固溶工艺对7C04铝合金组织与性能的影响

doi:10.13251/j.issn.0254-6051.2025.03.021

金属热处理 ›› 2025, Vol. 50 ›› Issue (3): 132-137.DOI: 10.13251/j.issn.0254-6051.2025.03.021

固溶工艺对7C04铝合金组织与性能的影响

郭旭东¹, 邹仕军², 卢影峰³, 龙泽熙¹

1.东北大学材料科学与工程学院, 辽宁沈阳 110819;
2.空军装备部驻沈阳地区军事代表局驻沈阳地区第一军事代表室, 辽宁沈阳 110850;
3.沈阳飞机工业(集团)有限公司, 辽宁沈阳 110850

收稿日期:2024-10-17 修回日期:2025-01-06 出版日期:2025-03-25 发布日期:2025-05-14
作者简介:郭旭东(1997—),男,硕士研究生,主要研究方向为铝合金热处理,E-mail:773744509@qq.com

Effect of solution treatment process on microstructure and properties of 7C04 aluminum alloy

Guo Xudong¹, Zou Shijun², Lu Yingfeng³, Long Zexi¹

1. School of Materials Science and Engineering, Northeastern University, Shenyang Liaoning 110819, China;
2. The First Military Representative Office of the Shenyang Regional Military Representative Bureau of the Air Force Armament Department, Shenyang Liaoning 110850, China;
3. Shenyang Aircraft Industry Group Co., Ltd., Shenyang Liaoning 110850, China

Received:2024-10-17 Revised:2025-01-06 Online:2025-03-25 Published:2025-05-14

摘要/Abstract

摘要： 通过硬度、导电率、拉伸试验及显微组织分析,研究了不同固溶温度(450/460/470 ℃×1 h)和固溶时间(470 ℃×0.5/1/2 h)+120 ℃×18 h 时效处理对挤压态7C04铝合金力学性能、导电率和微观组织的变化规律。结果表明,当固溶温度为450~470 ℃、固溶时间为1 h时,随固溶温度升高,时效态合金中可溶第二相粒子逐渐溶解,强度、伸长率和硬度升高,导电率下降。当固溶温度为470 ℃,固溶时间为0.5~2 h时,随固溶时间延长,时效态合金中可溶第二相粒子的溶解程度上升,1 h后达到过饱和状态,继续延长时间,第二相粒子个数无明显变化,强度先升高后降低,伸长率和硬度不断升高,导电率先降低后升高。470 ℃×1 h固溶+120 ℃×18 h时效处理条件下,合金的力学性能可达到抗拉强度为645.3 MPa,屈服强度为585.0 MPa,硬度为182.53 HV3,导电率为27.59%IACS。

关键词: 7C04铝合金, 固溶处理, 力学性能, 电导率

Abstract: Variation laws of mechanical properties, electrical conductivity and microstructure of extruded 7C04 aluminum alloy solution treated at 450, 460 and 470 ℃ for 1 h, respectively, and solution treated at 470 ℃ for 0.5, 1 and 2 h, respectively, and aged at 120 ℃ for 18 h were investigated by means of hardness, electrical conductivity, tensile test and microstructure analysis. The results show that when the solution treatment temperature is between 450-470 ℃ and the solution treatment time is 1 h, with the increase of solution treatment temperature, the soluble second phase particles in the aged state alloy gradually dissolve, the strength, elongation and hardness increase, and the electrical conductivity decreases. When the solution treatment temperature is 470 ℃ and the solution treatment time is between 0.5-2 h, with the extension of solution treatment time, the dissolution degree of soluble second phase particles in the aged state alloy increases, reaching a supersaturated state after 1 h. If the solution treatment time is further extended, the number of second phase particles does not change significantly, the strength increases first and then decreases, the elongation and hardness continuously increase, and the electrical conductivity first decreases and then increases. Under the condition of solution treatment at 470 ℃ for 1 h and aging at 120 ℃ for 18 h, the mechanical properties of the alloy can reach a tensile strength of 645.3 MPa, a yield strength of 585.0 MPa, a hardness of 182.53 HV3, and an electrical conductivity of 27.59%IACS.

Key words: 7C04 aluminum alloy, solution treatment, mechanical properties, electric conductivity

中图分类号:

TG166.3

郭旭东, 邹仕军, 卢影峰, 龙泽熙. 固溶工艺对7C04铝合金组织与性能的影响[J]. 金属热处理, 2025, 50(3): 132-137.

