doi:10.13251/j.issn.0254-6051.2023.01.020

金属热处理 ›› 2023, Vol. 48 ›› Issue (1): 115-121.DOI: 10.13251/j.issn.0254-6051.2023.01.020

Mg-6Gd-1.2Y-0.53Zr合金的热变形行为及热加工图

胡剑凌¹, 朱华明², 严红革¹, 陈吉华¹, 夏伟军¹, 张蒙¹

1.湖南大学材料科学与工程学院, 湖南长沙 410082;
2.广州众山精密科技有限公司, 广东广州 511340

收稿日期:2022-08-15 修回日期:2022-11-16 出版日期:2023-01-25 发布日期:2023-02-03
通讯作者: 严红革,教授,E-mail:yanhg68@163.com
作者简介:胡剑凌(1996—),男,硕士研究生,主要研究方向为耐热镁合金成形工艺,E-mail:827953093@qq.com。

Hot deformation behavior and processing map of Mg-6Gd-1.2Y-0.53Zr alloy

Hu Jianling¹, Zhu Huaming², Yan Hongge¹, Chen Jihua¹, Xia Weijun¹, Zhang Meng¹

1. College of Materials Science and Engineering, Hunan University, Changsha Hunan 410082, China;
2. Trio Metal (GZ) Co., Ltd., Guangzhou Guangdong 511340, China

Received:2022-08-15 Revised:2022-11-16 Online:2023-01-25 Published:2023-02-03

摘要/Abstract

摘要： 采用热模拟试验法研究了变形温度(340~500 ℃)和应变速率(0.01~25 s^-1)对均匀化态Mg-6Gd-1.2Y-0.53Zr合金动态再结晶(DRX)临界应变及体积分数的影响,通过构建热加工图优化了其热加工工艺参数范围。结果表明,在0.01~1 s^-1的低应变速率下,该合金的动态再结晶(DRX)临界应变量随变形温度的升高而升高,而在10~25 s^-1高应变速率下,DRX临界应变量随变形温度的升高而略微下降。应变速率及变形温度的升高都使DRX体积分数增大,在500 ℃、25 s^-1条件下,合金的动态再结晶体积分数最高,达90.0%。根据构建的热加工图,当变形量在30%~80%之间时,较佳的热加工工艺区间为400~500 ℃、0.01~1 s^-1以及420~500 ℃、10~25 s^-1。在10~25 s^-1应变速率下,当变形量为10%~80%时,合金最适宜的变形温度为460~500 ℃。

关键词: Mg-6Gd-1.2Y-0.53Zr合金, 热变形, 临界应变, 热加工图

Abstract: Influence of deformation temperature (340-500 ℃) and strain rate (0.01-25 s^-1) on critical strain and volume fraction of dynamic recrystallization (DRX) of homogenized Mg-6Gd-1.2Y-0.53Zr alloy was studied by thermal simulation test. The range of hot processing parameters was optimized by constructing processing maps. The results show that the DRX critical strain increases with the increase of deformation temperature in the low strain-rate range of 0.01-1 s^-1, while it decreases slightly with the increase of deformation temperature in the high strain-rate range of 10-25 s^-1. The volume fraction of DRX increases with the increase of strain rate and deformation temperature. The dynamic recrystallization volume fraction is the highest and reaches 90.0% at 500 ℃, 25 s^-1. According to the constructed processing map, when the deformation is 30%-80%, the better hot processing range is 400-500 ℃, 0.01-1 s^-1 and 420-500 ℃, 10-25 s^-1. At the strain rate of 10-25 s^-1, when the deformation amount is 10%-80%, the most appropriate deformation temperature of the alloy is 460-500 ℃.

Key words: Mg-6Gd-1.2Y-0.53Zr alloy, hot deformation, critical strain, processing map

中图分类号:

TG146.2

胡剑凌, 朱华明, 严红革, 陈吉华, 夏伟军, 张蒙. Mg-6Gd-1.2Y-0.53Zr合金的热变形行为及热加工图[J]. 金属热处理, 2023, 48(1): 115-121.

Hu Jianling, Zhu Huaming, Yan Hongge, Chen Jihua, Xia Weijun, Zhang Meng. Hot deformation behavior and processing map of Mg-6Gd-1.2Y-0.53Zr alloy[J]. Heat Treatment of Metals, 2023, 48(1): 115-121.

