027

Ce对50W400无取向硅钢常化组织及织构的影响

齐建波¹, 杨礼林¹, 张旭东², 金自力¹, 蔚惠民³

1.内蒙古科技大学工程训练中心, 内蒙古包头 014010;
2.宝钢湛江钢铁有限公司, 广东湛江 524000;
3.国家能源准能集团有限责任公司, 内蒙古鄂尔多斯 010300

收稿日期:2024-09-15 修回日期:2025-01-02 出版日期:2025-03-25 发布日期:2025-05-14
通讯作者: 杨礼林,讲师,博士,E-mail:yanglilin@imust.edu.cn
作者简介:齐建波(1974—),男,讲师,博士,主要研究方向为稀土钢开发与设计,E-mail:2016941@imust.edu.cn。
基金资助:
内蒙古自然科学基金(2024MS05058);内蒙古包钢钢联股份有限公司开发项目(2019089)

Effect of Ce on normalizing microstructure and texture of 50W400 non-oriented silicon steel

Qi Jianbo¹, Yang Lilin¹, Zhang Xudong², Jin Zili¹, Yu Huimin³

1. Engineering Training Center, Inner Mongolia University of Science and Technology, Baotou Inner Mongolia 014010, China;
2. Baosteel Zhanjiang steel Co., Ltd., Zhanjiang Guangdong 524000, China;
3. National Energy Quasi-Energy Group Co., Ltd., Erdos Inner Mongolia 010300, China

Received:2024-09-15 Revised:2025-01-02 Online:2025-03-25 Published:2025-05-14

摘要/Abstract

摘要： 采用金相观察、SEM-EBSD测试分析了加入稀土Ce后50W400无取向硅钢常化后组织与织构的演变规律,明确稀土Ce对常化后试验钢晶粒度和织构强度的变化趋势。结果表明,加入Ce可推迟常化时组织的完全再结晶时间,即添加稀土后的试验钢,在均温970 ℃下,保持晶粒尺寸均匀分布状态的时间,由155 s可以推迟至215 s,且晶粒尺寸相比更小。同时,在试验钢的纵截面厚度方向,有利面织构{100}和{110}占比增加,不利面织构{111}占比减少。

关键词: 无取向硅钢, 稀土Ce, 常化, 组织, 织构

Abstract: Evolution of the normalizing microstructure and texture of 50W400 non-oriented silicon steel after adding rare earth element Ce was analyzed by means of metallographic observation and SEM-EBSD instruments. This investigation aimed to clarify the trend of changes in grain size and texture strength of the tested steel after normalizing.The results indicate that the addition of Ce can delay the complete recrystallization time during normalizing. Specifically, with rare earth Ce adding, the time for maintaining a uniform grain size distribution at a uniform temperature of 970 ℃ can be postponed from 155 s to 215 s, and the grain size is smaller. Furthermore, in the thickness direction of the longitudinal section of the tested steel, the proportion of favorable surface textures {100} and {110} increases, while the proportion of the unfavorable surface texture {111} decreases.

Key words: non-oriented silicon steel, rare earth Ce, normalizing, microstructure, texture

中图分类号:

齐建波, 杨礼林, 张旭东, 金自力, 蔚惠民. Ce对50W400无取向硅钢常化组织及织构的影响[J]. 金属热处理, 2025, 50(3): 167-173.

Qi Jianbo, Yang Lilin, Zhang Xudong, Jin Zili, Yu Huimin. Effect of Ce on normalizing microstructure and texture of 50W400 non-oriented silicon steel[J]. Heat Treatment of Metals, 2025, 50(3): 167-173.