Guo Xudong, Zou Shijun, Lu Yingfeng, Long Zexi. Effect of solution treatment process on microstructure and properties of 7C04 aluminum alloy[J]. Heat Treatment of Metals, 2025, 50(3): 132-137.

参考文献

[1] 方华婵, 陈康华, 巢宏, 等. Al-Zn-Mg-Cu系超强铝合金的研究现状与展望[J]. 粉末冶金材料科学与工程, 2009, 14(6): 351-358.
Fang Huachan, Chen Kanghua, Chao Hong, et al. Current research status and prespects of ultra strength Al-Zn-Mg-Cu aluminum alloy[J]. Materials Science and Engineering of Powder Metallurgy, 2009, 14(6): 351-358.
[2] 武晓辉. 合金元素对7xxx系铝合金组织与腐蚀性能研究[D]. 大连: 大连理工大学, 2022.
Wu Xiaohui. Effect of alloy elements on microstructure evolution and corrosion resistance of 7xxx aluminum alloys[D]. Dalian: Dalian University of Technology, 2022.
[3] 臧金鑫, 陈军洲, 韩凯, 等. 航空铝合金研究进展与发展趋势[J]. 中国材料进展, 2022, 41(10): 769-777, 807.
Zang Jinxin, Chen Junzhou, Han Kai, et al. Research progress and development tendency of aeronautical aluminum alloys[J]. Materials China, 2022, 41(10): 769-777, 807.
[4] 苏睿明, 郭金成, 李广龙, 等. Al-Cu-Mg-Ag合金发展现状[C]//第二十届沈阳科学学术年会论文集. 2023: 40-44.
[5] 张王军, 李云, 吴玉娜, 等. 超高强7XXX系铝合金的研究现状及发展趋势[J]. 现代交通与冶金材料, 2023, 3(3): 52-60, 84.
Zhang Wangjun, Li Yun, Wu Yu'na, et al. A critical review of the state-of-the-art of ultra-high strength 7XXX aluminum alloys[J]. Modern Transportation and Metallurgical Materials, 2023, 3(3): 52-60, 84.
[6] 张尉, 仇振安, 靳冉, 等. 超高强铝合金热处理工艺及其应用[J]. 中国高新科技, 2021(10): 28-29.
Zhang Wei, Qiu Zhen'an, Jin Ran, et al. Application of heat treatment process of ultra-high strength aluminum alloy[J]. China High and New Technology, 2021(10): 28-29.
[7] 王经涛, 孙宁, 余浪, 等. 固溶方式对Al-Zn-Mg-Cu合金组织及性能的影响[J]. 航空材料学报, 2023, 43(6): 65-72.
Wang Jingtao, Sun Ning, Yu Lang, et al. Effect of solution treatment on microstructure and properties of Al-Zn-Mg-Cu alloy[J]. Journal of Aeronautical Materials, 2023, 43(6): 65-72.
[8] 王路. 固溶淬火处理及预拉伸对Al-Zn-Mg-Cu合金组织及性能的影响[D]. 重庆: 重庆大学, 2022.
Wang Lu. Effects of solution treatment and pre-stretching on microstructures and properties of Al-Zn-Mg-Cu alloy[D]. Chongqing: Chongqing University, 2022.
[9] 肖艳苹, 万里, 李创, 等. 固溶处理对Al-Zn-Mg-Cu合金显微组织的影响[J]. 铝加工, 2017(4): 10-15.
Xiao Yanping, Wan Li, Li Chuang, et al. Effect of solution treatment on microstructure of Al-Zn-Mg-Cu alloy[J]. Aluminium Fabrication, 2017(4): 10-15.
[10] 谢志诚, 海丰龙, 陈璐, 等. T6热处理对2618铝合金组织与力学性能的影响[J]. 轨道交通材料, 2024, 3(1): 37-41.
Xie Zhicheng, Hai Fenglong, Chen Lu, et al. Effect of T6 heat treatment on microstructure and mechanical properties of 2618 aluminum alloy[J]. Materials for Rail Transportation System, 2024, 3(1): 37-41.
[11] 李茂华, 陈志龙, 徐伊雯, 等. 固溶处理对7475铝合金组织和拉伸性能的影响[J]. 云南大学学报(自然科学版), 2024, 46(1): 127-135.
Li Maohua, Chen Zhilong, Xu Yiwen, et al. Effect of solution treatment on microstructure and mechanical properties of 7475 Al alloy[J]. Journal of Yunnan University(Natural Sciences Edition), 2024, 46(1): 127-135.
[12] 王会敏, 李炎光, 吴静依. 固溶时间对2219铝合金组织和力学性能的影响[J]. 金属热处理, 2023, 48(7): 152-156.
Wang Huimin, Li Yanguang, Wu Jingyi. Effect of solution time on microstructure and mechanical properties of 2219 aluminum alloy[J]. Heat Treatment of Metals, 2023, 48(7): 152-156.
[13] 马春雨, 李智, 刘常升. 固溶加热温度对2A70铝合金组织与性能的影响[J]. 轻合金加工技术, 2003(5): 43-46.
Ma Chunyu, Li Zhi, Liu Changsheng. Effect of solution treatment temperature on the microstructure and properties of 2A70 aluminum alloy[J]. Light Alloy Fabrication Technology, 2003(5): 43-46.
[14] 张丽娇. 航空航天高强铝合金材料应用及发展趋势研究[J]. 新材料产业, 2021(3): 7-11.
Zhang Lijiao. Research on application and development trend of high strength aluminum alloy materials for aerospace[J]. Advanced Materials Industry, 2021(3): 7-11.

