R350HT钢轨钢的连续冷却转变曲线

doi:10.13251/j.issn.0254-6051.2022.09.027

金属热处理 ›› 2022, Vol. 47 ›› Issue (9): 153-157.DOI: 10.13251/j.issn.0254-6051.2022.09.027

R350HT钢轨钢的连续冷却转变曲线

王瑞敏^1,2,3, 刘曼^1,2, 周剑华³, 张琪^1,2, 苏雪^1,2, 徐光^1,2

1.武汉科技大学省部共建耐火材料与冶金国家重点实验室, 湖北武汉 430081;
2.武汉科技大学钢铁冶金与资源利用省部共建教育部重点实验室, 湖北武汉 430081;
3.宝钢股份中央研究院武汉分院, 湖北武汉 430080

收稿日期:2022-04-09 修回日期:2022-07-08 发布日期:2022-10-18
通讯作者: 徐光,教授,博士,E-mail: xuguang@wust.edu.cn
作者简介:王瑞敏(1987—),男,博士研究生,主要研究方向为金属轧制等,E-mail: wangrm@baosteel.com。
基金资助:
湖北省技术创新专项重大项目(2017AAA116)

Continuous cooling transformation curve of R350HT rail steel

Wang Ruimin^1,2,3, Liu Man^1,2, Zhou Jianhua³, Zhang Qi^1,2, Su Xue^1,2, Xu Guang^1,2

1. The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology, Wuhan Hubei 430081, China;
2. Key Laboratory for Ferrous Metallurgy and Resources Utilization of Ministry of Education, Wuhan University of Science and Technology, Wuhan Hubei 430081, China;
3. Wuhan Branch, Baosteel Central Research Institute, Wuhan Hubei 430080, China

Received:2022-04-09 Revised:2022-07-08 Published:2022-10-18

摘要/Abstract

摘要： 在Gleeble-3500热模拟试验机上对欧标R350HT钢轨钢进行不同冷却速度的热模拟试验,观察显微组织并测量硬度,绘制试验钢的连续冷却转变(CCT)曲线。结果表明,在冷却速率为0.5~2.5 ℃/s时,组织以珠光体为主,有少量先共析铁素体。当冷却速度为3 ℃/s时,组织中出现马氏体。由于珠光体轨钢中不允许有马氏体组织,因此冷却速度应小于3 ℃/s。同时,随着冷却速率的增大,直至10 ℃/s,珠光体开始转变温度降低,这是因为随着冷却速率的增大,在高温区停留时间缩短,珠光体转变来不及发生,并且发生珠光体相变需要较大的过冷度。随着冷却速率增加至20 ℃/s,组织基本上为马氏体。当冷速大于20 ℃/s后,组织为单一马氏体。因此,马氏体临界转变冷速为20 ℃/s。

关键词: R350HT钢轨钢, 连续冷却转变曲线, 热模拟, 组织

Abstract: Thermal simulation test of European standard R350HT rail steel with different cooling rates was carried out on the Gleeble-3500 thermal simulation testing machine. The microstructure was observed, the hardness was measured, and the continuous cooling transformation (CCT) curves of the tested steel was drawn. The results show that when the cooling rate is between 0.5-2.5 ℃/s, the microstructure consists of pearlite and a small amount of proeutectoid ferrite. When the cooling rate is 3 ℃/s, martensite appears in the structure. Since the pearlite rail steel should not contain martensite, the cooling rate of the tested steel should be less than 3 ℃/s. At the same time, with the increase of cooling rate until 10 ℃/s, the pearlite transformation start temperature decreases, which is because the residence time in the high temperature region is shortened with the increase of the cooling rate, and the pearlite transformation is too late to occur, and the pearlite transformation requires a large degree of undercooling. In addition, with the cooling rate increasing to 20 ℃/s, the microstructure is basically composed of martensite. When the cooling rate is greater than 20 ℃/s, the microstructure only contains martensite. Hence, the critical cooling rate of martensite transformation is 20 ℃/s.