参考文献

[1] 林子博, 任慧平, 吴忠旺, 等. 常化工艺对新能源汽车驱动电机用高强无取向电工钢组织与织构的影响[J]. 热加工工艺, 2023, 52(10): 112-117, 122.
Lin Zibo, Ren Huiping, Wu Zhongwang, et al. Effects of normalizing process on microstructure and texture of high strength non-oriented electrical steel for new energy vehicle drive motors[J]. Hot Working Technology, 2023, 52(10): 112-117, 122.
[2] 龚坚, 罗海文. 新能源汽车驱动电机用高强度无取向硅钢片的研究与进展[J]. 材料工程, 2015, 43(6): 102-112.
Gong Jian, Luo Haiwen. Progress on the research of high-strength non-oriented silicon steel sheets in traction motors of hybrid/electrical vehicles[J]. Journal of Materials Engineering, 2015, 43(6): 102-112.
[3] 谢颂康, 李志红, 刘海涛. 常化温度对3. 0%Si无取向硅钢组织、织构及磁性能的影响[J]. 电工钢, 2023, 5(2): 13-19.
Xie Songkang, Li Zhihong, Liu Haitao. Effect of normalizing temperature on microstructure, texture and magnetic properties of 3.0%Si non-oriented silicon steel[J]. Electrica Steel, 2023, 5(2): 13-19.
[4] Komatsubara M, Sadahiro K, Kondo O, et al. Newly developed electrical steel for high-frequency use[J]. Journal of Magnetism and Magnetic Materials, 2002, 242-245: 212-215.
[5] Senda K, Namikawa M, Hayakawa Y. Electrical steels for advanced automobiles-Core materials for motors, generators, and high-frequency reactors[J]. JFE Technical Report, 2004(4): 67-73.
[6] 何忠治, 赵宇, 罗海文. 电工钢[M]. 北京: 冶金工业出版社, 2012.
[7] 谢珊珊, 李慧, 刘晓, 等. 织构及合金元素对硅钢性能的影响[J]. 热加工工艺, 2017, 46(6): 12-15.
Xie Shanshan, Li Hui, Liu Xiao, et al. Effect of texture and alloying elements on properties of silicon steel[J]. Hot Working Technology, 2017, 46(6): 12-15.
[8] 师彩娟, 任慧平, 金自力, 等. 铈对无取向硅钢再结晶组织及织构的影响[J]. 稀土, 2015, 36(2): 78-81.
Shi Caijuan, Ren Huiping, Jin Zili, et al. Effect of Ce on recrystallization microstructure and texture of non-oriented silicon steel[J]. Chinese Rare Earths, 2015, 36(2): 78-81.
[9] Li Hui, Feng Yunli, Song Meng, et al. Effect of normalizing cooling process on microstructure and precipitates in low-temperature silicon steel[J]. Transactions of Nonferrous Metals Society of China, 2014, 24(3): 770-776.
[10] Ling Chen, Xiang Li, Qiu Shengtao, et al. Effects of normalizing annealing on grain-oriented silicon steel[J]. Journal of Iron and Steel Research International, 2014, 21(7): 690-694.
[11] Wang Yang, Zhang Yuanxiang, Lu Xiang, et al. Effect of hot rolling on texture, precipitation, and magnetic properties of strip-cast grain-oriented silicon steel[J]. Steel Research International, 2016, 87(12): 1601-1608.
[12] 樊立峰, 岳尔斌, 项利, 等. CSP工艺生产高牌号无取向电工钢的组织和夹杂物[J]. 钢铁研究学报, 2008, 20(1): 32-36.
Fan Lifeng, Yue Erbin, Xiang Li, et al. Structure and inclusion of high grade non-oriented electrical steel produced in CSP process[J]. Journal of Iron and Steel Research, 2008, 20(1): 32-36.
[13] 罗翔, 项利, 仇圣桃, 等. 稀土铈含量对1.2%Si无取向电工钢组织、织构及磁性能的影响[J]. 机械工程材料, 2014, 38(1): 6-10, 31.
Luo Xiang, Xiang Li, Qiu Shengtao, et al. Effect of rare earth cerium contents on microstructure, texture and magnetic properties of 1.2%Si non-oriented electrical steels[J]. Materials for Mechnical Engineering, 2014, 38(1): 6-10, 31.
[14] 谢东西. 稀土Ce及其加入量对50W470无取向硅钢组织及织构的影响[D]. 包头: 内蒙古科技大学, 2021.
Xie Dongxi. Rare earth Ce and its added amount are not available for 50W470 influence on the structure and texture of silicon steel[D]. Baotou: Inner Mongolia University of Science & Technology, 2021.

