热处理工艺对Ti80钛合金棒材组织与性能的影响

doi:10.13251/j.issn.0254-6051.2021.09.026

摘要/Abstract

摘要： 研究了几种不同热处理工艺对Ti80钛合金棒材显微组织和室温力学性能的影响。结果表明:随着热处理温度的升高,显微组织由等轴组织变为魏氏组织;后期需要进行塑性成形时,适宜选择850 ℃保温80 min后空冷的工艺后热处理;经750 ℃保温80 min后空冷的热处理工艺,Ti80钛合金棒材的强度与塑性匹配较好。

关键词: Ti80钛合金, 热处理工艺, 显微组织, 力学性能

Abstract: Effects of different heat treatment process on microstructure and room temperature mechanical properties of the Ti80 titanium alloy bars were studied. The results show that with the increase of heat treatment temperature, the microstructure of the Ti80 titanium alloy changes from equiaxed structure to widmanstatite structure. When plastic forming is required in the later period, it is appropriate to choose the heat treatment process of air-cooling after heating at 850 ℃ for 80 min. After the heat treatment process of heating at 750 ℃ for 80 min and then air-cooling, the strength and plasticity of the Ti80 titanium alloy bars match well.

Key words: Ti80 titanium alloy, heat treatment, microstructure, mechanical properties

中图分类号:

TG156.2⁺1

华瑶. 热处理工艺对Ti80钛合金棒材组织与性能的影响[J]. 金属热处理, 2021, 46(9): 146-148.

Hua Yao. Effect of heat treatment on microstructure and properties of Ti80 titanium alloy bars[J]. Heat Treatment of Metals, 2021, 46(9): 146-148.

参考文献

[1]马济民, 贺金宇, 庞克昌, 等. 钛铸锭和钛锻造[M]. 北京: 冶金工业出版社, 2012.
[2]罗锦华, 朱燕丽, 孙小平, 等. 热加工及热处理工艺对Ti80合金棒材组织和性能的影响[J]. 钛工业进展, 2016, 33(2): 20-24.
Luo Jinhua, Zhu Yanli, Sun Xiaoping, et al. Effects of hot working process and heat treatment on microstructures and mechanical properties of Ti80 alloy bars[J]. Titanium Industry Progress, 2016, 33(2): 20-24.
[3]侯鹏, 李进元, 李维, 等. 热处理工艺对Ti80合金棒材组织与性能的影响[J]. 机械工程与自动化, 2013(2): 107-108, 111.
Hou Peng, Li Jinyuan, Li Wei, et al. Effect of heat treatment process on structure and properties of Ti80 alloy bars[J]. Mechanical Engineering and Automation, 2013(2): 107-108, 111.
[4]李梁, 孙建科, 孟祥军, 等. 通过热循环变形改善Ti80合金的超塑性[J]. 材料开发与应用, 2005, 20(6): 1-3, 8.
Li Liang, Sun Jianke, Meng Xiangjun, et al. Improvement of superplasticity of Ti80 alloy through thermal cycling deformation[J]. Development and Application of Materials, 2005, 20(6): 1-3, 8.
[5]袁满, 曹如玉, 张亚娟, 等. Ti80钛合金相变点的测定[J]. 热加工工艺, 2013, 42(14): 57-59, 92.
Yuan Man, Cao Yuru, Zhang Yajuan, et al. Measurement for phase transformation point of Ti80 alloy[J]. Hot Working Technology, 2013, 42(14): 57-59, 92.
[6]蒋鹏, 孟宪亮, 刘茵琪, 等. Ti80合金锻造工艺对显微组织和性能的影响[J]. 稀有金属材料与工程, 2005, 34(S3): 286-288.
Jiang Peng, Meng Xianliang, Liu Yinqi, et al. Effects of forge technology on microstructure and mechanical properties of Ti80 alloy[J]. Rare Metal Materials and Engineering, 2005, 34(S3): 286-288.
[7]王巧莉, 代春, 成小丽, 等. Ti80钛合金退火温度对挤压管材组织与性能的影响[J]. 中国钛业, 2012(3): 32-34.
Wang Qiaoli, Dai Chun, Cheng Xiaoli, et al. Effect of annealing process on microstructure and properties of Ti80 alloy tube produced by extruding[J]. China Titanium Industry, 2012(3): 32-34.
[8]马凡蛟, 杜予晅, 陈海生, 等. 退火工艺对Ti80合金组织与性能的影响[J]. 金属热处理, 2012, 37(4): 88-91.
Ma Fanjiao, Du Yuxuan, Chen Haisheng, et al. Effect of annealing process on microstructure and properties of Ti80 alloy[J]. Heat Treatment of Metals, 2012, 37(4): 88-91.
[9]王松茂, 白新房, 王辉, 等. Ti-80钛合金冲击韧性及力学性能异常原因探析[J]. 西安文理学院学报(自然科学版), 2013, 16(3): 84-87.
Wang Songmao, Bai Xinfang, Wang Hui, et al. On the abnormality of titanium alloy Ti-80's impact toughness and mechanical properties[J]. Journal of Xi'an University of Arts and Science(Natural Science Edition), 2013, 16(3): 84-87.
[10]王安东, 张禄祥, 陈彩凤, 等. 固溶时效处理对Ti-5322钛合金组织与性能的影响[J]. 金属热处理, 2020, 45(12): 24-28.
Wang Andong, Zhang Luxiang, Chen Caifeng, et al. Effect of solution and aging treatment on microstructure and tensile properties of Ti-5322 alloy[J]. Heat Treatment of Metals, 2020, 45(12): 24-28.
[11]杨洋, 锁红波, 陈哲源, 等. 固溶温度对电子束熔丝成形TC17合金组织与性能的影响[J]. 金属热处理, 2016, 41(9): 141-144.
Yang Yang, Suo Hongbo, Chen Zheyuan, et al. Effect of solution temperature on microstructure and mechanical properties of TC17 alloy fabricated by electron beam wire deposition[J]. Heat Treatment of Metals, 2016, 41(9): 141-144.
[12]包春玲, 马栓柱, 杨海涛, 等. 热处理温度对等轴初晶TC4钛合金组织及性能的影响[J]. 铸造, 2012, 61(8): 922-924.
Bao Chunling, Ma Shuanzhu, Yang Haitao, et al. Effects of heat treatment temperature on microstructure and properties of TC4 titanium alloy with equiaxed primary microstructure[J]. China Foundry, 2012, 61(8): 922-924.
[13]张宝昌. 有色金属及其热处理[M]. 西安: 西北工业大学出版社, 1993.
[14]杨柳, 代广霖, 王莹, 等. 退火工艺对TC4钛合金板材组织和性能的影响[J]. 金属热处理, 2020, 45(1): 122-125.
Yang Liu, Dai Guanglin, Wang Ying, et al. Effect of annealing process on microstructure and properties of TC4 alloy sheet[J]. Heat Treatment of Metals, 2020, 45(1): 122-125.

