控轧控冷对Ti-Mo-Nb复合微合金化低碳钢组织和力学性能的影响

doi:10.13251/j.issn.0254-6051.2023.01.027

金属热处理 ›› 2023, Vol. 48 ›› Issue (1): 155-162.DOI: 10.13251/j.issn.0254-6051.2023.01.027

控轧控冷对Ti-Mo-Nb复合微合金化低碳钢组织和力学性能的影响

张金城¹, 孙胜辉¹, 蔡明晖^1,2, 赵文柱³, 丁桦^1,2

1.东北大学材料科学与工程学院, 辽宁沈阳 110819;
2.辽宁省轻量化用关键金属材料重点实验室, 辽宁沈阳 110819;
3.东北大学轧制技术及连轧自动化国家重点实验室, 辽宁沈阳 110819

收稿日期:2022-08-12 修回日期:2022-11-08 出版日期:2023-01-25 发布日期:2023-02-03
通讯作者: 丁桦,教授,博士生导师,E-mail:dingh@smm.neu.edu.cn
作者简介:张金城(1996—),男,硕士研究生,主要研究方向为材料成形及组织性能控制,E-mail:1609822435@qq.com。

Effect of TMCP on microstructure and mechanical properties of Ti-Mo-Nb microalloyed low carbon steel

Zhang Jincheng¹, Sun Shenghui¹, Cai Minghui^1,2, Zhao Wenzhu³, Ding Hua^1,2

1. School of Materials Science and Engineering, Northeastern University, Shenyang Liaoning 110819, China;
2. Key Laboratory of Lightweight Structural Materials in Liaoning Province, Shenyang Liaoning 100819, China;
3. State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang Liaoning 110819, China

Received:2022-08-12 Revised:2022-11-08 Online:2023-01-25 Published:2023-02-03

摘要/Abstract

摘要： 研究了控轧控冷的冷却速度对Ti-Mo-Nb微合金高强钢组织与性能的影响。结果表明,随着冷却速度的降低,试验钢中铁素体逐渐等轴化,铁素体的体积分数、晶粒尺寸逐渐增加。冷却速度的降低可显著细化析出相尺寸并增加其体积分数,析出方式由弥散析出向相间析出转变。铁素体通过析出强化实现提升材料强度的同时,成形性能得到改善。当冷却速度为28 ℃/s时,试验钢获得了优异的综合力学性能,抗拉强度为853 MPa,屈服强度为750 MPa,伸长率为18.6%,扩孔率为68.5%。组织细化与析出强化是试验钢的主要强化机制,当冷却速度为28 ℃/s时,细晶强化和析出强化强度增量分别为206 MPa和328 MPa。

关键词: Ti-Mo-Nb钢, 析出物, 扩孔率, 强化机制

Abstract: Effect of cooling rate of TMCP on microstructure and mechanical properties of Ti-Mo-Nb microalloyed steel was studied. The results show that as the cooling rate decreases, the ferrite grains become equiaxed and the volume fraction and grain size of the ferrite gradually increase. Reducing the cooling rate can significantly refine the size of the precipitates and increase its volume fraction, and the precipitation behavior changes from dispersive precipitation to interphase precipitation. The precipitation strengthening of ferrite improves the strength of the tested steel, as well as the formability. When the cooling rate is 28 ℃/s, an excellent combination of strength and ductility is obtained as the tensile strength of 853 MPa, the yield strength of 750 MPa, the elongation of 18.6%and the hole expansion rate of 68.5%. The grain refinement strengthening and precipitation strengthening are the main strengthening mechanisms of the tested steel, when the cooling rate is 28 ℃/s, the strength increments of grain refinement strengthening and precipitation strengthening are 206 MPa and 328 MPa, respectively.

Key words: Ti-Mo-Nb steel, precipitation, hole expansion rate, strengthening mechanism

中图分类号:

TG142.1⁺4

张金城, 孙胜辉, 蔡明晖, 赵文柱, 丁桦. 控轧控冷对Ti-Mo-Nb复合微合金化低碳钢组织和力学性能的影响[J]. 金属热处理, 2023, 48(1): 155-162.

Zhang Jincheng, Sun Shenghui, Cai Minghui, Zhao Wenzhu, Ding Hua. Effect of TMCP on microstructure and mechanical properties of Ti-Mo-Nb microalloyed low carbon steel[J]. Heat Treatment of Metals, 2023, 48(1): 155-162.