参考文献

[1]陈振华, 严红革, 陈吉华, 等. 镁合金[M]. 北京: 化学工业出版社, 2004.
[2]Feng X H, Sun Y P, Lu Y W, et al. Effect of the strain rate on the damping and mechanical properties of a ZK60 magnesium alloy[J]. Materials, 2020, 13: 2969.
[3]Mo N, Tan Q Y, Bermingham M, et al. Current development of creep-resistant magnesium cast alloys: A review[J]. Materials and Design, 2018, 155: 422-442.
[4]Tekumalla S, Seetharaman S, Almajid A, et al. Mechanical properties of magnesium-rare earth alloy systems: A review[J]. Metals, 2015, 5: 1-39.
[5]Ruano O A, Alvarez-Leal M, Orozco-Caballero A, et al. Large elongations in WE54 magnesium alloy by solute-drag creep controlling the deformation behavior[J]. Materials Science and Engineering A, 2020, 791: 139757.
[6]Su X, Feng Z J, Li Y F, et al. Effect of pouring and mold temperatures on hot tearing susceptibility of WE43 magnesium alloy[J]. International Journal of Metalcasting, 2021, 2(15): 576-586.
[7]Ankur K, Khan M F, Kumar P S, et al. Microstructural evolution and corrosion behaviour of friction stir-processed QE22 magnesium alloy[J]. Corrosion Reviews, 2021, 39(4): 351-360.
[8]Liu J N, Bian D, Zheng Y F, et al. Comparative in vitro study on binary Mg-RE (Sc, Y, La, Ce, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu) alloy systems[J]. Acta Biomaterialia, 2020, 102: 508-528.
[9]Wu G H, Wang C L, Sun M, et al. Recent developments and applications on high-performance cast magnesium rare-earth alloys[J]. Journal of Magnesium and Alloys, 2021, 9: 1-20.
[10]Wang R, Dong J, Fan L K, et al. Microstructure and mechanical properties of rolled Mg-12Gd-3Y-0.4Zr alloy sheets[J]. Transactions of Nonferrous Metals Society of China, 2008, 18: 189-193.
[11]李德江. Mg-8Gd-3Y-0.5Zr合金的形变热处理组织与性能研究[D]. 上海: 上海交通大学, 2010.
Li Dejiang. Study on the microstructure and mechanical properties of Mg-8Gd-3Y-0.5Zr alloy processed by thermo-mechanical treatments[D]. Shanghai: Shanghai Jiao Tong University, 2010.
[12]Luo Q, Guo Y L, Liu B, et al. Thermodynamics and kinetics of phase transformation in rare earth-magnesium alloys: A critical review[J]. Journal of Materials Science and Technology, 2020, 44: 171-190.
[13]Zhou B P, Liu W C, Wu G H, et al. Microstructure and mechanical properties of sand-cast Mg-6Gd-3Y-0.5Zr alloy subject to thermal cycling treatment[J]. Journal of Materials Science and Technology, 2020, 43: 208-219.
[14]Zhou B, Wu D, Chen R S, et al. Enhanced tensile properties in a Mg-6Gd-3Y-0.5Zr alloy due to hot isostatic pressing (HIP)[J]. Journal of Materials Science and Technology, 2019, 35: 1860-1868.
[15]郑梁. Zn及变形工艺对Mg-6Gd-3Y-0.5Zr合金微观组织、织构及力学性能的影响[D]. 长沙: 中南大学, 2011.
Zhen Liang. Effects of Zn and deformation process on microstructure, texture and mechanical properties of Mg-6Gd-3Y-0.5Zr alloy[D]. Changsha: Central South University, 2011.
[16]谢艳才. Mg-10Gd-3Y-0.4Zr合金时效析出相的电子显微研究[D]. 上海: 上海交通大学, 2013.
Xie Yancai. Electron microscopy study of precipitates in Mg-10Gd-3Y-0.4Zr alloys[D]. Shanghai: Shanghai Jiao Tong University, 2013.
[17]Zhang Q, Li Q N, Chen X Y, et al. Dynamic precipitation and recrystallization mechanism during hot compression of Mg-Gd-Y-Zr alloy[J]. Journal of Materials Research and Technology, 2021, 15: 37-51.
[18]Zhou H, Wang Q D, Ye B, et al. Hot deformation and processing maps of as-extruded Mg-9.8Gd-2.7Y-0.4Zr Mg alloy[J]. Materials Science and Engineering A, 2013, 576: 101-107.
[19]Xiao H C, Tang B, Liu C M, et al. Dynamic precipitation in a Mg-Gd-Y-Zr alloy during hot compression[J]. Materials Science and Engineering A, 2015, 645: 241-247.
[20]Chao H Y, Sun H F, Wang E D. Working hardening behaviors of severely cold deformed and fine-grained AZ31 Mg alloys at room temperature[J]. Transactions of Nonferrous Metals Society of China, 2011, 21: 235-241.
[21]Del Valle J A, Carreno F, Ruano O A. Influence of texture and grain size on work hardening and ductility in magnesium-based alloys processed by ECAP and rolling[J]. Acta Materialia, 2006, 24(16): 4247-4259.
[22]Zhou Z H, Fan Q C, Xia Z H, et al. Constitutive relationship and hot processing maps of Mg-Gd-Y-Nb-Zr alloy[J]. Journal of Materials Science and Technology, 2017, 33: 637-644.

