高磁感取向硅钢轧制及热处理过程中的晶界和织构演化

doi:10.13251/j.issn.0254-6051.2021.12.033

摘要/Abstract

摘要： 采用电子背散射衍射(EBSD)对不同轧制和热处理态的高磁感取向硅钢的重合位置点阵(CSL)晶界和织构进行了研究。结果表明,热轧态取向硅钢截面织构呈层状分布,表层主要为{110}<001>Goss织构,1/4厚度主要为{001}<110>立方织构、{112}<111>铜型织构和{110}<001>Goss织构,而心部则形成较强的{112}<111>铜型织构、{111}<110>形变织构和{110}<001>Goss织构;常化处理后截面织构梯度变化不明显,但中心位置{112}<111>织构向{110}<001>Goss织构转变。冷轧退火态主要织构为{110}<001>Goss织构、{112}<111>织构和{111}<110>形变织构。二次再结晶后,则生成强烈的{110}<001>Goss织构。随着织构的变化,CSL晶界也发生了明显的转变。热轧态CSL重位晶界中∑3~∑29均有出现,但比例较低;常化处理后CSL重位晶界比例增加,冷轧退火后CSL晶界比例大幅提高,特别是∑3、∑7、∑9和∑15等晶界;二次再结晶后,由于CSL晶界发生了转化,CSL晶界类型减少,∑3、∑13等晶界比例增加,∑9晶界消失。

关键词: 高磁感取向硅钢, Goss织构, CSL晶界, 二次再结晶

Abstract: Coincident site lattice (CSL) boundary and texture of a high magnetic grain-oriented silicon steel in different rolled and heat treatment states were studied by means of electron backscatter diffraction (EBSD). The results show that the cross-section texture of hot-rolled oriented silicon steel is distributed in layers, the surface layer of which is mainly {110}<001> Goss texture, and the quarter of the thickness is mainly {001}<110> cubic texture, {112}<111> copper type texture and {110}<001> Goss texture, while the core forms strong {112}<111> copper type texture, {111}<110> deformation texture and {110}<001> Goss texture. After normalizing, the cross-sectional texture gradient is not obviously changed, but the {112}<111> texture at the center position changes to {110}<001> Goss texture. The texture components are {110}<001> Goss texture, {112}<111> texture and {111}<110> deformation texture in the cold rolled and annealed state steel. After secondary recrystallization, a strong {110}<001> Goss texture is produced. With the change of texture, the CSL grain boundary undergoes a significant transformation. ∑3-∑29 appear in the CSL boundaries in the hot-rolled state, with low proportions. The proportion of CSL grain boundary increases after normalizing. The proportion of CSL boundary increases greatly in the cold rolled and annealed state, especially ∑3, ∑7, ∑9 and ∑15 boundaries. Due to the transformation of CSL boundaries, the type of CSL boundary reduces during second recrystallization, while the proportions of ∑3, ∑13 and other grain boundaries increase, but the ∑9 grain boundary disappears.

Key words: high magnetic grain-oriented silicon steel, Goss texture, CSL boundary, secondary recrystallization

中图分类号:

TG142.1

喻春明, 张继明, 党波, 张毅. 高磁感取向硅钢轧制及热处理过程中的晶界和织构演化[J]. 金属热处理, 2021, 46(12): 204-208.

Yu Chunming, Zhang Jiming, Dang Bo, Zhang Yi. Grain boundary and texture evolution of a high magnetic grain-oriented silicon steel during rolling and heat treatment[J]. Heat Treatment of Metals, 2021, 46(12): 204-208.

