Cracking analysis of 8418 steel barrel used for aluminum-melting

[1]

Li Tianfu, Qu Shen, Dong Chen, Zhang Zhefeng. Failure analysis on spindle bearing of numerical control machine tool [J]. Heat Treatment of Metals, 2022, 47(4): 258-262.

[2]

Nie Xiaolong, Gao Jiaqiang, Meng Kairen, Wang Junyi, Liu Xinkuan. Fracture failure analysis of 60Si2Mn spring steel [J]. Heat Treatment of Metals, 2021, 46(8): 246-249.

[3]

Gao Zhiyu, He Wei, Jing Xiukun, Fan Xianjin, Wang Yingxin, Bai Jiang, Wang Daliang. Failure analysis and heat treatment process optimization of Cr12MoV steel blanking die [J]. Heat Treatment of Metals, 2021, 46(3): 206-212.

[4]

Li Jiahua, Li Ping, Sun Song, Xie Hui, Zeng Yin. Fracture failure analysis of stainless steel tie rod joint [J]. Heat Treatment of Metals, 2021, 46(3): 218-222.

[5]

Yu Haihua, Yan Haiyan, Zhang Jingtong, Wang Yukui, Huang Zhiyong, Wu Jianxin, Wei Zhenwei. Failure analysis of 30CrMnSiA steel countersunk bolt [J]. Heat Treatment of Metals, 2021, 46(3): 223-228.

[6]

Cheng Yuan, Hu Fangzhong, Hu Naiyue, Wang Kaizhong, Wang Lianglin, Jin Guozhong, Hao Zhenyu. Failure analysis of driving bevel gear of heavy truck rear axle [J]. Heat Treatment of Metals, 2021, 46(2): 218-222.

[7]

Meng Xinpei, Jin Linkui, Lin Quan, Huang Yihao, Fang Manting, Li Xiaohui, He Ping. Failure analysis of pitting on working surface of die-casting mold made of 8407 steel [J]. Heat Treatment of Metals, 2021, 46(12): 289-293.

[8]

Kang Zhenwei, Zhou Genshu, Liu Lijun, Zhang Xiaoke, Wang Mengjie. Failure analysis of compressor impeller blade made of 17-4PH stainless steel [J]. Heat Treatment of Metals, 2021, 46(11): 254-257.

[9]

He Liangliang, Wang Yuandong, Wang Mengmeng, Hou Shengwen, Wang Yan. Failure analysis of gear fracture cracking during bench test [J]. Heat Treatment of Metals, 2021, 46(1): 235-238.

[10]

Liu Jingfu, Zhou Xiangchun, Qu Yingdong. Research progress of stress corrosion cracking (SCC) of Al-Zn-Mg alloy [J]. Heat Treatment of Metals, 2020, 45(9): 21-28.

[11]

Jiang Qingbin, Zhang Zuozhi, Zhu Zhengwei, Zhou Yunjie. Failure analysis and improvement measures of quenched and tempered crack on42CrMoA steel pin shaft [J]. Heat Treatment of Metals, 2020, 45(9): 244-247.

[12]

Cong Jianchen, Yu Xiaodong, Ma Mingzhu, Wu Yongchen, Zhang Huadong. Failure cause analysis of crankshaft blank in cold straightening process [J]. Heat Treatment of Metals, 2020, 45(7): 224-227.

[13]

Pan Shumin, Wang Xiaohai, Liu Guoqiang, Xiang Hongyan, Yu Dawei, Yu Qingfeng. Fracture failure analysis on shaft of torque gauge in heavy duty vehicles [J]. Heat Treatment of Metals, 2020, 45(5): 257-261.

[14]

Liu Yanmei, Zhao Meilan, Feng Hui, Bai Yaru, Li Yan, Wang Tiegang. Failure analysis on cracking of die-forged connecting rod of 7A09 alloy [J]. HTM, 2020, 45(1): 234-238.

[15]

Long Yan, Kuang Xianren, Liu Wenhong, Ding Han, Lin Kai. Fracture reason analysis of well-logging stainless steel wire in a western oilfield [J]. HTM, 2016, 41(8): 192-196.

PDF