Mg-6Gd-1.2Y-0.53Zr合金的热变形行为及热加工图

Hot deformation behavior and processing map of Mg-6Gd-1.2Y-0.53Zr alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价

[1]	张铮, 陈进磊, 张敏, 乔珺威. 热变形对塑料模具钢SDFT600贝氏体相变的影响[J]. 金属热处理, 2022, 47(8): 1-6.
[2]	陈蕾蕾, 瞿宗宏, 王泽钰, 赖运金, 梁书锦. 热等静压态FGH96合金的热变形行为及热加工图[J]. 金属热处理, 2022, 47(7): 63-70.
[3]	周晓锋, 付文, 利成宁, 程方杰. Ti80钛合金两相区高温变形本构模型及热加工图[J]. 金属热处理, 2022, 47(5): 25-30.
[4]	李荣斌, 李博, 张志玺, 彭望君, 郭彦兵. X12CrMoWVNbN钢的热变形行为及热加工图[J]. 金属热处理, 2022, 47(5): 31-39.
[5]	舒玮, 宋丽强, 张威. 热变形对含铌奥氏体不锈钢07Cr18Ni11Nb再结晶行为的影响[J]. 金属热处理, 2022, 47(2): 59-64.
[6]	马宝霞, 乔洋, 毛明轩, 孙江辉, 吴昌桐, 刘泽瑀. 均匀化处理Al-Mg-Mn合金的组织及热变形行为[J]. 金属热处理, 2022, 47(11): 32-38.
[7]	任钰鹏, 刘平, 陈小红, 周洪雷, 梁晓飞. 新型Al-Mg-Si-RE合金的热变形行为[J]. 金属热处理, 2022, 47(11): 168-177.
[8]	邢晨, 程亮, 朱彬, 陈逸. 马氏体TiAl合金的热变形行为[J]. 金属热处理, 2022, 47(10): 58-64.
[9]	王英虎, 郑淮北, 宋令玺, 刘庭耀. 热变形工艺对铈-硫易切削不锈钢中硫化物形态演变的影响[J]. 金属热处理, 2022, 47(10): 99-106.
[10]	周宇森, 程晓农, 罗锐, 高佩, 刘瑜, 袁志钟. Inconel 600合金的微观组织及其热加工图[J]. 金属热处理, 2022, 47(10): 107-112.
[11]	何婵, 邹德宁, 赵洁, 陈兴润, 钱张信. 2507超级双相不锈钢的流变应力本构关系及热加工图[J]. 金属热处理, 2022, 47(1): 94-99.
[12]	郭利平, 何学清, 阳代军, 黄元春, 王强. Cu-0.5Cr-0.1Zr合金的热压缩变形行为[J]. 金属热处理, 2021, 46(9): 180-186.
[13]	廖雪峰, 张恒, 何学青, 黄元春, 李明. 不同Cr含量Cu-Cr-Zr合金的热拉伸变形行为[J]. 金属热处理, 2021, 46(9): 28-35.
[14]	吉光, 高秀华, 龙金花. 微合金元素Nb对高碳合金钢动态再结晶行为的影响[J]. 金属热处理, 2021, 46(8): 26-29.
[15]	潘龙博, 储滔, 张硕, 江济, 程采金, 谢庆忠, 邢学强, 斯庭智. 30CrNi3MoV钢动态再结晶行为及其模型的构建[J]. 金属热处理, 2021, 46(7): 23-30.