参考文献

[1]Goss N P. New development in electrical strip steels characterized by fine grain structure approaching the properties of a single crystal[J]. Transactions of American Society for Metals, 1935, 23(1): 511-544.
[2]何忠治, 赵宇, 罗海文. 电工钢[M]. 北京: 冶金工业出版社, 2012.
[3]王玉峰, 金自立, 任慧平, 等. 冷轧无取向硅钢再结晶退火过程的EBSD分析[J]. 电子显微学报, 2009, 28(1): 39-42.
Wang Yufeng, Jin Zili, Ren Huiping, et al. EBSD investigation of cold-rolled non-oriented silicon steel in recrystallization annealing process[J]. Journal of Chinese Electron Microscopy Society, 2009, 28(1): 39-42.
[4]李杰, 王凯琳, 宁江利, 等. 热轧工艺对含铌取向硅钢二次冷轧中织构的影响[J]. 金属热处理, 2018, 43(2): 137-143.
Li Jie, Wang Kailin, Ning Jiangli, et al. Effect of hot rolling process on texture of Nb-contained grain-oriented silicon steel after double cold rolling [J]. Heat Treatment of Metals, 2018, 43(2):137-143.
[5]李洋, 冯运莉, 王凯琳, 等.含铌低温取向硅钢热轧板及常化板的织构演变[J]. 金属热处理, 2018, 43(5): 6-10.
Li Yang, Feng Yunli, Wang Kailin, et al. Textures evolution of hot rolled plate and normalized plate of Nb-containing low temperature grain-oriented silicon steel [J]. Heat Treatment of Metals, 2018, 43(5): 6-10.
[6]唐超平, 吴隽, 詹东方, 等. 一次再结晶取向硅钢中第二相粒子局部密度与晶界的关系[J]. 材料热处理学报, 2018, 39(6): 76-82.
Tang Chaoping, Wu Jun, Zhan Dongfang, et al. Relationship between local densities of second-phase particles and corresponding grain boundary in primary recrystallized grain-oriented silicon steel[J]. Transactions of Materials and Heat Treatment, 2018, 39(6): 76-82.
[7]王玥瑶, 李杰, 冯运莉, 等. 热轧工艺对含铌取向硅钢一次冷轧织构的影响[J]. 金属热处理, 2017, 42(11): 39-44.
Wang Yueyao, Li Jie, Feng Yunli, et al. Effect of hot rolling process on texture of Nb-contained grain-oriented silicon steel after single cold rolling[J]. Heat Treatment of Metals, 2017, 42(11): 39-44.
[8]Yashiki H, Kaneko T. Effects of Mn and S on the grain growth and texture in cold rolled 0.5%Si steel[J]. ISIJ International, 1990, 30(4): 325-330.
[9]付勇军, 蒋奇武, 金文旭, 等. 取向硅钢高温退火样品晶粒尺寸、取向及磁性能关系的研究[J]. 电子显微学报, 2010, 29(1): 704-708.
Fu Yongjun, Jiang Qiwu, Jin Wenxu, et al. Influences of grain sizes and grain orientations in secondarily recrystallized samples on the magnetic properties of grain oriented steels[J]. Journal of Chinese Electron Microscopy Society, 2010, 29(1): 704-708.
[10]Kumano T, Haratani T, Ushigami Y. The improvement of primary texture for sharp Goss orientation on grain oriented silicon steel[J]. ISIJ International, 2003, 43(5): 736-745.
[11]黄孝瑛, 刘宗滨, 陈佩兰. 取向硅钢常化处理微观结构的TEM研究[J]. 电子显微学报, 1990(3): 204.
[12]Heo N H, Kim S B, Choi Y S, et al. Interfacial segregation, nucleation and texture development in 3% silicon steel[J]. Acta Materialia, 2003, 51(17): 4953-4964.
[13]Park J Y, Oh K H, Ra H Y. Texture and deformation behavior through thickness direction in strip-cast 4.5wt%Si steel sheet[J]. ISIJ International, 2000, 40(12): 1210-1215.
[14]Matsuo Munetsugu. Texture control in the production of grain oriented grain silicon steels[J]. Transactions of the Iron & Steel Institute of Japan, 1989, 29(10): 809-827.
[15]Yoshiyuki U, Takeshi K, Nobuyuki T. Mechanism of orientation selectivity of secondary recrystallization in Fe-3%Si alloy[J]. ISIJ International, 1998, 38(6): 553-558.
[16]Wang Y P, Liu H T, Song H Y, et al. Ultra-thin grain-oriented silicon steel sheet fabricated by a novel way: Twin-roll strip casting and two-stage cold rolling[J]. Journal of Magnetism and Magnetic Materials, 2018, 452: 288-296.
[17]Homma H, Hutchinson B. Oriention dependence of secondary recrystallization in silicon-iron[J]. Acta Materialia, 2003, 51(13): 3795-3805.
[18]Kumano T, Haratani T, Ushigami Y. Influence of primary recrystallization texture through thickness to secondary texture on grain oriented silicon steel[J]. ISIJ International, 2003, 43(3): 400-409.
[19]Kumano T, Haratani T, Ushigami Y. The relationship between primary and secondary recrystallization texture of grain oriented silicon steel[J]. ISIJ International, 2002, 42(4): 440-448.
[20]Kumano T, Haratani T, Ushigami Y. Grain boundary characteristics in grain oriented silicon steel[J]. ISIJ International, 2004, 44(11): 1888-1893.
[21]Rajmohan N, Szpunar J A, Hayakawa Y. Importance of fractions of highly mobile boundaries in abnormal growth of Goss grains[J]. Materials Science and Engineering A, 1999, 259(1): 8-16.
[22]Hayakawa Y, Muraki M, Szpunar J A. The changes of grain boundary character distribution during the secondary recrystallization of electrical steel[J]. Acta Metallurgica et Materialia, 1998, 46(3): 1063-1073.
[23]Lee K T, Szpunar J A, The role of special grain boundaries during the grain growth in Fe-3%Si[J]. Canadian Metallurgical Quarterly, 1995, 34(3): 257-263.
[24]Shimizu R, Harase J, Dingley D J. Prediction of secondary recrystallization texture in Fe-3%Si by three-dimension texture analysis[J]. Acta Metallurgica et Materialia, 1990, 38(6): 973-978.
[25]Liu G T, Liu Z Q, Yang P, et al. Correlation between primary and secondary recrystallization texture components in low-temperature reheated grain-oriented silicon steel[J]. Journal of Iron and Steel Research(International), 2016, 23(11): 1234-1242.
[26]Constantin G, Ana D. Evolution of texture in gain oriented silicon steels[J]. Journal of Iron and Steel Research(International), 2009, 16(4): 78-83.
[27]Yoshitomi Y, Iwayama K, Nagashima T, et al. Coincidence grain boundary and role of inhibitor for secondary recrystallization in Fe-3%Si alloy[J]. Acta Metallurgica et Materialia, 1993, 41(5): 1577-1585.
[28]Harase J, Shimizu R. Coincidence grain boundary and (100)[011]secondary recrystallization in Fe-3%Si[J]. Acta Metallurgica et Materialia, 1992, 40(5): 1101-1111.