[1]	张子延, 陈君, 陈晓亚, 李全安, 刘建鑫. 固溶时效处理对Mg-4Sm-3Gd-0.5Zr合金显微组织和耐蚀性能的影响[J]. 金属热处理, 2022, 47(4): 10-16.
[2]	梁恩溥, 徐乐, 杨勇, 王毛球. 添加Al、Cu对40CrNi3MoV钢组织和力学性能的影响[J]. 金属热处理, 2022, 47(4): 17-23.
[3]	祁晓亮, 李岩, 定巍, 赵增武. 含Al中锰TRIP钢原始组织对临界退火后组织与力学性能的影响[J]. 金属热处理, 2022, 47(4): 24-29.
[4]	陈保安, 张静媛, 祝志祥, 韩钰, 潘学东, 张磊, 陈素红. 化学成分对高强Al-Mg-Si合金组织和性能的影响[J]. 金属热处理, 2022, 47(4): 30-38.
[5]	陈连生, 张露友, 田亚强, 杨子旋, 李红斌, 潘红波, 魏英立. 低碳高强舰船用钢的CCT曲线及其组织性能[J]. 金属热处理, 2022, 47(4): 63-68.
[6]	王云龙, 余伟, 张昳, 史佳新, 李明辉. 奥氏体化温度对贝氏体钢等温转变及力学性能的影响[J]. 金属热处理, 2022, 47(4): 80-85.
[7]	骆再斌, 范子泽, 彭振. 轻质高熵合金的研究进展[J]. 金属热处理, 2022, 47(4): 100-107.
[8]	吕杰晟, 宋志刚, 何建国, 丰涵, 郑文杰, 朱玉亮. S32205双相不锈钢冷轧退火组织转变及强塑化机理分析[J]. 金属热处理, 2022, 47(4): 141-145.
[9]	王琪, 吴光亮. 回火温度对1100 MPa级高强钢组织与性能的影响[J]. 金属热处理, 2022, 47(4): 146-150.
[10]	孙凯, 陈研, 杨绍斌. 时效温度对激光选区熔化TC21钛合金微观组织及硬度的影响[J]. 金属热处理, 2022, 47(4): 155-158.
[11]	张骥俊, 邢彦锋, 曹菊勇. 超声振动对CMT电弧增材制造铝合金组织与性能的影响[J]. 金属热处理, 2022, 47(4): 159-164.
[12]	刘文彬, 乔龙阳, 潘新宇, 程格, 李爱娜, 裴新军. 淬火温度对刀剪用M390粉末冶金不锈钢组织和性能的影响[J]. 金属热处理, 2022, 47(4): 189-195.
[13]	王瑞琴, 葛鹏, 廖强, 侯鹏, 刘宇. 固溶冷却方式对短时用高温钛合金板材组织和性能的影响[J]. 金属热处理, 2022, 47(4): 196-198.
[14]	王绍灼, 孟晗, 王芬, 樊海卫, 李燕, 唐超. 改善低氧TC4-LC及重熔TC4钛合金性能的热处理工艺[J]. 金属热处理, 2022, 47(4): 204-207.
[15]	陈强, 陈林芳, 杨明华. 18CrNiMo7-6钢的可控气氛高温渗碳工艺[J]. 金属热处理, 2022, 47(4): 231-239.