参考文献

[1]陈俊, 吕梦阳, 唐帅, 等. V-Ti微合金钢的组织性能及相间析出行为[J]. 金属学报, 2014, 50(5): 524-530.
Chen Jun, Lü Mengyang, Tang Shuai, et al. Mechanical properties and interphase precipitation behaviors in V-Ti microalloyed steel[J]. Acta Metallurgica Sinica, 2014, 50(5): 524-530.
[2]Mukherjee S, Timokhina I, Zhu C, et al. Clustering and precipitation processes in a ferritic titanium-molybdenum microalloyed steel[J]. Journal of Alloys and Compounds, 2017, 690(5): 621-632.
[3]汪小培, 赵征志, 赵爱民, 等. Mo含量对Ti微合金低碳钢力学性能的影响[J]. 金属热处理, 2014, 39(10): 47-50.
Wang Xiaopei, Zhao Zhengzhi, Zhao Aimin, et al. Effect of Mo content on mechanical properties of Ti micro-alloyed low-carbon steel[J]. Heat Treatment of Metals, 2014, 39(10): 47-50.
[4]Cheng L, Cai Q W, Yu W. Coarsening of nanoscale (Ti, Mo)C precipitates in different ferritic matrixes[J]. Materials Characterization, 2018, 142: 195-202.
[5]张可, 雍岐龙, 孙新军, 等. 卷取温度对Ti-V-Mo复合微合金化超高强度钢组织及力学性能的影响[J]. 金属学报, 2016, 52(5): 529-537.
Zhang Ke, Yong Qilong, Sun Xinjun, et al. Effect of coiling temperature on microstructure and mechanical properties of Ti-V-Mo complex microalloyed ultra-high strength steel[J]. Acta Metallurgica Sinica, 2016, 52(5): 529-537.
[6]Huang H H, Yang G W, Zhao G, et al. Effect of Nb on the microstructure and properties of Ti-Mo microalloyed high-strength ferritic steel[J]. Materials Science and Engineering A, 2018, 736: 148-155.
[7]孙超凡, 蔡庆伍, 武会宾, 等. 轧制工艺对铁素体基体Ti-Mo微合金钢纳米尺度碳氮化物析出行为的影响[J]. 金属学报, 2012, 48(12): 1415-1421.
Sun Chaofan, Cai Qingwu, Wu Huibin, et al. Effect of controlled rolling processing on nanometer-sized carbonitride of Ti-Mo ferrite matrix microalloyed steel[J]. Acta Metallurgica Sinica, 2012, 48(12): 1415-1421.
[8]Funakawa Y, Shiozaki T, Tomita K, et al. Development of high strength hot-rolled sheet steel consisting of ferrite and nanometer-sized carbides[J]. ISIJ International, 2004, 44: 1945-1951.
[9]Lee W B, Hong S G, Park C G, et al. Carbide precipitation and high-temperature strength of hot-rolled high-strength, low-alloy steels containing Nb and Mo[J]. Metallurgical and Materials Transactions A, 2002, 33(6): 1689-1698.
[10]Hajyakbary F, Sietsma J, Böttger A J, et al. An improved X-ray diffraction analysis method to characterize dislocation density in lath martensitic structures[J]. Materials Science and Engineering A, 2015, 639: 208-218.
[11]Ungár T, Ott S, Sanders P G, et al. Dislocations, grain size and planar faults in nanostructured copper determined by high resolution X-ray diffraction and a new procedure of peak profile analysis[J]. Acta Materialia, 1998, 46(10): 3693-3699.
[12]Hong S G, Yong W K, Kim J H, et al. Effects of rolling temperature on the microstructure and mechanical properties of Ti-Mo microalloyed hot-rolled high strength steel[J]. Materials Science and Engineering A, 2014, 605: 244-252.
[13]Kamikawa N, Ab E Y, Miyamoto G, et al. Tensile behavior of Ti, Mo-added low carbon steels with interphase precipitation[J]. ISIJ International, 2014, 54(2): 474-474.
[14]Yen H W, Chen P Y, Huang C Y, et al. Interphase precipitation of nanometer-sized carbides in a titanium-molybdenum-bearing low-carbon steel[J]. Acta Materialia, 2011, 59(16): 6264-6274.
[15]Chun E J, Do H, Kim S, et al. Effect of nanocarbides and interphase hardness deviation on stretch-flangability in 998 MPa hot-rolled steels[J]. Materials Chemistry and Physics, 2013, 140(1): 307-315.
[16]Kamikawa N, Sato K, Miyamoto G, et al. Stress-strain behavior of ferrite and bainite with nano-precipitation in low carbon steels[J]. Acta Materialia, 2015, 83: 383-396.
[17]Cai M H, Chen L G, Fang K, et al. The effects of a ferritic or martensitic matrix on the tensile behavior of a nano-precipitation strengthened ultra-low carbon Ti-Mo-Nb steel[J]. Materials Science and Engineering A, 2021, 801(11): 140410.
[18]雍岐龙. 钢铁材料中的第二相[M]. 北京: 冶金工业出版社, 2006.
[19]Sarkar B, Jha B K. Development of precipitation strengthened steel with adequate stretch flangeability[J]. Journal of Materials Engineering and Performance, 2011, 20(8): 1414-1418.
[20]Wang R, Garcia C I, Hua H, et al. Microstructure and precipitation behavior of Nb, Ti complex microalloyed steel produced by compact strip processing[J]. ISIJ International, 2006, 46(9): 1345-1353.
[21]Shen Y F, Wang C M, Sun X. A micro-alloyed ferritic steel strengthened by nanoscale precipitates[J]. Materials Science and Engineering A, 2011, 528(28): 8150-8156.
[22]Gladman T. Precipitation hardening in metals[J]. Materials Science and Technology, 1999, 15(1): 30-36.

