Aging embrittlement of F12 steel after long-term high temperature running

doi:10.13251/j.issn.0254-6051.2015.06.014

HTM

Previous Articles Next Articles

Aging embrittlement of F12 steel after long-term high temperature running

1. State Grid Shandong Electric Power Research Institute; 2. Huadian Zouxian Electric Power Co., Ltd.

Online:2015-06-25 Published:2015-07-02

Abstract

CLC Number:

TG142.1

Zhang Zhongwen1, Li Xinmei1, Du Baoshuai1, Zhang Duqing1, Wei Yuzhong2. Aging embrittlement of F12 steel after long-term high temperature running[J]. HTM, doi: 10.13251/j.issn.0254-6051.2015.06.014.

[1]	Han Shaoqiang, Zhao Jiqing, Wan Rundong, Yang Gang. Effect of microstructure on long-term aging stability of 2.25Cr-1Mo steel [J]. HTM, 2020, 45(2): 11-18.
[2]	Ju Guangyu. Characterization of embrittlement behavior and leakage prevention measures for HR3C steel pipe in high temperature service [J]. Heat Treatment of Metals, 2020, 45(11): 26-31.
[3]	Wang Shuo, Liu Guangxing, Tan Shuping. High temperature aging embrittlement of austenitic heat resistant steel Tempaloy A-3 [J]. HTM, 2015, 40(9): 79-83.
[4]	Du Baoshuai1, Liu Rui 2, Zhang Zhongwen 1, Li Xinmei1. Microstructure and properties of HR3C steel weld joint exposed to elevated temperature for long-term [J]. HTM, 2015, 40(2): 52-55.

Aging embrittlement of F12 steel after long-term high temperature running

PDF

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 4

Recommended Articles

Metrics

Comments