[1]	李申奥, 陈思文, 牛红伟, 朱红倩, 阚允, 江艳, 王健, 赵洪运. 轧制温度对Sc微合金化Al-3.2Cu-1.5Li合金组织和性能的影响[J]. 金属热处理, 2025, 50(3): 1-8.
[2]	朱晨辉, 徐流杰, 谢红申, 石如星, 殷立涛. 回火温度对超级马氏体不锈钢组织和力学性能的影响[J]. 金属热处理, 2025, 50(3): 16-24.
[3]	王畅, 王良, 周培山, 申文竹, 王斌. 冷变形及热处理对GH738镍基合金组织与性能的影响[J]. 金属热处理, 2025, 50(3): 25-31.
[4]	赵伟男, 卢超, 曹建春, 徐朝勇, 杨立盛, 张金昌. 高压低温回火对铌微合金化高碳钢组织与性能的影响[J]. 金属热处理, 2025, 50(3): 32-37.
[5]	周晓舟, 孟利, 徐江杰, 张宁, 涂杨, 傅超, 杨勇. 挤压工艺对AZ80NC可溶镁合金组织和性能的影响[J]. 金属热处理, 2025, 50(3): 38-43.
[6]	徐和林, 王江华. 焊后热处理对4Cr5MoSiV模具钢修补焊接头组织和性能的影响[J]. 金属热处理, 2025, 50(3): 64-68.
[7]	张保华, 董福元, 崔书辉, 黄旭刚. 固溶温度对QBe1.9和QBe2铍铜合金组织与性能的影响[J]. 金属热处理, 2025, 50(3): 96-101.
[8]	王娇娇, 高云哲, 郭泰瑜, 侯伟, 周玉青, 任可飘, 赵林林, 张子悦. 回火时间对深井套管用钢组织性能的影响[J]. 金属热处理, 2025, 50(3): 102-106.
[9]	石磊, 田鹏勇, 温国强, 魏明江, 赵宇. 淬火工艺对铁素体/马氏体双相钢组织与性能的影响[J]. 金属热处理, 2025, 50(3): 138-142.
[10]	郭春成, 迟宏宵, 谷金波, 董丽丽, 朱留平. Mo对Fe-Co-Cr系轴承钢组织及强韧性的影响[J]. 金属热处理, 2025, 50(3): 150-157.
[11]	马若曦, 尹宇彬, 邓超, 李子瑜, 张哲临, 丁桦. Fe-18Mn-8Al-1C轻质钢的组织性能及变形机制[J]. 金属热处理, 2025, 50(3): 183-188.
[12]	周浩, 杜豪杰, 曾燕屏, 郭德瑞, 李炜丽, 马志宝, 王庆峰, 李旌鑫. 高温长时在役GH4145合金螺栓的显微组织和力学性能[J]. 金属热处理, 2025, 50(3): 189-195.
[13]	梁晓东, 王炜, 李永清, 袁博, 郭晓峰, 程言龙. G115钢大口径厚壁管长期时效后的微观组织及力学性能[J]. 金属热处理, 2025, 50(3): 196-200.
[14]	齐加胜, 徐文权. 汽车用中锰钢的研究现状与展望[J]. 金属热处理, 2025, 50(3): 244-249.
[15]	刘明珠, 丁桦, 邹宇明. 部分奥氏体逆转变工艺对Fe-8Mn-0.2C-3Al中锰钢组织性能的影响[J]. 金属热处理, 2025, 50(2): 90-95.

固溶工艺对7C04铝合金组织与性能的影响

Effect of solution treatment process on microstructure and properties of 7C04 aluminum alloy

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

本文评价