Key words: R350HT rail steel, continuous cooling transformation curves, thermal simulation, microstructure

中图分类号:

TG142.1

王瑞敏, 刘曼, 周剑华, 张琪, 苏雪, 徐光. R350HT钢轨钢的连续冷却转变曲线[J]. 金属热处理, 2022, 47(9): 153-157.

Wang Ruimin, Liu Man, Zhou Jianhua, Zhang Qi, Su Xue, Xu Guang. Continuous cooling transformation curve of R350HT rail steel[J]. Heat Treatment of Metals, 2022, 47(9): 153-157.

[1]	高星, 张宁, 丁燕, 蒋波. 热处理时间对激光选区成形TC4钛合金组织及力学性能的影响[J]. 金属热处理, 2022, 47(9): 12-17.
[2]	林凌峰, 袁鸽成, 杨濂, 丁灿培. 平均道次压下率对异步轧制-固溶6016铝合金板材显微组织的影响[J]. 金属热处理, 2022, 47(9): 36-40.
[3]	王璐, 王峰, 张明伟, 刘瑞, 傅正元, 刘景顺. 退火工艺对Ti-4Al-2V合金组织及耐蚀性能的影响[J]. 金属热处理, 2022, 47(9): 41-46.
[4]	潘冉, 刘宝胜, 曾元松, 曲海涛, 王东, 慕延宏. 深冷处理对15%SiC_p/2009铝基复合材料组织与力学性能的影响[J]. 金属热处理, 2022, 47(9): 65-70.
[5]	张浩泽, 王隽生, 宫鹏辉, 詹海艺, 王凯. 热处理对EB铸锭直接轧制TC4合金板材组织和力学性能的影响[J]. 金属热处理, 2022, 47(9): 71-78.
[6]	钟立伟, 冯朝辉, 高文理, 陈军洲, 陆政. 多轴锻造与T852热处理对Al-Cu-Li合金组织及力学性能的影响[J]. 金属热处理, 2022, 47(9): 79-86.
[7]	季德静, 杨维宇, 白雅琼. 高强韧工程机械用钢Q690D的淬火工艺优化[J]. 金属热处理, 2022, 47(9): 108-112.
[8]	温方明, 郝晓博, 曹恒, 张强, 李渤渤, 刘茵琪. 热处理工艺对N06600合金热轧板组织与性能的影响[J]. 金属热处理, 2022, 47(9): 113-118.
[9]	艾兵权, 邝霜, 田秀刚, 杨峰, 王玉慧, 逯志强, 王朝, 郝雷. 均热温度对不同成分980 MPa级高强钢组织和性能的影响[J]. 金属热处理, 2022, 47(9): 119-124.
[10]	王世凯, 王睿, 康燕, 于志强, 闫志杰. 淬火温度对Cr5MoVNi钢组织和性能的影响[J]. 金属热处理, 2022, 47(9): 125-129.
[11]	熊维亮, 梁文, 吴腾, 梁亮, 吴浩鸿. 控冷工艺对热轧双相钢组织与性能的影响[J]. 金属热处理, 2022, 47(9): 130-133.
[12]	范朝, 程宗辉, 张志强. 激光热输入对激光增材修复1Cr17Ni2不锈钢组织与力学性能的影响[J]. 金属热处理, 2022, 47(9): 140-145.
[13]	李敬, 刘辰, 杨跃辉, 苑少强, 艾晨光. 厚规格Q690D高强钢板的连续冷却转变行为[J]. 金属热处理, 2022, 47(9): 171-174.
[14]	骆艳萍, 汪家晗, 李沐泽, 张云祥, 周建勋, 赵志恒. HRB400E抗震螺纹钢静态CCT曲线测定及组织分析[J]. 金属热处理, 2022, 47(9): 188-193.
[15]	田伟, 潘伟, 钟庆元. 0Cr16Ni5Mo马氏体不锈钢δ-铁素体含量及奥氏体晶粒度的控制[J]. 金属热处理, 2022, 47(9): 194-201.

R350HT钢轨钢的连续冷却转变曲线

Continuous cooling transformation curve of R350HT rail steel

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价