[1]	李申奥, 陈思文, 牛红伟, 朱红倩, 阚允, 江艳, 王健, 赵洪运. 轧制温度对Sc微合金化Al-3.2Cu-1.5Li合金组织和性能的影响[J]. 金属热处理, 2025, 50(3): 1-8.
[2]	兖利鹏, 孙瑞雪, 马秉馨, 付靖, 苏光, 李全安, 郑鸿江. 时效处理对热挤压态Mg-Gd-Y-Sm-Zr合金组织和性能的影响[J]. 金属热处理, 2025, 50(3): 9-15.
[3]	王畅, 王良, 周培山, 申文竹, 王斌. 冷变形及热处理对GH738镍基合金组织与性能的影响[J]. 金属热处理, 2025, 50(3): 25-31.
[4]	郑东升, 范才河, 周顺志, 董跃, 夏毅. 工程机械用超高强钢的直接淬火-回火工艺及组织性能[J]. 金属热处理, 2025, 50(3): 51-56.
[5]	王广, 殷天青, 孙亚松, 王鑫, 柯汉章, 奚邱炎, 郝琛, 李子洲. 淬火温度对403马氏体不锈钢组织及硬度的影响[J]. 金属热处理, 2025, 50(3): 57-63.
[6]	徐和林, 王江华. 焊后热处理对4Cr5MoSiV模具钢修补焊接头组织和性能的影响[J]. 金属热处理, 2025, 50(3): 64-68.
[7]	宋子豪, 郭艳辉, 魏延新, 付斌. 中间退火温度对两阶段轧制无取向硅钢织构的影响[J]. 金属热处理, 2025, 50(3): 74-80.
[8]	王娇娇, 高云哲, 郭泰瑜, 侯伟, 周玉青, 任可飘, 赵林林, 张子悦. 回火时间对深井套管用钢组织性能的影响[J]. 金属热处理, 2025, 50(3): 102-106.
[9]	孙江波, 段路昭, 任帅, 孙彩凤, 高志新, 彭飞. 热处理工艺对20CrMoH钢齿轮锻件组织和硬度的影响[J]. 金属热处理, 2025, 50(3): 143-146.
[10]	毛福祥, 岳琪, 王奇, 李鹏, 张建国. 固溶时效处理对高铬合金3J40组织和性能的影响[J]. 金属热处理, 2025, 50(3): 147-149.
[11]	马若曦, 尹宇彬, 邓超, 李子瑜, 张哲临, 丁桦. Fe-18Mn-8Al-1C轻质钢的组织性能及变形机制[J]. 金属热处理, 2025, 50(3): 183-188.
[12]	周浩, 杜豪杰, 曾燕屏, 郭德瑞, 李炜丽, 马志宝, 王庆峰, 李旌鑫. 高温长时在役GH4145合金螺栓的显微组织和力学性能[J]. 金属热处理, 2025, 50(3): 189-195.
[13]	梁晓东, 王炜, 李永清, 袁博, 郭晓峰, 程言龙. G115钢大口径厚壁管长期时效后的微观组织及力学性能[J]. 金属热处理, 2025, 50(3): 196-200.
[14]	董恩涛, 滕艾均, 方强, 陈鑫, 代广霖, 康强, 王鹏, 耿乃涛. Ti-38644钛合金热变形行为及组织演变[J]. 金属热处理, 2025, 50(3): 201-207.
[15]	齐加胜, 徐文权. 汽车用中锰钢的研究现状与展望[J]. 金属热处理, 2025, 50(3): 244-249.

Ce对50W400无取向硅钢常化组织及织构的影响

Effect of Ce on normalizing microstructure and texture of 50W400 non-oriented silicon steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价