控轧控冷对Ti-Mo-Nb复合微合金化低碳钢组织和力学性能的影响

Effect of TMCP on microstructure and mechanical properties of Ti-Mo-Nb microalloyed low carbon steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	王明明, 马飞, 裴未迟, 李冬冬, 龙海洋, 纪宏超, 刘帅. 汽车用高强塑积中锰钢的研究进展[J]. 金属热处理, 2022, 47(9): 272-280.
[2]	邹英, 刘华赛, 韩赟, 王朝斌, 王海全. 800 MPa级热基镀锌复相钢的开发[J]. 金属热处理, 2022, 47(2): 65-69.
[3]	代永娟, 武祥祥, 李佳坤, 国栋, 王波. 退火温度对Fe-24.38Mn-0.44C TWIP钢组织性能的影响[J]. 金属热处理, 2022, 47(2): 146-152.
[4]	何利军, 周龙, 汤淳坡, 郭小钢, 金晓, 赵彦芬, 薛飞, 张国栋. 长时服役后T92钢管的微观组织及力学性能变化[J]. 金属热处理, 2021, 46(7): 31-36.
[5]	权晨, 刘新宝, 朱麟, 李博, 王妮. 高铬耐热钢蠕变过程中的组织演化行为[J]. 金属热处理, 2021, 46(6): 135-145.
[6]	麻衡, 霍孝新, 吴红艳, 高秀华, 杜林秀. Q550D钒氮钢特厚板组织性能与表面质量[J]. 金属热处理, 2021, 46(4): 65-69.
[7]	石晓霞, 任慧平, 李晓, 王超, 宫鑫. 26CrMoVNbRE钢高效热处理调质工艺边界探索[J]. 金属热处理, 2021, 46(3): 39-45.
[8]	陆佳栋, 吴圣杰, 岳重祥, 李化龙. 二次退火温度对无取向硅钢组织和磁性能的影响[J]. 金属热处理, 2021, 46(3): 67-70.
[9]	朱飞, 罗小兵, 杨才福, 柴锋, 张正延. 时效温度对直接淬火Ni-Cr-Mo-V-Cu钢组织及性能的影响[J]. 金属热处理, 2021, 46(11): 54-63.
[10]	刘阳, 金自力, 任慧平, 汲霖. 加热温度对高Nb-Ti新能源汽车用无取向硅钢第二相固溶行为的影响[J]. 金属热处理, 2021, 46(10): 34-38.
[11]	王科强, 刘仁东, 郭金宇, 付薇, 黄秋菊, 孙荣生. 汽车用800 MPa级冷轧低合金高强钢的研制[J]. 金属热处理, 2021, 46(1): 120-124.
[12]	史文杰, 王春华. Al-6.8Zn-2.3Mg-2.0Cu-0.15Sc合金的高温回归再时效工艺[J]. 金属热处理, 2020, 45(7): 63-67.
[13]	麻立振, 卢广玺, 关绍康, 朱世杰, 祝庆. 第二相尺寸分布对AA8111铝箔针孔率的影响[J]. 金属热处理, 2020, 45(2): 161-165.
[14]	张欣, 金自力, 任慧平, 吴忠旺. 稀土Ce对含Cu低温取向硅钢铸态析出物的影响[J]. 金属热处理, 2020, 45(10): 135-139.
[15]	朱　敏，朱万全，帅林飞，马国强，吴桂林. 表面纳米化过程中18CrNiMo7-6钢的软化与硬化[J]. 金属热处理, 2019, 44(1): 152-156.